On differences in mechanisms of metal fracture in conditions of low-cycle and high-cycle fatigue

• Datum: 2014
• Hauptverfasser: Мацевитый, В. М., Вакуленко, К. В., Казак, И. Б.
• Format: Artikel
• Sprache: Russian
• Veröffentlicht: Інститут енергетичних машин і систем ім. А. М. Підгорного Національної академії наук України 2014
• Schlagworte: low-cycle fatigue; high-cycle fatigue; intercrystalline fracture; intracrystalline fracture; submicrocracks; damage accumulation; coercive force; УДК; 537.624.8; 539.388.1; 539.422.24
• Online Zugang: https://journals.uran.ua/jme/article/view/27182
• Назва журналу: Journal of Mechanical Engineering

Differences in mechanisms of damage accumulation for low-cycle and high-cycle fatigue in terms of efficiency of use of the coercive force method in diagnostics of presence of defects in metal under cyclic loading are considered.It is pointed out that, depending on level of loading amplitude, differe...