Effect of prolonged holding under contact loading on the peculiarities of phase changes in silicon
It was shown that prolonged holding under the peak load during indentation of Si (100) led
 to the creep of material even at room temperature that became possible due to the phase
 transition into more plastic metallic b-Sn phase. The end structural phases in the indentation
...
Saved in:
| Published in: | Фізико-хімічна механіка матеріалів |
|---|---|
| Date: | 2015 |
| Main Authors: | , , |
| Format: | Article |
| Language: | English |
| Published: |
Фізико-механічний інститут ім. Г.В. Карпенка НАН України
2015
|
| Online Access: | https://nasplib.isofts.kiev.ua/handle/123456789/135757 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Journal Title: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Cite this: | Effect of prolonged holding under contact loading on the peculiarities of phase changes in silicon / O. Shikimaka, A. Prisacaru, A. Burlacu // Фізико-хімічна механіка матеріалів. — 2015. — Т. 51, № 3. — С. 100-106. — Бібліогр.: 15 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862690254379548672 |
|---|---|
| author | Shikimaka, O. Prisacaru, A. Burlacu, A. |
| author_facet | Shikimaka, O. Prisacaru, A. Burlacu, A. |
| citation_txt | Effect of prolonged holding under contact loading on the peculiarities of phase changes in silicon / O. Shikimaka, A. Prisacaru, A. Burlacu // Фізико-хімічна механіка матеріалів. — 2015. — Т. 51, № 3. — С. 100-106. — Бібліогр.: 15 назв. — англ. |
| collection | DSpace DC |
| container_title | Фізико-хімічна механіка матеріалів |
| description | It was shown that prolonged holding under the peak load during indentation of Si (100) led
to the creep of material even at room temperature that became possible due to the phase
transition into more plastic metallic b-Sn phase. The end structural phases in the indentation
zone, studied by micro-Raman spectroscopy were found to be affected by the longer
holding under the load and demonstrated more intensive peaks for amorphous phase (a-Si)
in the depth of the indentation comparatively with those for short holding indentations.
It was suggested that this effect was caused by the activation of the dislocation mechanism
of a-Si formation, as a result of longer shear stresses action under prolonged holding. This
fact induced some changes in the kinetics of the unloading events, which demonstrated the
tendency to the “kink pop-out” formation instead of typical “pop-out” and “elbow”.
Досліджено вплив тривалої витримки під час індентування на особливості фазових перетворень і деформації кремнію Si (100). Показано, що тривала витримка за
максимального навантаження призводить до повзучості матеріалу навіть за кімнатної температури завдяки фазовому перетворенню на пластичнішу металеву b-Sn фазу. Кінцеві структурні фази в зоні відбитка, виявлені за допомогою мікро-Рамановської спектроскопії, вказують на інтенсифікацію утворення аморфної фази (a-Si) зі зростанням часу
витримки. Передбачається, що причина цієї додаткової аморфізації може мати дислокаційну природу, як результат зростання щільності дислокацій під час повзучості і перебудови дислокаційної структури під час розвантаження. Цей факт вносить деякі зміни до
кінетики розвантажувальних явищ, які демонструють тенденцію до утворення “kink popout”
замість типових “pop-out” і “elbow”.
Исследованно влияние длительной выдержки при индентировании на
особенности фазовых превращений и деформирования кремния Si (100). Показано, что
длительная выдержка при максимальной нагрузке ведет к ползучести материала даже при
комнатной температуре благодаря фазовому превращению в более пластическую металлическую b-Sn фазу. Конечные структурные фазы в зоне отпечатка, выявленные посредством микро-Рамановской спектроскопии, указывают на интенсификацию образования
аморфной фазы (a-Si) с ростом времени выдержки. Предполагается, что причина этой дополнительной аморфизации может иметь дислокационную природу, как результат роста
плотности дислокаций во время ползучести и перестройки дислокационной структуры во
время разгрузки. Этот факт вносит некоторые изменения в кинетику разгрузочных явлений, которые демонстрируют тенденцию к образованию “kink pop-out” вместо типичных
“pop-out” и “elbow”.
|
| first_indexed | 2025-12-07T16:13:49Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-135757 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 0430-6252 |
| language | English |
| last_indexed | 2025-12-07T16:13:49Z |
| publishDate | 2015 |
| publisher | Фізико-механічний інститут ім. Г.В. Карпенка НАН України |
| record_format | dspace |
| spelling | Shikimaka, O. Prisacaru, A. Burlacu, A. 2018-06-15T14:38:10Z 2018-06-15T14:38:10Z 2015 Effect of prolonged holding under contact loading on the peculiarities of phase changes in silicon / O. Shikimaka, A. Prisacaru, A. Burlacu // Фізико-хімічна механіка матеріалів. — 2015. — Т. 51, № 3. — С. 100-106. — Бібліогр.: 15 назв. — англ. 0430-6252 https://nasplib.isofts.kiev.ua/handle/123456789/135757 It was shown that prolonged holding under the peak load during indentation of Si (100) led
 to the creep of material even at room temperature that became possible due to the phase
 transition into more plastic metallic b-Sn phase. The end structural phases in the indentation
 zone, studied by micro-Raman spectroscopy were found to be affected by the longer
 holding under the load and demonstrated more intensive peaks for amorphous phase (a-Si)
 in the depth of the indentation comparatively with those for short holding indentations.
 It was suggested that this effect was caused by the activation of the dislocation mechanism
 of a-Si formation, as a result of longer shear stresses action under prolonged holding. This
 fact induced some changes in the kinetics of the unloading events, which demonstrated the
 tendency to the “kink pop-out” formation instead of typical “pop-out” and “elbow”. Досліджено вплив тривалої витримки під час індентування на особливості фазових перетворень і деформації кремнію Si (100). Показано, що тривала витримка за
 максимального навантаження призводить до повзучості матеріалу навіть за кімнатної температури завдяки фазовому перетворенню на пластичнішу металеву b-Sn фазу. Кінцеві структурні фази в зоні відбитка, виявлені за допомогою мікро-Рамановської спектроскопії, вказують на інтенсифікацію утворення аморфної фази (a-Si) зі зростанням часу
 витримки. Передбачається, що причина цієї додаткової аморфізації може мати дислокаційну природу, як результат зростання щільності дислокацій під час повзучості і перебудови дислокаційної структури під час розвантаження. Цей факт вносить деякі зміни до
 кінетики розвантажувальних явищ, які демонструють тенденцію до утворення “kink popout”
 замість типових “pop-out” і “elbow”. Исследованно влияние длительной выдержки при индентировании на
 особенности фазовых превращений и деформирования кремния Si (100). Показано, что
 длительная выдержка при максимальной нагрузке ведет к ползучести материала даже при
 комнатной температуре благодаря фазовому превращению в более пластическую металлическую b-Sn фазу. Конечные структурные фазы в зоне отпечатка, выявленные посредством микро-Рамановской спектроскопии, указывают на интенсификацию образования
 аморфной фазы (a-Si) с ростом времени выдержки. Предполагается, что причина этой дополнительной аморфизации может иметь дислокационную природу, как результат роста
 плотности дислокаций во время ползучести и перестройки дислокационной структуры во
 время разгрузки. Этот факт вносит некоторые изменения в кинетику разгрузочных явлений, которые демонстрируют тенденцию к образованию “kink pop-out” вместо типичных
 “pop-out” и “elbow”. en Фізико-механічний інститут ім. Г.В. Карпенка НАН України Фізико-хімічна механіка матеріалів Effect of prolonged holding under contact loading on the peculiarities of phase changes in silicon Вплив тривалої витримки за контактного навантаження на фазові зміни у кремнії Влияние длительной выдержки при контактной нагрузке на фазовые изменения в кремнии Article published earlier |
| spellingShingle | Effect of prolonged holding under contact loading on the peculiarities of phase changes in silicon Shikimaka, O. Prisacaru, A. Burlacu, A. |
| title | Effect of prolonged holding under contact loading on the peculiarities of phase changes in silicon |
| title_alt | Вплив тривалої витримки за контактного навантаження на фазові зміни у кремнії Влияние длительной выдержки при контактной нагрузке на фазовые изменения в кремнии |
| title_full | Effect of prolonged holding under contact loading on the peculiarities of phase changes in silicon |
| title_fullStr | Effect of prolonged holding under contact loading on the peculiarities of phase changes in silicon |
| title_full_unstemmed | Effect of prolonged holding under contact loading on the peculiarities of phase changes in silicon |
| title_short | Effect of prolonged holding under contact loading on the peculiarities of phase changes in silicon |
| title_sort | effect of prolonged holding under contact loading on the peculiarities of phase changes in silicon |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/135757 |
| work_keys_str_mv | AT shikimakao effectofprolongedholdingundercontactloadingonthepeculiaritiesofphasechangesinsilicon AT prisacarua effectofprolongedholdingundercontactloadingonthepeculiaritiesofphasechangesinsilicon AT burlacua effectofprolongedholdingundercontactloadingonthepeculiaritiesofphasechangesinsilicon AT shikimakao vplivtrivaloívitrimkizakontaktnogonavantažennânafazovízmíniukremníí AT prisacarua vplivtrivaloívitrimkizakontaktnogonavantažennânafazovízmíniukremníí AT burlacua vplivtrivaloívitrimkizakontaktnogonavantažennânafazovízmíniukremníí AT shikimakao vliâniedlitelʹnoivyderžkiprikontaktnoinagruzkenafazovyeizmeneniâvkremnii AT prisacarua vliâniedlitelʹnoivyderžkiprikontaktnoinagruzkenafazovyeizmeneniâvkremnii AT burlacua vliâniedlitelʹnoivyderžkiprikontaktnoinagruzkenafazovyeizmeneniâvkremnii |