The effect of architecture of Cu/Ni-Cu multilayer coatings on their microhardness
The results of measuring of the microhardness of Cu/(Ni-Cu) multilayer coatings are reported. These coatings were deposited from the pyrophosphate-ammonium electrolyte. It is shown that the microhardness of the multilayer coatings strongly depends on their architecture, as long as coatings were form...
Gespeichert in:
| Datum: | 2012 |
|---|---|
| Hauptverfasser: | , , , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
НТК «Інститут монокристалів» НАН України
2012
|
| Schriftenreihe: | Functional Materials |
| Schlagworte: | |
| Online Zugang: | https://nasplib.isofts.kiev.ua/handle/123456789/135293 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | The effect of architecture of Cu/Ni-Cu multilayer coatings on their microhardness / A.A. Maizelis, B.I. Bairachniy, L.V. Trubnikova, B.A. Savitsky // Functional Materials. — 2012. — Т. 19, № 2. — С. 238-244. — Бібліогр.: 22 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| Zusammenfassung: | The results of measuring of the microhardness of Cu/(Ni-Cu) multilayer coatings are reported. These coatings were deposited from the pyrophosphate-ammonium electrolyte. It is shown that the microhardness of the multilayer coatings strongly depends on their architecture, as long as coatings were formed from the layers under the identical optimal conditions. The microhardness reaches its maximum when the bilayer thickness is in the range of 40-60 nm and the Ni-Cu and Cu layers thicknesses ratio is in the range of 1.8-2.5. For each layer thickness ratio, the microhardness has the maximum at its own bi layer thickness range. |
|---|