Influence of high-energy electrons irradiation on nanoceramics properties of zirconia

Influence of high-energy electrons irradiation on nanoceramics properties of zirconia

Radiation defects in nanoceramics zirconia were investigated after electron irradiation with energy 41…89 MeV up to doze 2.28…5.7·10¹⁴ electrons/cm². Radioactive isotopes ⁸⁷,⁸⁸Y, ⁸⁸,⁸⁹,⁹⁵Zr, ⁹⁵Nb, ¹⁷⁵Hf are registered after irradiation of electrons with energy 41 and 47.2 MeV. The activity of ⁸³Rb w...

Повний опис

Збережено в:
Бібліографічні деталі
Дата:2013
Автори: Aizatskyi, M.I., Dikiy, N.P., Dovbnya, A.N., Fedorets, I.D., Kushnir, V.A., Lyashko, Yu.V., Medvedev, D.V., Mytrochenko, V.V., Onishchenko, I.N., Perezhogin, S.A., Pelichatyi, N.M., Danilenko, I.A., Konstantinova, T.E.
Формат: Стаття
Мова:English
Опубліковано: Національний науковий центр «Харківський фізико-технічний інститут» НАН України 2013
Назва видання:Вопросы атомной науки и техники
Теми:
Применение ускоренных пучков. детекторы и детектирование ядерных излучений
Онлайн доступ:http://dspace.nbuv.gov.ua/handle/123456789/111876
Теги: Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
Назва журналу:Digital Library of Periodicals of National Academy of Sciences of Ukraine
Цитувати:Influence of high-energy electrons irradiation on nanoceramics properties of zirconia / M.I. Aizatskyi, N.P. Dikiy, A.N. Dovbnya, I.D. Fedorets, V.A. Kushnir, Yu.V. Lyashko, D.V. Medvedev, V.V. Mytrochenko, I.N. Onishchenko, S.A. Perezhogin, N.M. Pelichatyi,I.A. Danilenko, T.E. Konstantinova // Вопросы атомной науки и техники. — 2013. — № 6. — С. 161-164. — Бібліогр.: 8 назв. — англ.

Репозитарії

Digital Library of Periodicals of National Academy of Sciences of Ukraine
id irk-123456789-111876
record_format dspace
institution Digital Library of Periodicals of National Academy of Sciences of Ukraine
collection DSpace DC
language English
topic Применение ускоренных пучков. детекторы и детектирование ядерных излучений
Применение ускоренных пучков. детекторы и детектирование ядерных излучений
spellingShingle Применение ускоренных пучков. детекторы и детектирование ядерных излучений
Применение ускоренных пучков. детекторы и детектирование ядерных излучений
Aizatskyi, M.I.
Dikiy, N.P.
Dovbnya, A.N.
Fedorets, I.D.
Kushnir, V.A.
Lyashko, Yu.V.
Medvedev, D.V.
Mytrochenko, V.V.
Onishchenko, I.N.
Perezhogin, S.A.
Pelichatyi, N.M.
Danilenko, I.A.
Konstantinova, T.E.
Influence of high-energy electrons irradiation on nanoceramics properties of zirconia
Вопросы атомной науки и техники
description Radiation defects in nanoceramics zirconia were investigated after electron irradiation with energy 41…89 MeV up to doze 2.28…5.7·10¹⁴ electrons/cm². Radioactive isotopes ⁸⁷,⁸⁸Y, ⁸⁸,⁸⁹,⁹⁵Zr, ⁹⁵Nb, ¹⁷⁵Hf are registered after irradiation of electrons with energy 41 and 47.2 MeV. The activity of ⁸³Rb was registered after irradiation by electrons with energy 86 and 88.9 MeV. Activity of ⁸³Rb can be formed in reactions (γ, 6n) or (e, 6n). Different process of annealing radiation defects in samples of nanoceramics is detected after irradiated by electrons with energy 41…47.2 or 86…88.9 MeV. The colour centres for samples of nanoceramics after irradiated by electrons with energy 41…47.2 MeV practically completely was annealed at 500°С. For samples of nanoceramics after irradiated by electrons with energy 86…88.9 MeV and after annealing at 500°С significant absorption for lengths of waves of 430 and 470 nm is observed. It is supposed that these distinctions at annealing the colour centres of zirconia are caused by formation in nuclear reactions by high-energy electrons on isotopes of a matrix of krypton atoms. The krypton atoms are the centres segregation point defects. As a result the steady defective complexes were formed.
format Article
author Aizatskyi, M.I.
Dikiy, N.P.
Dovbnya, A.N.
Fedorets, I.D.
Kushnir, V.A.
Lyashko, Yu.V.
Medvedev, D.V.
Mytrochenko, V.V.
Onishchenko, I.N.
Perezhogin, S.A.
Pelichatyi, N.M.
Danilenko, I.A.
Konstantinova, T.E.
author_facet Aizatskyi, M.I.
Dikiy, N.P.
Dovbnya, A.N.
Fedorets, I.D.
Kushnir, V.A.
Lyashko, Yu.V.
Medvedev, D.V.
Mytrochenko, V.V.
Onishchenko, I.N.
Perezhogin, S.A.
Pelichatyi, N.M.
Danilenko, I.A.
Konstantinova, T.E.
author_sort Aizatskyi, M.I.
title Influence of high-energy electrons irradiation on nanoceramics properties of zirconia
title_short Influence of high-energy electrons irradiation on nanoceramics properties of zirconia
title_full Influence of high-energy electrons irradiation on nanoceramics properties of zirconia
title_fullStr Influence of high-energy electrons irradiation on nanoceramics properties of zirconia
title_full_unstemmed Influence of high-energy electrons irradiation on nanoceramics properties of zirconia
title_sort influence of high-energy electrons irradiation on nanoceramics properties of zirconia
publisher Національний науковий центр «Харківський фізико-технічний інститут» НАН України
publishDate 2013
topic_facet Применение ускоренных пучков. детекторы и детектирование ядерных излучений
url http://dspace.nbuv.gov.ua/handle/123456789/111876
citation_txt Influence of high-energy electrons irradiation on nanoceramics properties of zirconia / M.I. Aizatskyi, N.P. Dikiy, A.N. Dovbnya, I.D. Fedorets, V.A. Kushnir, Yu.V. Lyashko, D.V. Medvedev, V.V. Mytrochenko, I.N. Onishchenko, S.A. Perezhogin, N.M. Pelichatyi,I.A. Danilenko, T.E. Konstantinova // Вопросы атомной науки и техники. — 2013. — № 6. — С. 161-164. — Бібліогр.: 8 назв. — англ.
series Вопросы атомной науки и техники
work_keys_str_mv AT aizatskyimi influenceofhighenergyelectronsirradiationonnanoceramicspropertiesofzirconia
AT dikiynp influenceofhighenergyelectronsirradiationonnanoceramicspropertiesofzirconia
AT dovbnyaan influenceofhighenergyelectronsirradiationonnanoceramicspropertiesofzirconia
AT fedoretsid influenceofhighenergyelectronsirradiationonnanoceramicspropertiesofzirconia
AT kushnirva influenceofhighenergyelectronsirradiationonnanoceramicspropertiesofzirconia
AT lyashkoyuv influenceofhighenergyelectronsirradiationonnanoceramicspropertiesofzirconia
AT medvedevdv influenceofhighenergyelectronsirradiationonnanoceramicspropertiesofzirconia
AT mytrochenkovv influenceofhighenergyelectronsirradiationonnanoceramicspropertiesofzirconia
AT onishchenkoin influenceofhighenergyelectronsirradiationonnanoceramicspropertiesofzirconia
AT perezhoginsa influenceofhighenergyelectronsirradiationonnanoceramicspropertiesofzirconia
AT pelichatyinm influenceofhighenergyelectronsirradiationonnanoceramicspropertiesofzirconia
AT danilenkoia influenceofhighenergyelectronsirradiationonnanoceramicspropertiesofzirconia
AT konstantinovate influenceofhighenergyelectronsirradiationonnanoceramicspropertiesofzirconia
first_indexed 2024-03-30T09:19:15Z
last_indexed 2024-03-30T09:19:15Z
_version_ 1796149828005134336
spelling irk-123456789-1118762017-01-16T03:03:12Z Influence of high-energy electrons irradiation on nanoceramics properties of zirconia Aizatskyi, M.I. Dikiy, N.P. Dovbnya, A.N. Fedorets, I.D. Kushnir, V.A. Lyashko, Yu.V. Medvedev, D.V. Mytrochenko, V.V. Onishchenko, I.N. Perezhogin, S.A. Pelichatyi, N.M. Danilenko, I.A. Konstantinova, T.E. Применение ускоренных пучков. детекторы и детектирование ядерных излучений Radiation defects in nanoceramics zirconia were investigated after electron irradiation with energy 41…89 MeV up to doze 2.28…5.7·10¹⁴ electrons/cm². Radioactive isotopes ⁸⁷,⁸⁸Y, ⁸⁸,⁸⁹,⁹⁵Zr, ⁹⁵Nb, ¹⁷⁵Hf are registered after irradiation of electrons with energy 41 and 47.2 MeV. The activity of ⁸³Rb was registered after irradiation by electrons with energy 86 and 88.9 MeV. Activity of ⁸³Rb can be formed in reactions (γ, 6n) or (e, 6n). Different process of annealing radiation defects in samples of nanoceramics is detected after irradiated by electrons with energy 41…47.2 or 86…88.9 MeV. The colour centres for samples of nanoceramics after irradiated by electrons with energy 41…47.2 MeV practically completely was annealed at 500°С. For samples of nanoceramics after irradiated by electrons with energy 86…88.9 MeV and after annealing at 500°С significant absorption for lengths of waves of 430 and 470 nm is observed. It is supposed that these distinctions at annealing the colour centres of zirconia are caused by formation in nuclear reactions by high-energy electrons on isotopes of a matrix of krypton atoms. The krypton atoms are the centres segregation point defects. As a result the steady defective complexes were formed. Досліджувалися радіаційні дефекти в нанокераміці двоокису цирконію при опроміненні електронами з енергією 41…89 МеВ до дози 2,28…5,7·10¹⁴ часток/см². При опроміненні електронами з енергією 41 і 47,2 МеВ реєструються радіоактивні ізотопи ⁸⁷,⁸⁸Y, ⁸⁸,⁸⁹,⁹⁵Zr, ⁹⁵Nb, ¹⁷⁵Hf. При опроміненні електронами з енергією 86 і 88,9 МеВ додатково реєструється активність ⁸³Rb, що може бути утворена в реакціях (γ, 6n) або (e, 6n). Виявлено різний процес відпалу радіаційних дефектів у зразках нанокераміки, опромінених при енергії електронів 41…47,2 і 86…88,9 МеВ. Центри фарбування для зразків нанокераміки, опромінених електронами з енергією 41…47,2 МеВ, практично повністю відпалювались при 500 °С. Для зразків нанокераміки, опромінених електронами з енергією 86…88,9 МеВ, після відпалу при 500 °C спостерігається значне поглинання для довжин хвиль 430 і 470 нм. Передбачається, що ці розходження при відпалі центрів забарвлення двоокису цирконію обумовлені утворенням у ядерних реакціях під дією високоенергетичних електронів на ізотопах матриці атомів криптону, які є центрами сегрегації крапкових дефектів, що приводить до утворення стійких дефектних комплексів. Исследовались радиационные дефекты в нанокерамике диоксида циркония при облучении электронами с энергией 41…89 МэВ до дозы 2,28…5,7·10¹⁴ частиц/см². При облучении электронами с энергией 41 и 47,2 МэВ регистрируются радиоактивные изотопы ⁸⁷,⁸⁸Y, ⁸⁸,⁸⁹,⁹⁵Zr, ⁹⁵Nb, ¹⁷⁵Hf При облучении электронами с энергией 86 и 88,9 МэВ дополнительно регистрируется активность ⁸³Rb, которая может быть образована в реакциях (γ, 6n) или (e, 6n). Обнаружен различный процесс отжига радиационных дефектов в образцах нанокерамики, облученных при энергии электронов 41…47,2 и 86…88,9 МэВ. Центры окраски для образцов нанокерамики, облученных электронами с энергией 41…47,2 МэВ, практически полностью отожглись при 500 °С. Для образцов нанокерамики, облученных электронами с энергией 86…88,9 МэВ, после отжига при 500 °С наблюдается значительное поглощение для длин волн 430 и 470 нм. Предполагается, что эти различия при отжиге центров окраски двуокиси циркония обусловлены образованием в ядерных реакциях под действием высокоэнергетических электронов на изотопах матрицы атомов криптона, которые являются центрами сегрегации точечных дефектов, что приводит к образованию устойчивых дефектных комплексов. 2013 Article Influence of high-energy electrons irradiation on nanoceramics properties of zirconia / M.I. Aizatskyi, N.P. Dikiy, A.N. Dovbnya, I.D. Fedorets, V.A. Kushnir, Yu.V. Lyashko, D.V. Medvedev, V.V. Mytrochenko, I.N. Onishchenko, S.A. Perezhogin, N.M. Pelichatyi,I.A. Danilenko, T.E. Konstantinova // Вопросы атомной науки и техники. — 2013. — № 6. — С. 161-164. — Бібліогр.: 8 назв. — англ. 1562-6016 PACS: 61.46.+w, 61.80.Fe http://dspace.nbuv.gov.ua/handle/123456789/111876 en Вопросы атомной науки и техники Національний науковий центр «Харківський фізико-технічний інститут» НАН України

Схожі ресурси