Effect of severe plastic deformation on radiation hardening of T91 ferritic-martensitic steel
Effect of thermomechanical treatment on radiation hardening behavior in T91 ferritic-martensitic steel was evaluated. An applying of severe plastic deformation (SPD) by the “upsetting-extrusion” method and subsequent heat treatment led to a considerable grain refinement, crushing of martensite lamel...
Gespeichert in:
| Datum: | 2021 |
|---|---|
| Hauptverfasser: | , , , , , , , , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Національний науковий центр «Харківський фізико-технічний інститут» НАН України
2021
|
| Schriftenreihe: | Вопросы атомной науки и техники |
| Schlagworte: | |
| Online Zugang: | http://dspace.nbuv.gov.ua/handle/123456789/194682 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Effect of severe plastic deformation on radiation hardening of T91 ferritic-martensitic steel / V.N. Voyevodin, G.D. Tolstolutskaya, S.A. Karpov, A.N. Velikodnyi, M.A. Tikhonovsky, A.S. Kalchenko, G.N. Tolmachova, R.L. Vasilenko, I.E. Kopanets // Problems of Atomic Science and Technology. — 2021. — № 2. — С. 35-42. — Бібліогр.: 34 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| Zusammenfassung: | Effect of thermomechanical treatment on radiation hardening behavior in T91 ferritic-martensitic steel was evaluated. An applying of severe plastic deformation (SPD) by the “upsetting-extrusion” method and subsequent heat treatment led to a considerable grain refinement, crushing of martensite lamellas, reduction of MX carbides size and their more uniform distribution. Nanoindentation measurements of SPD-modified steel revealed a 1.4-fold increase in the hardness relative to the initial steel. Irradiation response of modified steel was examined after 1.4 MeV Ar+ ion irradiations in the dose range of 10…45 displacements per atom (dpa) at room temperature and 460 °C. Microstructure characterization was performed by means of transmission electron microscopy (TEM). It was found that dislocation loops and nano-sized argon bubbles dominated the damage microstructure after ion irradiation. The effects of SPD-induced transformations as well as nano-bubbles formation are discussed regarding to the hardening phenomenon observed in irradiated steel. |
|---|