Analysis of Metal Corrosion under Conditions of Mechanical Impacts and Aggressive Environments
Based on standpoints of the surface physics, fracture mechanics and electrochemistry, a mathematical model of the physical and chemical processes near the crack tip of a metal under mechanical loads in aqueous electrolyte solutions is developed. Calculations of the energy and electrochemical charact...
Збережено в:
| Опубліковано в: : | Металлофизика и новейшие технологии |
|---|---|
| Дата: | 2017 |
| Автори: | , , |
| Формат: | Стаття |
| Мова: | Англійська |
| Опубліковано: |
Інститут металофізики ім. Г.В. Курдюмова НАН України
2017
|
| Теми: | |
| Онлайн доступ: | https://nasplib.isofts.kiev.ua/handle/123456789/130471 |
| Теги: |
Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Цитувати: | Analysis of Metal Corrosion under Conditions of Mechanical Impacts and Aggressive Environments / V.M. Yuzevych, R.M. Dzhala, B.P. Koman // Металлофизика и новейшие технологии. — 2017. — Т. 39, № 12. — С. 1655-1667. — Бібліогр.: 16 назв. — англ. |
Репозитарії
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862748110137065472 |
|---|---|
| author | Yuzevych, V.M. Dzhala, R.M. Koman, B.P. |
| author_facet | Yuzevych, V.M. Dzhala, R.M. Koman, B.P. |
| citation_txt | Analysis of Metal Corrosion under Conditions of Mechanical Impacts and Aggressive Environments / V.M. Yuzevych, R.M. Dzhala, B.P. Koman // Металлофизика и новейшие технологии. — 2017. — Т. 39, № 12. — С. 1655-1667. — Бібліогр.: 16 назв. — англ. |
| collection | DSpace DC |
| container_title | Металлофизика и новейшие технологии |
| description | Based on standpoints of the surface physics, fracture mechanics and electrochemistry, a mathematical model of the physical and chemical processes near the crack tip of a metal under mechanical loads in aqueous electrolyte solutions is developed. Calculations of the energy and electrochemical characteristics are performed for the steel 20 in the 3% solution of sodium chloride. Parameters of the Tafel-type relationship between the anode current and the difference of electrode potentials are analysed. Well-known Kaeshe expression for the current density on the juvenile surface of a crack bottom is generalized both by linear approximation of the dependence of corrosion current density on surface energy of plastic deformation of the metal and with accounting for increase of mechanical tensile stress up to yield limit.
Исходя из положений физики поверхности, механики разрушения и электрохимии сформулирована математическая модель физико-химических процессов в вершине трещины металла при его механическом нагружении в водном растворе электролита. Проведены расчёты энергетических и электрохимических характеристик для стали 20 в 3% растворе хлорида натрия. Проанализированы параметры уравнения типа Тафеля между анодным током и разницей электродных потенциалов. В линейном приближении связи плотности коррозионного тока с поверхностной энергией пластического деформирования металла и с учётом увеличения механических растягивающих напряжений до предела текучести обобщено известное соотношение (Kaeshe) для плотности тока на ювенильной поверхности дна трещины.
З позицій фізики поверхні, механіки руйнування та електрохемії сформульовано математичний модель фізико-хемічних процесів у вершині тріщини металу при його механічному навантаженні у водному розчині електроліту. Проведено розрахунки енергетичних та електрохемічних характеристик для криці 20 у 3% розчині хлориду натрію. Проаналізовано параметри рівняння типу Тафелевого між анодним струмом і ріжницею електродних потенціялів. У лінійному наближенні зв’язку густини корозійного струму з поверхневою енергією пластичного деформування металу та з урахуванням зростання механічних розтягувальних напружень до границі плинности узагальнено відоме співвідношення (Kaeshe) для густини струму на ювенільній поверхні дна тріщини.
|
| first_indexed | 2025-12-07T20:54:08Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-130471 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 1024-1809 |
| language | English |
| last_indexed | 2025-12-07T20:54:08Z |
| publishDate | 2017 |
| publisher | Інститут металофізики ім. Г.В. Курдюмова НАН України |
| record_format | dspace |
| spelling | Yuzevych, V.M. Dzhala, R.M. Koman, B.P. 2018-02-13T20:17:47Z 2018-02-13T20:17:47Z 2017 Analysis of Metal Corrosion under Conditions of Mechanical Impacts and Aggressive Environments / V.M. Yuzevych, R.M. Dzhala, B.P. Koman // Металлофизика и новейшие технологии. — 2017. — Т. 39, № 12. — С. 1655-1667. — Бібліогр.: 16 назв. — англ. 1024-1809 PACS: 62.20.mt, 68.35.bd, 68.35.Gy, 68.35.Md, 81.40.Np, 81.65.Kn, 82.45.Bb DOI: doi.org/10.15407/mfint.39.12.1655 https://nasplib.isofts.kiev.ua/handle/123456789/130471 Based on standpoints of the surface physics, fracture mechanics and electrochemistry, a mathematical model of the physical and chemical processes near the crack tip of a metal under mechanical loads in aqueous electrolyte solutions is developed. Calculations of the energy and electrochemical characteristics are performed for the steel 20 in the 3% solution of sodium chloride. Parameters of the Tafel-type relationship between the anode current and the difference of electrode potentials are analysed. Well-known Kaeshe expression for the current density on the juvenile surface of a crack bottom is generalized both by linear approximation of the dependence of corrosion current density on surface energy of plastic deformation of the metal and with accounting for increase of mechanical tensile stress up to yield limit. Исходя из положений физики поверхности, механики разрушения и электрохимии сформулирована математическая модель физико-химических процессов в вершине трещины металла при его механическом нагружении в водном растворе электролита. Проведены расчёты энергетических и электрохимических характеристик для стали 20 в 3% растворе хлорида натрия. Проанализированы параметры уравнения типа Тафеля между анодным током и разницей электродных потенциалов. В линейном приближении связи плотности коррозионного тока с поверхностной энергией пластического деформирования металла и с учётом увеличения механических растягивающих напряжений до предела текучести обобщено известное соотношение (Kaeshe) для плотности тока на ювенильной поверхности дна трещины. З позицій фізики поверхні, механіки руйнування та електрохемії сформульовано математичний модель фізико-хемічних процесів у вершині тріщини металу при його механічному навантаженні у водному розчині електроліту. Проведено розрахунки енергетичних та електрохемічних характеристик для криці 20 у 3% розчині хлориду натрію. Проаналізовано параметри рівняння типу Тафелевого між анодним струмом і ріжницею електродних потенціялів. У лінійному наближенні зв’язку густини корозійного струму з поверхневою енергією пластичного деформування металу та з урахуванням зростання механічних розтягувальних напружень до границі плинности узагальнено відоме співвідношення (Kaeshe) для густини струму на ювенільній поверхні дна тріщини. en Інститут металофізики ім. Г.В. Курдюмова НАН України Металлофизика и новейшие технологии Металлические поверхности и плёнки Analysis of Metal Corrosion under Conditions of Mechanical Impacts and Aggressive Environments Анализ коррозии металлов в условиях механических воздействий и агрессивных сред Аналіза корозії металів в умовах механічних впливів і аґресивних середовищ Article published earlier |
| spellingShingle | Analysis of Metal Corrosion under Conditions of Mechanical Impacts and Aggressive Environments Yuzevych, V.M. Dzhala, R.M. Koman, B.P. Металлические поверхности и плёнки |
| title | Analysis of Metal Corrosion under Conditions of Mechanical Impacts and Aggressive Environments |
| title_alt | Анализ коррозии металлов в условиях механических воздействий и агрессивных сред Аналіза корозії металів в умовах механічних впливів і аґресивних середовищ |
| title_full | Analysis of Metal Corrosion under Conditions of Mechanical Impacts and Aggressive Environments |
| title_fullStr | Analysis of Metal Corrosion under Conditions of Mechanical Impacts and Aggressive Environments |
| title_full_unstemmed | Analysis of Metal Corrosion under Conditions of Mechanical Impacts and Aggressive Environments |
| title_short | Analysis of Metal Corrosion under Conditions of Mechanical Impacts and Aggressive Environments |
| title_sort | analysis of metal corrosion under conditions of mechanical impacts and aggressive environments |
| topic | Металлические поверхности и плёнки |
| topic_facet | Металлические поверхности и плёнки |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/130471 |
| work_keys_str_mv | AT yuzevychvm analysisofmetalcorrosionunderconditionsofmechanicalimpactsandaggressiveenvironments AT dzhalarm analysisofmetalcorrosionunderconditionsofmechanicalimpactsandaggressiveenvironments AT komanbp analysisofmetalcorrosionunderconditionsofmechanicalimpactsandaggressiveenvironments AT yuzevychvm analizkorroziimetallovvusloviâhmehaničeskihvozdeistviiiagressivnyhsred AT dzhalarm analizkorroziimetallovvusloviâhmehaničeskihvozdeistviiiagressivnyhsred AT komanbp analizkorroziimetallovvusloviâhmehaničeskihvozdeistviiiagressivnyhsred AT yuzevychvm analízakorozíímetalívvumovahmehaníčnihvplivívíagresivnihseredoviŝ AT dzhalarm analízakorozíímetalívvumovahmehaníčnihvplivívíagresivnihseredoviŝ AT komanbp analízakorozíímetalívvumovahmehaníčnihvplivívíagresivnihseredoviŝ |