Study of characteristics of Al + 5 wt.% TiO₂ + 6 wt.% Gr hybrid p/m composite powders prepared by ball milling process
This paper is an attempt to understand the characteristics of Al + TiO₂ + Gr hybrid ball
 milled composite powders, which is anticipated to have large application in the near future.
 Aluminium with titanium dioxide (TiO₂) and graphite (Gr) powders was ball milled in
 order t...
Gespeichert in:
| Veröffentlicht in: | Фізико-хімічна механіка матеріалів |
|---|---|
| Datum: | 2015 |
| Hauptverfasser: | , , |
| Format: | Artikel |
| Sprache: | Englisch |
| Veröffentlicht: |
Фізико-механічний інститут ім. Г.В. Карпенка НАН України
2015
|
| Online Zugang: | https://nasplib.isofts.kiev.ua/handle/123456789/136252 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Study of characteristics of Al + 5 wt.% TiO₂ + 6 wt.% Gr hybrid p/m composite powders prepared by ball milling process / M. Ravichandran, VS. Vidhya, V. Anandakrishanan // Фізико-хімічна механіка матеріалів. — 2015. — Т. 51, № 4. — С. 136-143. — Бібліогр.: 16 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862545354750164992 |
|---|---|
| author | Ravichandran, M. Vidhya, VS. Anandakrishanan, V. |
| author_facet | Ravichandran, M. Vidhya, VS. Anandakrishanan, V. |
| citation_txt | Study of characteristics of Al + 5 wt.% TiO₂ + 6 wt.% Gr hybrid p/m composite powders prepared by ball milling process / M. Ravichandran, VS. Vidhya, V. Anandakrishanan // Фізико-хімічна механіка матеріалів. — 2015. — Т. 51, № 4. — С. 136-143. — Бібліогр.: 16 назв. — англ. |
| collection | DSpace DC |
| container_title | Фізико-хімічна механіка матеріалів |
| description | This paper is an attempt to understand the characteristics of Al + TiO₂ + Gr hybrid ball
milled composite powders, which is anticipated to have large application in the near future.
Aluminium with titanium dioxide (TiO₂) and graphite (Gr) powders was ball milled in
order to yield the composition like: Al + 0% TiO₂, Al + 5% TiO₂, Al + 5% TiO₂ + 2% Gr,
Al + 5% TiO₂ + 4% Gr and Al + 5% TiO₂ + 6% Gr. From the X-Ray diffraction analysis
of the milled powders, the grain size, lattice space, lattice constant, stress, strain, dislocation
density and unit cell volume were calculated. Compressibility was performed in a
hardened steel die at pressures between 100 to 500 MPa to determine Al with 5 wt.% TiO₂
and 2 & 4 wt.% of Gr powder mixtures. For understanding of compaction behavior of aluminum
based hybrid composites reinforced with TiO₂ and Gr particles under various
applied pressure conditions, experimental research has been made using several powder
compaction equations. Microstructure analysis for Al + 5% TiO₂ + 6% Gr composite has
been reported.
Вивчали характеристики композитних порошків Al + TiO₂ + Gr. Композити складу Al + 0% TiO₂, Al + 5% TiO₂, Al + 5% TiO₂ + 2% Gr, Al + 5% TiO₂ + 4% Gr та
Al + 5% TiO₂ + 6% Gr отримували шляхом кульового помелу відповідних компонентів.
Для визначення розмірів зерен, параметрів кристалічної решітки, напруження, деформації, густини дислокацій та об’єму елементарної комірки використовували рентгенівський
дифракційний аналіз. Здатність до компактування Al з сумішшю порошків 5 wt.% TiO₂ та
2 і 4 wt.% Gr визначали в гартованих сталевих прес-формах за тиску 100… 500 МPа. Для
розуміння особливостей компактування гібридних композитів на основі Al, зміцнених
частинками TiO₂ та Gr за різних тисків, виконували експериментальні дослідження з
використанням декількох підходів. Наведено мікроструктурний аналіз композита
Al + 5% TiO₂ + 6% Gr.
Изучали характеристики композитных порошков Al + TiO₂ + Gr. Композиты состава Al + 0% TiO₂, Al + 5% TiO₂, Al + 5% TiO₂ + 2% Gr, Al + 5% TiO₂ + + 4% Gr и
Al + 5% TiO₂ + 6% Gr получали путем шарового помола соответствующих компонентов.
Для определения размеров зерен, параметров кристаллической решетки, напряжения,
деформации, плотности дислокаций и объема элементарной ячейки использовали рентгеновский дифракционный анализ. Способность к компактированию Al со смесью порошков 5 wt.% TiO₂ и 2…4 wt.% Gr определяли в закаливаемых стальных пресс-формах при
давлении 100...500 МPа. Для понимания особенностей компактирования гибридных композитов на основе Al, упрочненных частицами TiO₂ та Gr при различных давлениях, проводили экспериментальные исследования с использованием нескольких подходов. Представлен микроструктурный анализ композита Al + 5% TiO₂ + 6% Gr.
|
| first_indexed | 2025-11-25T04:36:29Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-136252 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 0430-6252 |
| language | English |
| last_indexed | 2025-11-25T04:36:29Z |
| publishDate | 2015 |
| publisher | Фізико-механічний інститут ім. Г.В. Карпенка НАН України |
| record_format | dspace |
| spelling | Ravichandran, M. Vidhya, VS. Anandakrishanan, V. 2018-06-16T08:29:14Z 2018-06-16T08:29:14Z 2015 Study of characteristics of Al + 5 wt.% TiO₂ + 6 wt.% Gr hybrid p/m composite powders prepared by ball milling process / M. Ravichandran, VS. Vidhya, V. Anandakrishanan // Фізико-хімічна механіка матеріалів. — 2015. — Т. 51, № 4. — С. 136-143. — Бібліогр.: 16 назв. — англ. 0430-6252 https://nasplib.isofts.kiev.ua/handle/123456789/136252 This paper is an attempt to understand the characteristics of Al + TiO₂ + Gr hybrid ball
 milled composite powders, which is anticipated to have large application in the near future.
 Aluminium with titanium dioxide (TiO₂) and graphite (Gr) powders was ball milled in
 order to yield the composition like: Al + 0% TiO₂, Al + 5% TiO₂, Al + 5% TiO₂ + 2% Gr,
 Al + 5% TiO₂ + 4% Gr and Al + 5% TiO₂ + 6% Gr. From the X-Ray diffraction analysis
 of the milled powders, the grain size, lattice space, lattice constant, stress, strain, dislocation
 density and unit cell volume were calculated. Compressibility was performed in a
 hardened steel die at pressures between 100 to 500 MPa to determine Al with 5 wt.% TiO₂
 and 2 & 4 wt.% of Gr powder mixtures. For understanding of compaction behavior of aluminum
 based hybrid composites reinforced with TiO₂ and Gr particles under various
 applied pressure conditions, experimental research has been made using several powder
 compaction equations. Microstructure analysis for Al + 5% TiO₂ + 6% Gr composite has
 been reported. Вивчали характеристики композитних порошків Al + TiO₂ + Gr. Композити складу Al + 0% TiO₂, Al + 5% TiO₂, Al + 5% TiO₂ + 2% Gr, Al + 5% TiO₂ + 4% Gr та
 Al + 5% TiO₂ + 6% Gr отримували шляхом кульового помелу відповідних компонентів.
 Для визначення розмірів зерен, параметрів кристалічної решітки, напруження, деформації, густини дислокацій та об’єму елементарної комірки використовували рентгенівський
 дифракційний аналіз. Здатність до компактування Al з сумішшю порошків 5 wt.% TiO₂ та
 2 і 4 wt.% Gr визначали в гартованих сталевих прес-формах за тиску 100… 500 МPа. Для
 розуміння особливостей компактування гібридних композитів на основі Al, зміцнених
 частинками TiO₂ та Gr за різних тисків, виконували експериментальні дослідження з
 використанням декількох підходів. Наведено мікроструктурний аналіз композита
 Al + 5% TiO₂ + 6% Gr. Изучали характеристики композитных порошков Al + TiO₂ + Gr. Композиты состава Al + 0% TiO₂, Al + 5% TiO₂, Al + 5% TiO₂ + 2% Gr, Al + 5% TiO₂ + + 4% Gr и
 Al + 5% TiO₂ + 6% Gr получали путем шарового помола соответствующих компонентов.
 Для определения размеров зерен, параметров кристаллической решетки, напряжения,
 деформации, плотности дислокаций и объема элементарной ячейки использовали рентгеновский дифракционный анализ. Способность к компактированию Al со смесью порошков 5 wt.% TiO₂ и 2…4 wt.% Gr определяли в закаливаемых стальных пресс-формах при
 давлении 100...500 МPа. Для понимания особенностей компактирования гибридных композитов на основе Al, упрочненных частицами TiO₂ та Gr при различных давлениях, проводили экспериментальные исследования с использованием нескольких подходов. Представлен микроструктурный анализ композита Al + 5% TiO₂ + 6% Gr. en Фізико-механічний інститут ім. Г.В. Карпенка НАН України Фізико-хімічна механіка матеріалів Study of characteristics of Al + 5 wt.% TiO₂ + 6 wt.% Gr hybrid p/m composite powders prepared by ball milling process Дослідження характеристик композитних порошків на основі Al + 5 wt.% TiO₂ + 6 wt.% Gr, отриманих шляхом помелу Исследование характеристик композитных порошков на основе Al + 5 wt.% TiO₂ + 6 wt.% Gr, полученных путем помола Article published earlier |
| spellingShingle | Study of characteristics of Al + 5 wt.% TiO₂ + 6 wt.% Gr hybrid p/m composite powders prepared by ball milling process Ravichandran, M. Vidhya, VS. Anandakrishanan, V. |
| title | Study of characteristics of Al + 5 wt.% TiO₂ + 6 wt.% Gr hybrid p/m composite powders prepared by ball milling process |
| title_alt | Дослідження характеристик композитних порошків на основі Al + 5 wt.% TiO₂ + 6 wt.% Gr, отриманих шляхом помелу Исследование характеристик композитных порошков на основе Al + 5 wt.% TiO₂ + 6 wt.% Gr, полученных путем помола |
| title_full | Study of characteristics of Al + 5 wt.% TiO₂ + 6 wt.% Gr hybrid p/m composite powders prepared by ball milling process |
| title_fullStr | Study of characteristics of Al + 5 wt.% TiO₂ + 6 wt.% Gr hybrid p/m composite powders prepared by ball milling process |
| title_full_unstemmed | Study of characteristics of Al + 5 wt.% TiO₂ + 6 wt.% Gr hybrid p/m composite powders prepared by ball milling process |
| title_short | Study of characteristics of Al + 5 wt.% TiO₂ + 6 wt.% Gr hybrid p/m composite powders prepared by ball milling process |
| title_sort | study of characteristics of al + 5 wt.% tio₂ + 6 wt.% gr hybrid p/m composite powders prepared by ball milling process |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/136252 |
| work_keys_str_mv | AT ravichandranm studyofcharacteristicsofal5wttio26wtgrhybridpmcompositepowderspreparedbyballmillingprocess AT vidhyavs studyofcharacteristicsofal5wttio26wtgrhybridpmcompositepowderspreparedbyballmillingprocess AT anandakrishananv studyofcharacteristicsofal5wttio26wtgrhybridpmcompositepowderspreparedbyballmillingprocess AT ravichandranm doslídžennâharakteristikkompozitnihporoškívnaosnovíal5wttio26wtgrotrimanihšlâhompomelu AT vidhyavs doslídžennâharakteristikkompozitnihporoškívnaosnovíal5wttio26wtgrotrimanihšlâhompomelu AT anandakrishananv doslídžennâharakteristikkompozitnihporoškívnaosnovíal5wttio26wtgrotrimanihšlâhompomelu AT ravichandranm issledovanieharakteristikkompozitnyhporoškovnaosnoveal5wttio26wtgrpolučennyhputempomola AT vidhyavs issledovanieharakteristikkompozitnyhporoškovnaosnoveal5wttio26wtgrpolučennyhputempomola AT anandakrishananv issledovanieharakteristikkompozitnyhporoškovnaosnoveal5wttio26wtgrpolučennyhputempomola |