Peculiarities of stress relaxation of nanostructured alloy Zr1Nb after various influences
Processes of relaxation of internal stresses in the nanocrystalline alloy Zr1Nb after various thermomechanical influences was studied. The relationship of structural states obtained as a result of the relaxation effects with the laws of plastic deformation during creep were established. Shown that h...
Gespeichert in:
| Veröffentlicht in: | Вопросы атомной науки и техники |
|---|---|
| Datum: | 2017 |
| Hauptverfasser: | , , , , |
| Format: | Artikel |
| Sprache: | Englisch |
| Veröffentlicht: |
Національний науковий центр «Харківський фізико-технічний інститут» НАН України
2017
|
| Schlagworte: | |
| Online Zugang: | https://nasplib.isofts.kiev.ua/handle/123456789/136142 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Peculiarities of stress relaxation of nanostructured alloy Zr1Nb after various influences / V.I. Sokolenko, E.V. Karaseva, A.V. Mats, E.S. Savchuk, V.A. Frolov // Вопросы атомной науки и техники. — 2017. — № 4. — С. 79-83. — Бібліогр.: 17 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862695487391399936 |
|---|---|
| author | Sokolenko, V.I. Karaseva, E.V. Mats, A.V. Savchuk, E.S. Frolov, V.A. |
| author_facet | Sokolenko, V.I. Karaseva, E.V. Mats, A.V. Savchuk, E.S. Frolov, V.A. |
| citation_txt | Peculiarities of stress relaxation of nanostructured alloy Zr1Nb after various influences / V.I. Sokolenko, E.V. Karaseva, A.V. Mats, E.S. Savchuk, V.A. Frolov // Вопросы атомной науки и техники. — 2017. — № 4. — С. 79-83. — Бібліогр.: 17 назв. — англ. |
| collection | DSpace DC |
| container_title | Вопросы атомной науки и техники |
| description | Processes of relaxation of internal stresses in the nanocrystalline alloy Zr1Nb after various thermomechanical influences was studied. The relationship of structural states obtained as a result of the relaxation effects with the laws of plastic deformation during creep were established. Shown that heat treatments of nanostructured alloy Zr1Nb, which provide the increase of the plasticity, changed qualitatively the alloy structure, destructing the nanostructured state, that results to decrease of the mechanical characteristics of the material and the degree of resistance to subsequent deformation during the creep at the temperature of 700 K. Ultrasonic processing reduces the level of internal stress of nanostructured material by forming the equilibrium structure of boundaries without noticeable growth of grains. During subsequent creep deformation at 700 K of nanostructured alloy Zr1Nb, subjected to ultrasonic treatment, the relaxation of the internal stresses due to dynamic recrystallization and the formation of new stable nanostructure take place that leads to the marked increase of the material thermomechanical stability.
Досліджували процеси релаксації внутрішніх напружень у нанокристалічному сплаві Zr1Nb після різних механікотермічних впливів. Встановили взаємозв'язок структурних станів, отриманих в результаті релаксаційних впливів з закономірностями розвитку пластичної деформації при повзучості. Показали, що термообробки наноструктурованого сплаву Zr1Nb, які забезпечують підвищення пластичності, якісно змінюють структуру сплаву, руйнуючи наноструктурований стан, що призводить до зниження механічних характеристик і ступеня стійкості матеріалу до наступної деформації в процесі повзучості при температурі 700 К. Ультразвукова обробка призводить до зниження рівня внутрішніх напружень наноструктурованого матеріалу за рахунок формування більш рівноважної структури границь без помітного зростання зерен. У процесі подальшої деформації в умовах повзучості при 700 К наноструктурованого сплаву Zr1Nb, що піддавали ультразвуковому впливу, відбуваються релаксація внутрішніх напружень внаслідок динамічної рекристалізації і утворення нової стабільної наноструктури, що призводить до помітного підвищення термомеханічної стійкості матеріалу.
Исследовали процессы релаксации внутренних напряжений в нанокристаллическом сплаве Zr1Nb после различных механико-термических воздействий. Установили взаимосвязь структурных состояний, полученных в результате релаксационных воздействий с закономерностями развития пластической деформации при ползучести. Показали, что термообработки наноструктурного сплава Zr1Nb, которые обеспечивают повышение пластичности, качественно изменяют структуру сплава, разрушая наноструктурное состояние, что приводит к снижению механических характеристик и степени устойчивости материала к последующей деформации в процессе ползучести при температуре 700 К. Ультразвуковая обработка приводит к снижению уровня внутренних напряжений наноструктурного материала за счет формирования более равновесной структуры границ без заметного роста зерен. В процессе последующей деформации в условиях ползучести при 700 К наноструктурного сплава Zr1Nb, подвергнутого ультразвуковому воздействию, происходят релаксация внутренних напряжений вследствие динамической рекристаллизации и образование новой стабильной наноструктуры, что приводит к заметному повышению термомеханической устойчивости материала.
|
| first_indexed | 2025-12-07T16:24:34Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-136142 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 1562-6016 |
| language | English |
| last_indexed | 2025-12-07T16:24:34Z |
| publishDate | 2017 |
| publisher | Національний науковий центр «Харківський фізико-технічний інститут» НАН України |
| record_format | dspace |
| spelling | Sokolenko, V.I. Karaseva, E.V. Mats, A.V. Savchuk, E.S. Frolov, V.A. 2018-06-16T05:59:22Z 2018-06-16T05:59:22Z 2017 Peculiarities of stress relaxation of nanostructured alloy Zr1Nb after various influences / V.I. Sokolenko, E.V. Karaseva, A.V. Mats, E.S. Savchuk, V.A. Frolov // Вопросы атомной науки и техники. — 2017. — № 4. — С. 79-83. — Бібліогр.: 17 назв. — англ. 1562-6016 https://nasplib.isofts.kiev.ua/handle/123456789/136142 669.296:539.377 Processes of relaxation of internal stresses in the nanocrystalline alloy Zr1Nb after various thermomechanical influences was studied. The relationship of structural states obtained as a result of the relaxation effects with the laws of plastic deformation during creep were established. Shown that heat treatments of nanostructured alloy Zr1Nb, which provide the increase of the plasticity, changed qualitatively the alloy structure, destructing the nanostructured state, that results to decrease of the mechanical characteristics of the material and the degree of resistance to subsequent deformation during the creep at the temperature of 700 K. Ultrasonic processing reduces the level of internal stress of nanostructured material by forming the equilibrium structure of boundaries without noticeable growth of grains. During subsequent creep deformation at 700 K of nanostructured alloy Zr1Nb, subjected to ultrasonic treatment, the relaxation of the internal stresses due to dynamic recrystallization and the formation of new stable nanostructure take place that leads to the marked increase of the material thermomechanical stability. Досліджували процеси релаксації внутрішніх напружень у нанокристалічному сплаві Zr1Nb після різних механікотермічних впливів. Встановили взаємозв'язок структурних станів, отриманих в результаті релаксаційних впливів з закономірностями розвитку пластичної деформації при повзучості. Показали, що термообробки наноструктурованого сплаву Zr1Nb, які забезпечують підвищення пластичності, якісно змінюють структуру сплаву, руйнуючи наноструктурований стан, що призводить до зниження механічних характеристик і ступеня стійкості матеріалу до наступної деформації в процесі повзучості при температурі 700 К. Ультразвукова обробка призводить до зниження рівня внутрішніх напружень наноструктурованого матеріалу за рахунок формування більш рівноважної структури границь без помітного зростання зерен. У процесі подальшої деформації в умовах повзучості при 700 К наноструктурованого сплаву Zr1Nb, що піддавали ультразвуковому впливу, відбуваються релаксація внутрішніх напружень внаслідок динамічної рекристалізації і утворення нової стабільної наноструктури, що призводить до помітного підвищення термомеханічної стійкості матеріалу. Исследовали процессы релаксации внутренних напряжений в нанокристаллическом сплаве Zr1Nb после различных механико-термических воздействий. Установили взаимосвязь структурных состояний, полученных в результате релаксационных воздействий с закономерностями развития пластической деформации при ползучести. Показали, что термообработки наноструктурного сплава Zr1Nb, которые обеспечивают повышение пластичности, качественно изменяют структуру сплава, разрушая наноструктурное состояние, что приводит к снижению механических характеристик и степени устойчивости материала к последующей деформации в процессе ползучести при температуре 700 К. Ультразвуковая обработка приводит к снижению уровня внутренних напряжений наноструктурного материала за счет формирования более равновесной структуры границ без заметного роста зерен. В процессе последующей деформации в условиях ползучести при 700 К наноструктурного сплава Zr1Nb, подвергнутого ультразвуковому воздействию, происходят релаксация внутренних напряжений вследствие динамической рекристаллизации и образование новой стабильной наноструктуры, что приводит к заметному повышению термомеханической устойчивости материала. en Національний науковий центр «Харківський фізико-технічний інститут» НАН України Вопросы атомной науки и техники Материалы реакторов на тепловых и быстрых нейтронах Peculiarities of stress relaxation of nanostructured alloy Zr1Nb after various influences Особливості релаксації напружень наноструктурованого сплаву Zr1Nb після різних впливів Особенности релаксации напряжений наноструктурного сплава Zr1Nb после различных воздействий Article published earlier |
| spellingShingle | Peculiarities of stress relaxation of nanostructured alloy Zr1Nb after various influences Sokolenko, V.I. Karaseva, E.V. Mats, A.V. Savchuk, E.S. Frolov, V.A. Материалы реакторов на тепловых и быстрых нейтронах |
| title | Peculiarities of stress relaxation of nanostructured alloy Zr1Nb after various influences |
| title_alt | Особливості релаксації напружень наноструктурованого сплаву Zr1Nb після різних впливів Особенности релаксации напряжений наноструктурного сплава Zr1Nb после различных воздействий |
| title_full | Peculiarities of stress relaxation of nanostructured alloy Zr1Nb after various influences |
| title_fullStr | Peculiarities of stress relaxation of nanostructured alloy Zr1Nb after various influences |
| title_full_unstemmed | Peculiarities of stress relaxation of nanostructured alloy Zr1Nb after various influences |
| title_short | Peculiarities of stress relaxation of nanostructured alloy Zr1Nb after various influences |
| title_sort | peculiarities of stress relaxation of nanostructured alloy zr1nb after various influences |
| topic | Материалы реакторов на тепловых и быстрых нейтронах |
| topic_facet | Материалы реакторов на тепловых и быстрых нейтронах |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/136142 |
| work_keys_str_mv | AT sokolenkovi peculiaritiesofstressrelaxationofnanostructuredalloyzr1nbaftervariousinfluences AT karasevaev peculiaritiesofstressrelaxationofnanostructuredalloyzr1nbaftervariousinfluences AT matsav peculiaritiesofstressrelaxationofnanostructuredalloyzr1nbaftervariousinfluences AT savchukes peculiaritiesofstressrelaxationofnanostructuredalloyzr1nbaftervariousinfluences AT frolovva peculiaritiesofstressrelaxationofnanostructuredalloyzr1nbaftervariousinfluences AT sokolenkovi osoblivostírelaksacíínapruženʹnanostrukturovanogosplavuzr1nbpíslâríznihvplivív AT karasevaev osoblivostírelaksacíínapruženʹnanostrukturovanogosplavuzr1nbpíslâríznihvplivív AT matsav osoblivostírelaksacíínapruženʹnanostrukturovanogosplavuzr1nbpíslâríznihvplivív AT savchukes osoblivostírelaksacíínapruženʹnanostrukturovanogosplavuzr1nbpíslâríznihvplivív AT frolovva osoblivostírelaksacíínapruženʹnanostrukturovanogosplavuzr1nbpíslâríznihvplivív AT sokolenkovi osobennostirelaksaciinaprâženiinanostrukturnogosplavazr1nbposlerazličnyhvozdeistvii AT karasevaev osobennostirelaksaciinaprâženiinanostrukturnogosplavazr1nbposlerazličnyhvozdeistvii AT matsav osobennostirelaksaciinaprâženiinanostrukturnogosplavazr1nbposlerazličnyhvozdeistvii AT savchukes osobennostirelaksaciinaprâženiinanostrukturnogosplavazr1nbposlerazličnyhvozdeistvii AT frolovva osobennostirelaksaciinaprâženiinanostrukturnogosplavazr1nbposlerazličnyhvozdeistvii |