Influence of RRA treatment on microstructure and stress corrosion cracking behavior of spray formed 7075 alloy
The effects of retrogression via under pre-aging on microstructure, mechanical properties and stress corrosion cracking behavior of spray formed 7075 aluminum alloy were investigated by transmission electron microscope, tensile test and slow strain rate test. The results show that with under agin...
Gespeichert in:
| Veröffentlicht in: | Фізико-хімічна механіка матеріалів |
|---|---|
| Datum: | 2015 |
| Hauptverfasser: | , , , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Фізико-механічний інститут ім. Г.В. Карпенка НАН України
2015
|
| Online Zugang: | https://nasplib.isofts.kiev.ua/handle/123456789/135165 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Influence of RRA treatment on microstructure and stress corrosion cracking behavior of spray formed 7075 alloy / Rui-Ming Su, Ying-Dong Qu, Rong-De Li, Jun-Hua You // Фізико-хімічна механіка матеріалів. — 2015. — Т. 51, № 3. — С. 68-75. — Бібліогр.: 23 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| id |
nasplib_isofts_kiev_ua-123456789-135165 |
|---|---|
| record_format |
dspace |
| spelling |
Rui-Ming Su Ying-Dong Qu Rong-De Li Jun-Hua You 2018-06-14T16:21:02Z 2018-06-14T16:21:02Z 2015 Influence of RRA treatment on microstructure and stress corrosion cracking behavior of spray formed 7075 alloy / Rui-Ming Su, Ying-Dong Qu, Rong-De Li, Jun-Hua You // Фізико-хімічна механіка матеріалів. — 2015. — Т. 51, № 3. — С. 68-75. — Бібліогр.: 23 назв. — англ. 0430-6252 https://nasplib.isofts.kiev.ua/handle/123456789/135165 The effects of retrogression via under pre-aging on microstructure, mechanical properties and stress corrosion cracking behavior of spray formed 7075 aluminum alloy were investigated by transmission electron microscope, tensile test and slow strain rate test. The results show that with under aging at 120°C for 16 h as pre-aging, the strength of the alloy can maintain at a high level and grain boundary precipitates are discrete after retrogression and re-aging treatment. However, retrogression treatment is uncontrollable by shortened retrogression period. After retrogression at 200°C for 8 min and re-aging, the ultimate tensile strength, elongation and SCC index of the alloy is 791 MPa, 8.5% and 0.155 respectively. Вивчено вплив RRA-обробки, яка полягає у витримці сплавів після штучного старіння у соляній ванні при 200°С і повторному штучному старінні, на мікроструктуру і механічні властивості алюмінієвого сплаву 7075. Для досліджень використано трансмісійний електронний мікроскоп. Зразки випробовували на розтяг за малої швидкості деформації. Встановлено, що після RRA-обробки вторинні частинки уздовж меж зерен виділяються дискретно. Під час такої обробки при 200°С упродовж 8 min границя міцності за розтягу, відносне видовження та коефіцієнт чутливості до корозійного розтріскування сплаву становлять 791 MPa, 8,5% та 0,155 відповідно. Изучено влияние RRA-обработки, заключающейся в выдержке сплавов после искусственного старения в соляной ванне при 200°С и повторном искусственном старении, на микроструктуру и механические свойства алюминиевого сплава 7075. Для исследований использован трасмиссионный електронный микроскоп. Образцы испытывали на растяжение и при малой скорости деформации. Выявлено, что после RRA-обработке вторичные частицы вдоль границ зерен выделяются дискретно. При такой бработке при 200°С в течение 8 min предел прочности при растяжении, относительное удлинение и коэффициент чувствительности к коррозионному растрескиванию сплава составляют 791 MPa, 8,5% и 0,155 соответственно. Acknowledgements. This research was financially supported by the Program for Liaoning Innovative Research Team in University (LT2012004) and Fok Ying-Tong Education Foundation (121054). en Фізико-механічний інститут ім. Г.В. Карпенка НАН України Фізико-хімічна механіка матеріалів Influence of RRA treatment on microstructure and stress corrosion cracking behavior of spray formed 7075 alloy Вплив RRA-обробки на мікроструктуру та корозійне розтріскування алюмінієвого сплаву 7075 Влияние RRA- обработки на микроструктуру и коррозионное растрескивание алюминиевого сплава 7075 Article published earlier |
| institution |
Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| collection |
DSpace DC |
| title |
Influence of RRA treatment on microstructure and stress corrosion cracking behavior of spray formed 7075 alloy |
| spellingShingle |
Influence of RRA treatment on microstructure and stress corrosion cracking behavior of spray formed 7075 alloy Rui-Ming Su Ying-Dong Qu Rong-De Li Jun-Hua You |
| title_short |
Influence of RRA treatment on microstructure and stress corrosion cracking behavior of spray formed 7075 alloy |
| title_full |
Influence of RRA treatment on microstructure and stress corrosion cracking behavior of spray formed 7075 alloy |
| title_fullStr |
Influence of RRA treatment on microstructure and stress corrosion cracking behavior of spray formed 7075 alloy |
| title_full_unstemmed |
Influence of RRA treatment on microstructure and stress corrosion cracking behavior of spray formed 7075 alloy |
| title_sort |
influence of rra treatment on microstructure and stress corrosion cracking behavior of spray formed 7075 alloy |
| author |
Rui-Ming Su Ying-Dong Qu Rong-De Li Jun-Hua You |
| author_facet |
Rui-Ming Su Ying-Dong Qu Rong-De Li Jun-Hua You |
| publishDate |
2015 |
| language |
English |
| container_title |
Фізико-хімічна механіка матеріалів |
| publisher |
Фізико-механічний інститут ім. Г.В. Карпенка НАН України |
| format |
Article |
| title_alt |
Вплив RRA-обробки на мікроструктуру та корозійне розтріскування алюмінієвого сплаву 7075 Влияние RRA- обработки на микроструктуру и коррозионное растрескивание алюминиевого сплава 7075 |
| description |
The effects of retrogression via under pre-aging on microstructure, mechanical properties
and stress corrosion cracking behavior of spray formed 7075 aluminum alloy were investigated
by transmission electron microscope, tensile test and slow strain rate test. The results
show that with under aging at 120°C for 16 h as pre-aging, the strength of the alloy can
maintain at a high level and grain boundary precipitates are discrete after retrogression and
re-aging treatment. However, retrogression treatment is uncontrollable by shortened retrogression
period. After retrogression at 200°C for 8 min and re-aging, the ultimate tensile
strength, elongation and SCC index of the alloy is 791 MPa, 8.5% and 0.155 respectively.
Вивчено вплив RRA-обробки, яка полягає у витримці сплавів після штучного старіння у соляній ванні при 200°С і повторному штучному старінні, на мікроструктуру і механічні властивості алюмінієвого сплаву 7075. Для досліджень використано
трансмісійний електронний мікроскоп. Зразки випробовували на розтяг за малої швидкості деформації. Встановлено, що після RRA-обробки вторинні частинки уздовж меж зерен
виділяються дискретно. Під час такої обробки при 200°С упродовж 8 min границя міцності за розтягу, відносне видовження та коефіцієнт чутливості до корозійного розтріскування сплаву становлять 791 MPa, 8,5% та 0,155 відповідно.
Изучено влияние RRA-обработки, заключающейся в выдержке сплавов
после искусственного старения в соляной ванне при 200°С и повторном искусственном
старении, на микроструктуру и механические свойства алюминиевого сплава 7075. Для
исследований использован трасмиссионный електронный микроскоп. Образцы испытывали на растяжение и при малой скорости деформации. Выявлено, что после RRA-обработке вторичные частицы вдоль границ зерен выделяются дискретно. При такой бработке
при 200°С в течение 8 min предел прочности при растяжении, относительное удлинение и
коэффициент чувствительности к коррозионному растрескиванию сплава составляют
791 MPa, 8,5% и 0,155 соответственно.
|
| issn |
0430-6252 |
| url |
https://nasplib.isofts.kiev.ua/handle/123456789/135165 |
| citation_txt |
Influence of RRA treatment on microstructure and stress corrosion cracking behavior of spray formed 7075 alloy / Rui-Ming Su, Ying-Dong Qu, Rong-De Li, Jun-Hua You // Фізико-хімічна механіка матеріалів. — 2015. — Т. 51, № 3. — С. 68-75. — Бібліогр.: 23 назв. — англ. |
| work_keys_str_mv |
AT ruimingsu influenceofrratreatmentonmicrostructureandstresscorrosioncrackingbehaviorofsprayformed7075alloy AT yingdongqu influenceofrratreatmentonmicrostructureandstresscorrosioncrackingbehaviorofsprayformed7075alloy AT rongdeli influenceofrratreatmentonmicrostructureandstresscorrosioncrackingbehaviorofsprayformed7075alloy AT junhuayou influenceofrratreatmentonmicrostructureandstresscorrosioncrackingbehaviorofsprayformed7075alloy AT ruimingsu vplivrraobrobkinamíkrostrukturutakorozíineroztrískuvannâalûmíníêvogosplavu7075 AT yingdongqu vplivrraobrobkinamíkrostrukturutakorozíineroztrískuvannâalûmíníêvogosplavu7075 AT rongdeli vplivrraobrobkinamíkrostrukturutakorozíineroztrískuvannâalûmíníêvogosplavu7075 AT junhuayou vplivrraobrobkinamíkrostrukturutakorozíineroztrískuvannâalûmíníêvogosplavu7075 AT ruimingsu vliânierraobrabotkinamikrostrukturuikorrozionnoerastreskivaniealûminievogosplava7075 AT yingdongqu vliânierraobrabotkinamikrostrukturuikorrozionnoerastreskivaniealûminievogosplava7075 AT rongdeli vliânierraobrabotkinamikrostrukturuikorrozionnoerastreskivaniealûminievogosplava7075 AT junhuayou vliânierraobrabotkinamikrostrukturuikorrozionnoerastreskivaniealûminievogosplava7075 |
| first_indexed |
2025-12-07T20:15:46Z |
| last_indexed |
2025-12-07T20:15:46Z |
| _version_ |
1850881917010837504 |