Formation of Aluminium Surface Layers’ Structure during Laser Alloying with Copper and Cobalt Powders

• Published in: Металлофизика и новейшие технологии
• Date: 2013
• Main Authors: Girzhon, V.V., Kovalyova, V.M., Smolyakov, O.V.
• Format: Article
• Language: English
• Published: Інститут металофізики ім. Г.В. Курдюмова НАН України 2013
• Subjects: Металлические поверхности и плёнки
• Online Access: https://nasplib.isofts.kiev.ua/handle/123456789/104180
• Journal Title: Digital Library of Periodicals of National Academy of Sciences of Ukraine
• Cite this: Formation of Aluminium Surface Layers’ Structure during Laser Alloying with Copper and Cobalt Powders / V.V. Girzhon, V.M. Kovalyova, O.V. Smolyakov // Металлофизика и новейшие технологии. — 2013. — Т. 35, № 8. — С. 1095-1100. — Бібліогр.: 12 назв. — рос.

Possibility of quasi-crystal decagonal phase formation in the surface layers of aluminium during laser alloying is demonstrated. Alloying is carried out by mixture of copper and cobalt powders with atomic ratio 1:1. The phase state of laser alloying zone is thermally stable up to the temperatures close to the matrix melting point. Показано можливість одержання квазикристалічної декагональної фази в поверхневих шарах алюмінію при лазерному леґуванні. Леґування ви-конувалося сумішшю порошків міді і кобальту з атомним відношенням 1:1. Встановлено, що структурно-фазовий стан зони леґування характе-ризується термічною стійкістю аж до температур, близьких до темпера-тури топлення матеріалу матриці. Показана возможность получения квазикристаллической декагональной фазы в поверхностных слоях алюминия при лазерном легировании. Ле-гирование выполнялось смесью порошков меди и кобальта с атомным от-ношением 1:1. Установлено, что структурно-фазовое состояние зоны ле-гирования характеризуется термической устойчивостью вплоть до темпе-ратур, близких к температуре плавления материала матрицы.