Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 1. Static tests and stiffness degradation at failure studies
The analysis of stiffness and the identification of rupture mechanisms during and after static tests of sandwich panels and their components have been investigated. The sandwich panels, having cross-ply laminates skins made of glass fibre and epoxy resin were manufactured by vacuum moulding an...
Збережено в:
| Дата: | 2007 |
|---|---|
| Автори: | , , , |
| Формат: | Стаття |
| Мова: | English |
| Опубліковано: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2007
|
| Назва видання: | Проблемы прочности |
| Теми: | |
| Онлайн доступ: | http://dspace.nbuv.gov.ua/handle/123456789/48041 |
| Теги: |
Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Цитувати: | Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 1. Static tests and stiffness degradation at failure studies / A. Bezazi, A. El Mahi, J.-M. Berthelot, B. Bezzazi // Проблемы прочности. — 2007. — № 2. — С. 88-98. — Бібліогр.: 29 назв. — англ. |
Репозитарії
Digital Library of Periodicals of National Academy of Sciences of Ukraine| id |
irk-123456789-48041 |
|---|---|
| record_format |
dspace |
| spelling |
irk-123456789-480412013-08-13T20:06:54Z Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 1. Static tests and stiffness degradation at failure studies Bezazi, A. El Mahi, A. Berthelot, J.-M. Bezzazi, B. Научно-технический раздел The analysis of stiffness and the identification of rupture mechanisms during and after static tests of sandwich panels and their components have been investigated. The sandwich panels, having cross-ply laminates skins made of glass fibre and epoxy resin were manufactured by vacuum moulding and subjected to three-point bending tests. Two PVC cores of similar type but with differing densities were investigated. The effect of core density and its thickness on the behavior and the damage was highlighted. In terms of stiffness and load at failure, the sandwich structure has better mechanical characteristics compared to its components. Експериментально досліджено зміну жорсткості та проаналізовано механізми руйнування при статичних випробуваннях багатошарових композитних пластин і їх компонентів. Багатошарові композитні пластини з перехресними шарами зі скловолокна та епоксидної смоли, що виготовлені методом вакуумної відливки, піддавали навантаженню триточковим згином. Досліджували два варіанти пластин з однотипними наповнювачами з полі- вінілопласта різної щільності. Розглянуто вплив щільності і товщини внутрішнього шару наповнювача на поведінку та пошкодження композита. Показано, що композит із наповнювачем великої щільності має більш високі характеристики статичної міцності і стійкості порівняно з композитом із наповнювачем меншої щільності. Экспериментально исследовано изменение жесткости и проанализированы механизмы разрушения при статических испытаниях многослойных композитных пластин и их компонентов. Многослойные композитные пластины с перекрестными слоями из стекловолокна и эпоксидной смолы, изготовленные методом вакуумной отливки, подвергали нагружению трехточечным изгибом. Исследовали два варианта пластин с однотипными наполнителями из пеновинилопласта различной плотности. Рассмотрено влияние плотности и толщины внутреннего слоя наполнителя на поведение и повреждение композита. Показано, что композит с наполнителем большей плотности обладает более высокими характеристиками статической прочности и устойчивости по сравнению с композитом, имеющим наполнитель меньшей плотности. 2007 Article Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 1. Static tests and stiffness degradation at failure studies / A. Bezazi, A. El Mahi, J.-M. Berthelot, B. Bezzazi // Проблемы прочности. — 2007. — № 2. — С. 88-98. — Бібліогр.: 29 назв. — англ. 0556-171X http://dspace.nbuv.gov.ua/handle/123456789/48041 539.4 en Проблемы прочности Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| institution |
Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| collection |
DSpace DC |
| language |
English |
| topic |
Научно-технический раздел Научно-технический раздел |
| spellingShingle |
Научно-технический раздел Научно-технический раздел Bezazi, A. El Mahi, A. Berthelot, J.-M. Bezzazi, B. Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 1. Static tests and stiffness degradation at failure studies Проблемы прочности |
| description |
The analysis of stiffness and the identification
of rupture mechanisms during and after static
tests of sandwich panels and their components
have been investigated. The sandwich panels,
having cross-ply laminates skins made of glass
fibre and epoxy resin were manufactured by
vacuum moulding and subjected to three-point
bending tests. Two PVC cores of similar type
but with differing densities were investigated.
The effect of core density and its thickness on
the behavior and the damage was highlighted.
In terms of stiffness and load at failure, the
sandwich structure has better mechanical
characteristics compared to its components. |
| format |
Article |
| author |
Bezazi, A. El Mahi, A. Berthelot, J.-M. Bezzazi, B. |
| author_facet |
Bezazi, A. El Mahi, A. Berthelot, J.-M. Bezzazi, B. |
| author_sort |
Bezazi, A. |
| title |
Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 1. Static tests and stiffness degradation at failure studies |
| title_short |
Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 1. Static tests and stiffness degradation at failure studies |
| title_full |
Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 1. Static tests and stiffness degradation at failure studies |
| title_fullStr |
Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 1. Static tests and stiffness degradation at failure studies |
| title_full_unstemmed |
Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 1. Static tests and stiffness degradation at failure studies |
| title_sort |
experimental analysis of behavior and damage of sandwich composite materials in three-point bending. part 1. static tests and stiffness degradation at failure studies |
| publisher |
Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| publishDate |
2007 |
| topic_facet |
Научно-технический раздел |
| url |
http://dspace.nbuv.gov.ua/handle/123456789/48041 |
| citation_txt |
Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 1. Static tests and stiffness degradation at failure studies / A. Bezazi, A. El Mahi, J.-M. Berthelot, B. Bezzazi // Проблемы прочности. — 2007. — № 2. — С. 88-98. — Бібліогр.: 29 назв. — англ. |
| series |
Проблемы прочности |
| work_keys_str_mv |
AT bezazia experimentalanalysisofbehavioranddamageofsandwichcompositematerialsinthreepointbendingpart1statictestsandstiffnessdegradationatfailurestudies AT elmahia experimentalanalysisofbehavioranddamageofsandwichcompositematerialsinthreepointbendingpart1statictestsandstiffnessdegradationatfailurestudies AT berthelotjm experimentalanalysisofbehavioranddamageofsandwichcompositematerialsinthreepointbendingpart1statictestsandstiffnessdegradationatfailurestudies AT bezzazib experimentalanalysisofbehavioranddamageofsandwichcompositematerialsinthreepointbendingpart1statictestsandstiffnessdegradationatfailurestudies |
| first_indexed |
2023-10-18T18:08:56Z |
| last_indexed |
2023-10-18T18:08:56Z |
| _version_ |
1796143441219944448 |