Application of electroconsolidation of powder components for production of ultradenced ceramics Al₂O₃ and ZrO₂ (3% Y₂O₃)
The possibility of application of electroconsolidation for production of ultradenced ceramics based on Al₂O₃ and ZrO₂ (3% Y₂O₃ ) compounds is studied. As a result of the conducted researches optimum values of process temperature at which the best parameters of Al₂O₃ and ZrO₂ (3% Y₂O₃ ) ceramic prope...
Saved in:
| Published in: | Физическая инженерия поверхности |
|---|---|
| Date: | 2013 |
| Main Authors: | , , |
| Format: | Article |
| Language: | English |
| Published: |
Науковий фізико-технологічний центр МОН та НАН України
2013
|
| Online Access: | https://nasplib.isofts.kiev.ua/handle/123456789/100314 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Journal Title: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Cite this: | Application of electroconsolidation of powder components for production of ultradenced ceramics Al₂O₃ and ZrO₂ (3% Y₂O₃) / S.Yu. Sayenko, Eu.O. Svitlychniy, K.V. Lobach // Физическая инженерия поверхности. — 2013. — Т. 11, № 3. — С. 285–288. — Бібліогр.: 9 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862750398851317760 |
|---|---|
| author | Sayenko, S.Yu. Svitlychniy, Eu.O. Lobach, K.V. |
| author_facet | Sayenko, S.Yu. Svitlychniy, Eu.O. Lobach, K.V. |
| citation_txt | Application of electroconsolidation of powder components for production of ultradenced ceramics Al₂O₃ and ZrO₂ (3% Y₂O₃) / S.Yu. Sayenko, Eu.O. Svitlychniy, K.V. Lobach // Физическая инженерия поверхности. — 2013. — Т. 11, № 3. — С. 285–288. — Бібліогр.: 9 назв. — англ. |
| collection | DSpace DC |
| container_title | Физическая инженерия поверхности |
| description | The possibility of application of electroconsolidation for production of ultradenced ceramics based on Al₂O₃ and ZrO₂ (3% Y₂O₃ ) compounds is studied. As a result of the conducted researches optimum values of process temperature at which the best parameters of Al₂O₃ and ZrO₂ (3% Y₂O₃ ) ceramic properties are reached: the apparent density – 3.98 and 6.08 g/cm³ , bending strength – 350 and 800 MPa, fracture toughness – 4.0 and 8.0 МPa⋅m0.5 respectively are established. The researches of a ceramics microstructure are found that high parameters of Al₂O₃ and ZrO₂ (3% Y₂O₃ ) properties are defined by dense and fine-crystalline structure.
Изучена возможность применения электроконсолидации для получения особоплотной керамики на основе Al₂O₃ и ZrO₂ (3% Y₂O₃ ). В результате проведенных исследований установлены оптимальные значения температуры процесса, при которых достигаются наибольшие показатели свойств керамики на основе Al₂O₃ и ZrO₂ (3% Y₂O₃ ) кажущаяся плотность 3.98 и 6.08 г/см³ , предел прочности при изгибе 350 и 800 МПа, коэффициент интенсивности напряжений 4.0 и 8.0 МПа⋅м 0,5 соответственно. Исследованиями микроструктуры керамики установлено, что высокие показатели свойств Al₂O₃ и ZrO₂ (3% Y₂O₃ ) определяются плотной и мелкокристаллической структурой.
Вивчена можливість щодо використання електроконсолідації для отримання особливощільної кераміки на основі Al₂O₃ та ZrO₂ (3% Y₂O₃ ). За результатами наведених досліджень встановлено оптимальні значення температури процесу, при яких досягаються найбільші показники властивостей кераміки Al₂O₃ та ZrO₂ (3% Y₂O₃ ): уявна щільність 3.98 та 6.08 г/см³ , міцність на вигин 350 та 800 МПа, коефіцієнт інтенсивності напруг 4.0 та 8.0 МПа⋅м0,5 відповідно. Дослідженнями мікроструктури було доведено, що високі показники властивостей Al₂O₃ та ZrO₂ (3% Y₂O₃ ) визначаються щільною та дрібнокристалічною структурою кераміки.
|
| first_indexed | 2025-12-07T21:05:54Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-100314 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 1999-8074 |
| language | English |
| last_indexed | 2025-12-07T21:05:54Z |
| publishDate | 2013 |
| publisher | Науковий фізико-технологічний центр МОН та НАН України |
| record_format | dspace |
| spelling | Sayenko, S.Yu. Svitlychniy, Eu.O. Lobach, K.V. 2016-05-19T16:16:35Z 2016-05-19T16:16:35Z 2013 Application of electroconsolidation of powder components for production of ultradenced ceramics Al₂O₃ and ZrO₂ (3% Y₂O₃) / S.Yu. Sayenko, Eu.O. Svitlychniy, K.V. Lobach // Физическая инженерия поверхности. — 2013. — Т. 11, № 3. — С. 285–288. — Бібліогр.: 9 назв. — англ. 1999-8074 https://nasplib.isofts.kiev.ua/handle/123456789/100314 666.762.11:666.762.52 The possibility of application of electroconsolidation for production of ultradenced ceramics based on Al₂O₃ and ZrO₂ (3% Y₂O₃ ) compounds is studied. As a result of the conducted researches optimum values of process temperature at which the best parameters of Al₂O₃ and ZrO₂ (3% Y₂O₃ ) ceramic properties are reached: the apparent density – 3.98 and 6.08 g/cm³ , bending strength – 350 and 800 MPa, fracture toughness – 4.0 and 8.0 МPa⋅m0.5 respectively are established. The researches of a ceramics microstructure are found that high parameters of Al₂O₃ and ZrO₂ (3% Y₂O₃ ) properties are defined by dense and fine-crystalline structure. Изучена возможность применения электроконсолидации для получения особоплотной керамики на основе Al₂O₃ и ZrO₂ (3% Y₂O₃ ). В результате проведенных исследований установлены оптимальные значения температуры процесса, при которых достигаются наибольшие показатели свойств керамики на основе Al₂O₃ и ZrO₂ (3% Y₂O₃ ) кажущаяся плотность 3.98 и 6.08 г/см³ , предел прочности при изгибе 350 и 800 МПа, коэффициент интенсивности напряжений 4.0 и 8.0 МПа⋅м 0,5 соответственно. Исследованиями микроструктуры керамики установлено, что высокие показатели свойств Al₂O₃ и ZrO₂ (3% Y₂O₃ ) определяются плотной и мелкокристаллической структурой. Вивчена можливість щодо використання електроконсолідації для отримання особливощільної кераміки на основі Al₂O₃ та ZrO₂ (3% Y₂O₃ ). За результатами наведених досліджень встановлено оптимальні значення температури процесу, при яких досягаються найбільші показники властивостей кераміки Al₂O₃ та ZrO₂ (3% Y₂O₃ ): уявна щільність 3.98 та 6.08 г/см³ , міцність на вигин 350 та 800 МПа, коефіцієнт інтенсивності напруг 4.0 та 8.0 МПа⋅м0,5 відповідно. Дослідженнями мікроструктури було доведено, що високі показники властивостей Al₂O₃ та ZrO₂ (3% Y₂O₃ ) визначаються щільною та дрібнокристалічною структурою кераміки. en Науковий фізико-технологічний центр МОН та НАН України Физическая инженерия поверхности Application of electroconsolidation of powder components for production of ultradenced ceramics Al₂O₃ and ZrO₂ (3% Y₂O₃) Применение электроконсолидации порошковых компонентов для получения особоплотной керамики Al₂O₃ и ZrO₂ (3% Y₂O₃) Застусовання електроконсолідації порошкових компонентів для отримання особливощільної кераміки Al₂O₃ та ZrO₂ (3% Y₂O₃) Article published earlier |
| spellingShingle | Application of electroconsolidation of powder components for production of ultradenced ceramics Al₂O₃ and ZrO₂ (3% Y₂O₃) Sayenko, S.Yu. Svitlychniy, Eu.O. Lobach, K.V. |
| title | Application of electroconsolidation of powder components for production of ultradenced ceramics Al₂O₃ and ZrO₂ (3% Y₂O₃) |
| title_alt | Применение электроконсолидации порошковых компонентов для получения особоплотной керамики Al₂O₃ и ZrO₂ (3% Y₂O₃) Застусовання електроконсолідації порошкових компонентів для отримання особливощільної кераміки Al₂O₃ та ZrO₂ (3% Y₂O₃) |
| title_full | Application of electroconsolidation of powder components for production of ultradenced ceramics Al₂O₃ and ZrO₂ (3% Y₂O₃) |
| title_fullStr | Application of electroconsolidation of powder components for production of ultradenced ceramics Al₂O₃ and ZrO₂ (3% Y₂O₃) |
| title_full_unstemmed | Application of electroconsolidation of powder components for production of ultradenced ceramics Al₂O₃ and ZrO₂ (3% Y₂O₃) |
| title_short | Application of electroconsolidation of powder components for production of ultradenced ceramics Al₂O₃ and ZrO₂ (3% Y₂O₃) |
| title_sort | application of electroconsolidation of powder components for production of ultradenced ceramics al₂o₃ and zro₂ (3% y₂o₃) |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/100314 |
| work_keys_str_mv | AT sayenkosyu applicationofelectroconsolidationofpowdercomponentsforproductionofultradencedceramicsal2o3andzro23y2o3 AT svitlychniyeuo applicationofelectroconsolidationofpowdercomponentsforproductionofultradencedceramicsal2o3andzro23y2o3 AT lobachkv applicationofelectroconsolidationofpowdercomponentsforproductionofultradencedceramicsal2o3andzro23y2o3 AT sayenkosyu primenenieélektrokonsolidaciiporoškovyhkomponentovdlâpolučeniâosoboplotnoikeramikial2o3izro23y2o3 AT svitlychniyeuo primenenieélektrokonsolidaciiporoškovyhkomponentovdlâpolučeniâosoboplotnoikeramikial2o3izro23y2o3 AT lobachkv primenenieélektrokonsolidaciiporoškovyhkomponentovdlâpolučeniâosoboplotnoikeramikial2o3izro23y2o3 AT sayenkosyu zastusovannâelektrokonsolídacííporoškovihkomponentívdlâotrimannâosoblivoŝílʹnoíkeramíkial2o3tazro23y2o3 AT svitlychniyeuo zastusovannâelektrokonsolídacííporoškovihkomponentívdlâotrimannâosoblivoŝílʹnoíkeramíkial2o3tazro23y2o3 AT lobachkv zastusovannâelektrokonsolídacííporoškovihkomponentívdlâotrimannâosoblivoŝílʹnoíkeramíkial2o3tazro23y2o3 |