Strength Degradation of Glass Fiber Reinforced Polymer Bars Subjected to Reversed Cyclic Load
Glass fiber reinforced polymer (GFRP) due to
 its corrosion resistance is gaining popularity in
 the civil engineering community, as an alternative
 material to steel reinforcement. GFRP reinforced
 bar (rebar) has a high tensile strength
 with moderate elasti...
Gespeichert in:
| Veröffentlicht in: | Проблемы прочности |
|---|---|
| Datum: | 2014 |
| Hauptverfasser: | , , , |
| Format: | Artikel |
| Sprache: | Englisch |
| Veröffentlicht: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2014
|
| Schlagworte: | |
| Online Zugang: | https://nasplib.isofts.kiev.ua/handle/123456789/112713 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Strength Degradation of Glass Fiber Reinforced Polymer Bars Subjected to Reversed Cyclic Load / J.Y. Lee, K.H. Kim, S.W. Kim, M. Chang // Проблемы прочности. — 2014. — № 2. — С. 98-105. — Бібліогр.: 16 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862686102011248640 |
|---|---|
| author | Lee, J.Y. Kim, K.H. Kim, S.W. Chang, M. |
| author_facet | Lee, J.Y. Kim, K.H. Kim, S.W. Chang, M. |
| citation_txt | Strength Degradation of Glass Fiber Reinforced Polymer Bars Subjected to Reversed Cyclic Load / J.Y. Lee, K.H. Kim, S.W. Kim, M. Chang // Проблемы прочности. — 2014. — № 2. — С. 98-105. — Бібліогр.: 16 назв. — англ. |
| collection | DSpace DC |
| container_title | Проблемы прочности |
| description | Glass fiber reinforced polymer (GFRP) due to
its corrosion resistance is gaining popularity in
the civil engineering community, as an alternative
material to steel reinforcement. GFRP reinforced
bar (rebar) has a high tensile strength
with moderate elastic modulus and is elastic up
to failure. However, it should not be treated in
the same way as steel rebar because the interfacial
bond behavior of GFRP bars to concrete is
expected to vary from that of conventional steel
bars, since various parameters that influence
bond performance are different. This paper presents
the results of an experimental and analytical
studies on the bond strength of glass fiber
reinforced polymer bars subjected to monotonic
or reversed cyclic loads. The experimental program
consisted of 30 test specimens. The test results
indicated that the interfacial strength of the
GFRP bars was quite different to that of the
steel bars. In addition, the strength degradation
of GFRP bars subjected to reversed cyclic load
was more severe than that of the GFRP bars
subjected to a monotonic load.
Полимеры, армированные стекловолокном, имеют повышенную коррозионную стойкость, по-этому используются в строительстве в качестве альтернативы стальной арматуре. Арматурный стержень, армированный стекловолокном, обладает высоким пределом прочности
при растяжении, средним модулем упругости и упругим поведением вплоть до разрушения.
При расчете данного стержня необходимо использовать нетрадиционный подход, поскольку
предполагается, что связь на границе раздела между арматурным стержнем, армированным
стекловолокном, и бетоном отличается от таковой для традиционных стальных стержней,
так как параметры, оказывающие влияние на прочностную характеристику, имеют разные
значения. Представлены результаты экспериментальных и аналитических исследований по
оценке прочности связи полимерных стержней, армированных стекловолокном, при монотонной или циклической переменной нагрузке. Для экспериментальных исследований использовали 30 образцов. Установлено, что значения прочности при сдвиге по поверхности раздела
для полимерных стержней, армированных стекловолокном, отличаются от таковых для
стальных стержней. Процесс разупрочнения полимерных стержней, армированных стекловолокном, при циклической переменной нагрузке более жесткий, чем при монотонной нагрузке.
Полімери, армовані скловолокном, мають підвищену корозійну стійкість, тому використовуються на будівництві як альтернатива стальній арматурі. Арматурний стрижень, армований скловолокном, має високу границю міцності при розтязі, середній
модуль пружності і пружну поведінку майже до руйнування. Для розрахунку даного
стрижня необхідно використовувати нетрадиційний підхід, оскільки припускається,
що зв’язок на границі поділу між арматурним стрижнем, армованим скловолокном, і
бетоном відрізняється від такого для традиційних стальних стрижнів, оскільки параметри, що мають вплив на міцнісну характеристику, мають різні значення. Представлено результати експериментальних і аналітичних досліджень щодо оцінки міцності зв’язку полімерних стрижнів, армованих скловолокном, за монотонного або
циклічного змінного навантаження. Для експериментальних випробувань використовували 30 зразків. Установлено, що значення міцності при зсуві по поверхні поділу
для полімерних стрижнів, армованих скловолокном, відрізняються від таких для
стальних. Процес знеміцнення полімерних стрижнів, армованих скловолокном, під
час циклічного змінного навантаження більш жорсткий, аніж за монотонного навантаження.
|
| first_indexed | 2025-12-07T16:03:12Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-112713 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 0556-171X |
| language | English |
| last_indexed | 2025-12-07T16:03:12Z |
| publishDate | 2014 |
| publisher | Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| record_format | dspace |
| spelling | Lee, J.Y. Kim, K.H. Kim, S.W. Chang, M. 2017-01-26T18:51:18Z 2017-01-26T18:51:18Z 2014 Strength Degradation of Glass Fiber Reinforced Polymer Bars Subjected to Reversed Cyclic Load / J.Y. Lee, K.H. Kim, S.W. Kim, M. Chang // Проблемы прочности. — 2014. — № 2. — С. 98-105. — Бібліогр.: 16 назв. — англ. 0556-171X https://nasplib.isofts.kiev.ua/handle/123456789/112713 539.4 Glass fiber reinforced polymer (GFRP) due to
 its corrosion resistance is gaining popularity in
 the civil engineering community, as an alternative
 material to steel reinforcement. GFRP reinforced
 bar (rebar) has a high tensile strength
 with moderate elastic modulus and is elastic up
 to failure. However, it should not be treated in
 the same way as steel rebar because the interfacial
 bond behavior of GFRP bars to concrete is
 expected to vary from that of conventional steel
 bars, since various parameters that influence
 bond performance are different. This paper presents
 the results of an experimental and analytical
 studies on the bond strength of glass fiber
 reinforced polymer bars subjected to monotonic
 or reversed cyclic loads. The experimental program
 consisted of 30 test specimens. The test results
 indicated that the interfacial strength of the
 GFRP bars was quite different to that of the
 steel bars. In addition, the strength degradation
 of GFRP bars subjected to reversed cyclic load
 was more severe than that of the GFRP bars
 subjected to a monotonic load. Полимеры, армированные стекловолокном, имеют повышенную коррозионную стойкость, по-этому используются в строительстве в качестве альтернативы стальной арматуре. Арматурный стержень, армированный стекловолокном, обладает высоким пределом прочности
 при растяжении, средним модулем упругости и упругим поведением вплоть до разрушения.
 При расчете данного стержня необходимо использовать нетрадиционный подход, поскольку
 предполагается, что связь на границе раздела между арматурным стержнем, армированным
 стекловолокном, и бетоном отличается от таковой для традиционных стальных стержней,
 так как параметры, оказывающие влияние на прочностную характеристику, имеют разные
 значения. Представлены результаты экспериментальных и аналитических исследований по
 оценке прочности связи полимерных стержней, армированных стекловолокном, при монотонной или циклической переменной нагрузке. Для экспериментальных исследований использовали 30 образцов. Установлено, что значения прочности при сдвиге по поверхности раздела
 для полимерных стержней, армированных стекловолокном, отличаются от таковых для
 стальных стержней. Процесс разупрочнения полимерных стержней, армированных стекловолокном, при циклической переменной нагрузке более жесткий, чем при монотонной нагрузке. Полімери, армовані скловолокном, мають підвищену корозійну стійкість, тому використовуються на будівництві як альтернатива стальній арматурі. Арматурний стрижень, армований скловолокном, має високу границю міцності при розтязі, середній
 модуль пружності і пружну поведінку майже до руйнування. Для розрахунку даного
 стрижня необхідно використовувати нетрадиційний підхід, оскільки припускається,
 що зв’язок на границі поділу між арматурним стрижнем, армованим скловолокном, і
 бетоном відрізняється від такого для традиційних стальних стрижнів, оскільки параметри, що мають вплив на міцнісну характеристику, мають різні значення. Представлено результати експериментальних і аналітичних досліджень щодо оцінки міцності зв’язку полімерних стрижнів, армованих скловолокном, за монотонного або
 циклічного змінного навантаження. Для експериментальних випробувань використовували 30 зразків. Установлено, що значення міцності при зсуві по поверхні поділу
 для полімерних стрижнів, армованих скловолокном, відрізняються від таких для
 стальних. Процес знеміцнення полімерних стрижнів, армованих скловолокном, під
 час циклічного змінного навантаження більш жорсткий, аніж за монотонного навантаження. This research was supported by Basic Science Research Program
 through the National Research Foundation of Korea (NRF) funded by the Ministry of
 Education (2013006697) en Інститут проблем міцності ім. Г.С. Писаренко НАН України Проблемы прочности Научно-технический раздел Strength Degradation of Glass Fiber Reinforced Polymer Bars Subjected to Reversed Cyclic Load Разупрочнение полимерных стержней, армированных стекловолокном, при циклической переменной нагрузке Article published earlier |
| spellingShingle | Strength Degradation of Glass Fiber Reinforced Polymer Bars Subjected to Reversed Cyclic Load Lee, J.Y. Kim, K.H. Kim, S.W. Chang, M. Научно-технический раздел |
| title | Strength Degradation of Glass Fiber Reinforced Polymer Bars Subjected to Reversed Cyclic Load |
| title_alt | Разупрочнение полимерных стержней, армированных стекловолокном, при циклической переменной нагрузке |
| title_full | Strength Degradation of Glass Fiber Reinforced Polymer Bars Subjected to Reversed Cyclic Load |
| title_fullStr | Strength Degradation of Glass Fiber Reinforced Polymer Bars Subjected to Reversed Cyclic Load |
| title_full_unstemmed | Strength Degradation of Glass Fiber Reinforced Polymer Bars Subjected to Reversed Cyclic Load |
| title_short | Strength Degradation of Glass Fiber Reinforced Polymer Bars Subjected to Reversed Cyclic Load |
| title_sort | strength degradation of glass fiber reinforced polymer bars subjected to reversed cyclic load |
| topic | Научно-технический раздел |
| topic_facet | Научно-технический раздел |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/112713 |
| work_keys_str_mv | AT leejy strengthdegradationofglassfiberreinforcedpolymerbarssubjectedtoreversedcyclicload AT kimkh strengthdegradationofglassfiberreinforcedpolymerbarssubjectedtoreversedcyclicload AT kimsw strengthdegradationofglassfiberreinforcedpolymerbarssubjectedtoreversedcyclicload AT changm strengthdegradationofglassfiberreinforcedpolymerbarssubjectedtoreversedcyclicload AT leejy razupročneniepolimernyhsteržneiarmirovannyhsteklovoloknompricikličeskoiperemennoinagruzke AT kimkh razupročneniepolimernyhsteržneiarmirovannyhsteklovoloknompricikličeskoiperemennoinagruzke AT kimsw razupročneniepolimernyhsteržneiarmirovannyhsteklovoloknompricikličeskoiperemennoinagruzke AT changm razupročneniepolimernyhsteržneiarmirovannyhsteklovoloknompricikličeskoiperemennoinagruzke |