On melting of boron phosphide under pressure

• Veröffentlicht in: Сверхтвердые материалы
• Datum: 2015
• Hauptverfasser: Solozhenko, V.L., Mukhanov, V.A.
• Format: Artikel
• Sprache: English
• Veröffentlicht: Інститут надтвердих матеріалів ім. В.М. Бакуля НАН України 2015
• Schlagworte: Письма в редакцию
• Online Zugang: https://nasplib.isofts.kiev.ua/handle/123456789/129924
• Назва журналу: Digital Library of Periodicals of National Academy of Sciences of Ukraine
• Zitieren: On melting of boron phosphide under pressure / V.L. Solozhenko, V.A. Mukhanov // Сверхтвердые материалы. — 2015. — № 6. — С. 98-100. — Бібліогр.: 144 назв. — англ.

Melting of cubic boron phosphide has been studied at pressures to 9 GPa using synchrotron X-ray diffraction and electrical resistivity measurements. It has been found that above 2.6 GPa boron phosphide melts congruently, and the melting curve exhibits negative slope (–60±7 K/GPa), which is indicative of a higher density of the melt as compared to the solid phase. Плавление кубического фосфида бора было изучено при давлениях до 9 ГПа методами дифракции синхротронного излучения и измерения электрического сопротивления. Было установлено, что выше 2,6 ГПа фосфид бора плавится конгруэнтно, и кривая плавления имеет отрицательный наклон (-60±7 K/ГПа), что свидетельствует о более высокой плотности расплава по сравнению с твердой фазой. Плавлення кубічного фосфіду бору було вивчено при тисках до 9 ГПа методами дифракції синхротронного випромінювання і вимірювання електричного опору. Було встановлено, що вище 2,6 ГПа фосфід бору плавиться конґруентно і крива плавлення має негативний нахил (-60±7 K/ГПа), що свідчить про більш високої щільності розплаву в порівнянні з твердою фазою.