Multiwalled Carbon Nanotubes Modified with Biocompatible Compounds
Oxidized with solution of hydrogen peroxide multiwalled carbon nanotubes (MWCNTs) were modified with 2-hydroxyethylmethacrylate (HEMA) or chitosan (CTS). Morphology and surface properties of the pristine and modified MWCNTs have been investigated. The zeta-potential behaviour of MWCNTs was studied a...
Збережено в:
Видавець: | Інститут хімії поверхні ім. О.О. Чуйка НАН України |
---|---|
Дата: | 2010 |
Автори: | , , , , , , |
Формат: | Стаття |
Мова: | English |
Опубліковано: |
Інститут хімії поверхні ім. О.О. Чуйка НАН України
2010
|
Назва видання: | Хімія, фізика та технологія поверхні |
Онлайн доступ: | http://dspace.nbuv.gov.ua/handle/123456789/29022 |
Теги: |
Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
|
Цитувати: | Multiwalled Carbon Nanotubes Modified with Biocompatible Compounds / Y. Bolbukh, G. Gunko, G. Prikhod’ko, V. Tertykh, K. László, A. Tóth, B. Koczka // Хімія, фізика та технологія поверхні. — 2010. — Т. 1, № 4. — С. 389-400. — Бібліогр.: 36 назв. — англ. |
Репозиторії
Digital Library of Periodicals of National Academy of Sciences of Ukraineid |
irk-123456789-29022 |
---|---|
record_format |
dspace |
institution |
Digital Library of Periodicals of National Academy of Sciences of Ukraine |
collection |
DSpace DC |
language |
English |
description |
Oxidized with solution of hydrogen peroxide multiwalled carbon nanotubes (MWCNTs) were modified with 2-hydroxyethylmethacrylate (HEMA) or chitosan (CTS). Morphology and surface properties of the pristine and modified MWCNTs have been investigated. The zeta-potential behaviour of MWCNTs was studied as a function of pH and suspension concentration. After oxidation, the divided nanotubes are found to have uncapped ports decorated with hydroxyl groups mostly. Surface oxygencontaining groups specify the negative zeta-potential in all pH range studied (pH=3-11). The values of zeta-potential display an inverse dependence on the dispersion concentration in acidic and basic solutions. After modification of oxidized MWCNTs with HEMA their isoelectric point is shifted from pH=2 to pH=10. Repeated surface treatment with HEMA (MWCNTs-HEMA-HEMA), along with change of the nature of terminal groups, provides stable surface charge increasing with nanotubes concentration in the pH range of 3-9. The isoelectric point of MWCNTs modified with CTS occurs at pH=4.5. At relatively small zeta-potential values, which become more negative with a decrease in the nanotubes concentration, such suspensions are the most stable. |
format |
Article |
author |
Bolbukh, Y. Gunko, G. Prikhod’ko, G. Tertykh, V. László, K. Tóth, A. Koczka, B. |
spellingShingle |
Bolbukh, Y. Gunko, G. Prikhod’ko, G. Tertykh, V. László, K. Tóth, A. Koczka, B. Multiwalled Carbon Nanotubes Modified with Biocompatible Compounds Хімія, фізика та технологія поверхні |
author_facet |
Bolbukh, Y. Gunko, G. Prikhod’ko, G. Tertykh, V. László, K. Tóth, A. Koczka, B. |
author_sort |
Bolbukh, Y. |
title |
Multiwalled Carbon Nanotubes Modified with Biocompatible Compounds |
title_short |
Multiwalled Carbon Nanotubes Modified with Biocompatible Compounds |
title_full |
Multiwalled Carbon Nanotubes Modified with Biocompatible Compounds |
title_fullStr |
Multiwalled Carbon Nanotubes Modified with Biocompatible Compounds |
title_full_unstemmed |
Multiwalled Carbon Nanotubes Modified with Biocompatible Compounds |
title_sort |
multiwalled carbon nanotubes modified with biocompatible compounds |
publisher |
Інститут хімії поверхні ім. О.О. Чуйка НАН України |
publishDate |
2010 |
url |
http://dspace.nbuv.gov.ua/handle/123456789/29022 |
citation_txt |
Multiwalled Carbon Nanotubes Modified with Biocompatible Compounds / Y. Bolbukh, G. Gunko, G. Prikhod’ko, V. Tertykh, K. László, A. Tóth, B. Koczka // Хімія, фізика та технологія поверхні. — 2010. — Т. 1, № 4. — С. 389-400. — Бібліогр.: 36 назв. — англ. |
series |
Хімія, фізика та технологія поверхні |
work_keys_str_mv |
AT bolbukhy multiwalledcarbonnanotubesmodifiedwithbiocompatiblecompounds AT gunkog multiwalledcarbonnanotubesmodifiedwithbiocompatiblecompounds AT prikhodkog multiwalledcarbonnanotubesmodifiedwithbiocompatiblecompounds AT tertykhv multiwalledcarbonnanotubesmodifiedwithbiocompatiblecompounds AT laszlok multiwalledcarbonnanotubesmodifiedwithbiocompatiblecompounds AT totha multiwalledcarbonnanotubesmodifiedwithbiocompatiblecompounds AT koczkab multiwalledcarbonnanotubesmodifiedwithbiocompatiblecompounds |
first_indexed |
2023-10-18T17:27:19Z |
last_indexed |
2023-10-18T17:27:19Z |
_version_ |
1796141585542414336 |
spelling |
irk-123456789-290222011-11-29T12:06:30Z Multiwalled Carbon Nanotubes Modified with Biocompatible Compounds Bolbukh, Y. Gunko, G. Prikhod’ko, G. Tertykh, V. László, K. Tóth, A. Koczka, B. Oxidized with solution of hydrogen peroxide multiwalled carbon nanotubes (MWCNTs) were modified with 2-hydroxyethylmethacrylate (HEMA) or chitosan (CTS). Morphology and surface properties of the pristine and modified MWCNTs have been investigated. The zeta-potential behaviour of MWCNTs was studied as a function of pH and suspension concentration. After oxidation, the divided nanotubes are found to have uncapped ports decorated with hydroxyl groups mostly. Surface oxygencontaining groups specify the negative zeta-potential in all pH range studied (pH=3-11). The values of zeta-potential display an inverse dependence on the dispersion concentration in acidic and basic solutions. After modification of oxidized MWCNTs with HEMA their isoelectric point is shifted from pH=2 to pH=10. Repeated surface treatment with HEMA (MWCNTs-HEMA-HEMA), along with change of the nature of terminal groups, provides stable surface charge increasing with nanotubes concentration in the pH range of 3-9. The isoelectric point of MWCNTs modified with CTS occurs at pH=4.5. At relatively small zeta-potential values, which become more negative with a decrease in the nanotubes concentration, such suspensions are the most stable. Досліджено фізико-хімічні властивості, морфологію та характер поверхні вихідних і модифікованих 2-гідроксіетилметакрилатом (HEMA) і хітозаном багатошарових вуглецевих нанотрубок (БШВНТ). Вимірювання дзета-потенціалу БШВНТ проводили при різних рН розчину електроліту і концентраціях суспензії. Показано, що при окисненні БШВНТ відбувається їхнє дроблення з утворенням портів, що обрамлені переважно гідроксильними групами. Кисеньвмісні групи визначають негативний дзета-потенціал окиснених нанотрубок в досліджуваному діапазоні рН (3-11), але залежність дзета-потенціалу від концентрації дисперсії у кислому і основному середовищах обернена. Після модифікування БШВНТ НЕМА ізоелектрична точка зміщується з рН=2 до рН=10. Подовження ланцюжка прикріпленого до нанотрубок модифікатора (БШВНТ-HЕМА-HЕМА) разом із зміною кінцевих функціональних груп забезпечує позитивний і стабільний заряд поверхні, що збільшується симбатно концентрації нанотрубок в діапазоні рН 3-9. Ізоелектрична точка БШВНТ-хітозан близька до рН=4,5. За відносно невеликих значень дзета-потенціалу, який стає більш негативним зі зменшенням концентрації нанотрубок, такі суспензії є найбільш стійкими. Исследованы физико-химические свойства, морфология и характер поверхности исходных и модифицированных 2-гидроксиэтилметакрилатом (НЕМА) и хитозаном многослойных углеродных нанотрубок (МУНТ). Измерение дзета-потенциала МУНТ проводили при разных рН раствора электролита и концентрациях суспензии. Показано, что при окислении МУНТ происходит их дробление, а образующиеся порты обрамлены преимущественно гидроксильными группами. Кислородсодержащие группы определяют отрицательный дзета-потенциал окисленных нанотрубок в исследуемом диапазоне рН (3-11), но зависимость дзета-потенциала от концентрации дисперсии в кислой и основной средах обратная. После модифицирования МУНТ НЕМА изоэлектрическая точка смещается от рН=2 к рН=10. Удлинение цепочки прикрепленного к нанотрубкам модификатора (МУНТ-НЕМА-НЕМА) вместе с изменением концевых функциональных групп обеспечивает положительный и стабильный заряд поверхности, который увеличивается симбатно концентрации нанотрубок в диапазоне рН 3-9. Изоэлектрическая точка МУНТ-хитозан близка к рН=4,5. При относительно небольшом значении дзета-потенциала, который становится более отрицательным с уменьшением концентрации нанотрубок, такие суспензии являются наиболее устойчивыми. 2010 Article Multiwalled Carbon Nanotubes Modified with Biocompatible Compounds / Y. Bolbukh, G. Gunko, G. Prikhod’ko, V. Tertykh, K. László, A. Tóth, B. Koczka // Хімія, фізика та технологія поверхні. — 2010. — Т. 1, № 4. — С. 389-400. — Бібліогр.: 36 назв. — англ. 2079-1704 http://dspace.nbuv.gov.ua/handle/123456789/29022 544.723:544.77 en Хімія, фізика та технологія поверхні Інститут хімії поверхні ім. О.О. Чуйка НАН України |