Effect of sintering conditions on physical properties of carbonated hydroxyapatite ceramics
The carbonated hydroxyapatite powder was obtained by reaction of calcium carbonate with ortho-phosphoric acid. The compacted powder samples were sintered in the 800- 1000°C range in dry carbon dioxide atmosphere under atmospheric pressure. It is revealed that ceramics synthesized in such conditions...
Збережено в:
| Опубліковано в: : | Functional Materials |
|---|---|
| Дата: | 2008 |
| Автори: | , |
| Формат: | Стаття |
| Мова: | Англійська |
| Опубліковано: |
НТК «Інститут монокристалів» НАН України
2008
|
| Теми: | |
| Онлайн доступ: | https://nasplib.isofts.kiev.ua/handle/123456789/136550 |
| Теги: |
Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Цитувати: | Effect of sintering conditions on physical properties of carbonated hydroxyapatite ceramics // M.V. Tkachenko, Z.Z. Zyman // Functional Materials. — 2008. — Т. 15, № 4. — С. 574-579. — Бібліогр.: 12 назв. — англ. |
Репозитарії
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862711604789903360 |
|---|---|
| author | Tkachenko, M.V. Zyman, Z.Z. |
| author_facet | Tkachenko, M.V. Zyman, Z.Z. |
| citation_txt | Effect of sintering conditions on physical properties of carbonated hydroxyapatite ceramics // M.V. Tkachenko, Z.Z. Zyman // Functional Materials. — 2008. — Т. 15, № 4. — С. 574-579. — Бібліогр.: 12 назв. — англ. |
| collection | DSpace DC |
| container_title | Functional Materials |
| description | The carbonated hydroxyapatite powder was obtained by reaction of calcium carbonate with ortho-phosphoric acid. The compacted powder samples were sintered in the 800- 1000°C range in dry carbon dioxide atmosphere under atmospheric pressure. It is revealed that ceramics synthesized in such conditions is the AB type carbonated hydroxyapatite. The carbonization kind varies from mainly B type (at relatively low sintering temperatures) to mainly A type (at high ones). The carbonic gas atmosphere did not allow to suppress disintegration of a carbonated apatite at a sintering temperatures above 1100°C, a partial decomposition of the B type apatite occurs with calcium oxide release. As a result, porosity of the ceramics increases and its mechanical properties drop sharply. However, at temperatures below 1100°C, the carbon dioxide favors the activated shrinkage of compacts due to accelerated diffusion migration of the powder particles. In particular, the maximum density of ceramics (~94% from the theoretical value) is reached at 1000°C.
Порошок карбонізованого гідроксилапатиту отримано реакцією між карбонатом кальцію та ортофосфорною кислотою. Виготовлені з нього пресовані зразки спікалися в інтервалі температур 800-1000°С у атмосфері сухого діоксиду вуглецю (при нормальному тиску). Кераміка, отримана у такий спосіб, є карбонізованим гідроксилапатитом АЕ-типу. Вид карбонізації змінюється від переважно В-типу при відносно низьких температурах до переважно А-типу - при високих температурах спікання. Вище 1100°С відбувається частковий розпад апатиту В-типу та виділення окису кальцію. При цьому пористість кераміки зростає та різко падають її механічні властивості. При температурах нижче 1100°С атмосфера діоксиду вуглецю сприяє активованій усадці пресовок завдяки прискоренню дифузійної міграції частинок порошку. Зокрема, це приводить до досягнення високої щільності кераміки (~94% від теоретичного значення ГА) при температурі 1000°С.
Порошок карбонизированного гидроксилапатита получен путем проведения реакции между карбонатом кальция и ортофосфорной кислотой. Изготовленные из него прессовки спекались в интервале температур 800-1000°С в атмосфере сухого углекислого газа (при нормальном давлении). Керамика, полученная таким способом, является карбонизированным гидроксилапатитом АВ-типа. Вид карбонизации изменяется от преимущественно В-типа при относительно низких температурах до преимущественно А-типа - при высоких температурах спекания. Выше 1100°С происходит частичный распад апатита В-типа и выделение окиси кальция. При этом пористость керамики увеличивается и резко падают ее механические свойства. При температурах нижe 1100°С, атмосфера углекислого газа способствует активированной усадке прессовок благодаря ускорению диффузионной миграции частиц порошка. В частности, это приводит к достижению высокой плотности керамики (~94% от теоретического значения ГА) при температуре 1000°С.
|
| first_indexed | 2025-12-07T17:32:01Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-136550 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 1027-5495 |
| language | English |
| last_indexed | 2025-12-07T17:32:01Z |
| publishDate | 2008 |
| publisher | НТК «Інститут монокристалів» НАН України |
| record_format | dspace |
| spelling | Tkachenko, M.V. Zyman, Z.Z. 2018-06-16T13:38:47Z 2018-06-16T13:38:47Z 2008 Effect of sintering conditions on physical properties of carbonated hydroxyapatite ceramics // M.V. Tkachenko, Z.Z. Zyman // Functional Materials. — 2008. — Т. 15, № 4. — С. 574-579. — Бібліогр.: 12 назв. — англ. 1027-5495 https://nasplib.isofts.kiev.ua/handle/123456789/136550 The carbonated hydroxyapatite powder was obtained by reaction of calcium carbonate with ortho-phosphoric acid. The compacted powder samples were sintered in the 800- 1000°C range in dry carbon dioxide atmosphere under atmospheric pressure. It is revealed that ceramics synthesized in such conditions is the AB type carbonated hydroxyapatite. The carbonization kind varies from mainly B type (at relatively low sintering temperatures) to mainly A type (at high ones). The carbonic gas atmosphere did not allow to suppress disintegration of a carbonated apatite at a sintering temperatures above 1100°C, a partial decomposition of the B type apatite occurs with calcium oxide release. As a result, porosity of the ceramics increases and its mechanical properties drop sharply. However, at temperatures below 1100°C, the carbon dioxide favors the activated shrinkage of compacts due to accelerated diffusion migration of the powder particles. In particular, the maximum density of ceramics (~94% from the theoretical value) is reached at 1000°C. Порошок карбонізованого гідроксилапатиту отримано реакцією між карбонатом кальцію та ортофосфорною кислотою. Виготовлені з нього пресовані зразки спікалися в інтервалі температур 800-1000°С у атмосфері сухого діоксиду вуглецю (при нормальному тиску). Кераміка, отримана у такий спосіб, є карбонізованим гідроксилапатитом АЕ-типу. Вид карбонізації змінюється від переважно В-типу при відносно низьких температурах до переважно А-типу - при високих температурах спікання. Вище 1100°С відбувається частковий розпад апатиту В-типу та виділення окису кальцію. При цьому пористість кераміки зростає та різко падають її механічні властивості. При температурах нижче 1100°С атмосфера діоксиду вуглецю сприяє активованій усадці пресовок завдяки прискоренню дифузійної міграції частинок порошку. Зокрема, це приводить до досягнення високої щільності кераміки (~94% від теоретичного значення ГА) при температурі 1000°С. Порошок карбонизированного гидроксилапатита получен путем проведения реакции между карбонатом кальция и ортофосфорной кислотой. Изготовленные из него прессовки спекались в интервале температур 800-1000°С в атмосфере сухого углекислого газа (при нормальном давлении). Керамика, полученная таким способом, является карбонизированным гидроксилапатитом АВ-типа. Вид карбонизации изменяется от преимущественно В-типа при относительно низких температурах до преимущественно А-типа - при высоких температурах спекания. Выше 1100°С происходит частичный распад апатита В-типа и выделение окиси кальция. При этом пористость керамики увеличивается и резко падают ее механические свойства. При температурах нижe 1100°С, атмосфера углекислого газа способствует активированной усадке прессовок благодаря ускорению диффузионной миграции частиц порошка. В частности, это приводит к достижению высокой плотности керамики (~94% от теоретического значения ГА) при температуре 1000°С. en НТК «Інститут монокристалів» НАН України Functional Materials Technology Effect of sintering conditions on physical properties of carbonated hydroxyapatite ceramics Вплив умов спікання на фізичні властивості карбонізованої гідроксилапатитної кераміки Article published earlier |
| spellingShingle | Effect of sintering conditions on physical properties of carbonated hydroxyapatite ceramics Tkachenko, M.V. Zyman, Z.Z. Technology |
| title | Effect of sintering conditions on physical properties of carbonated hydroxyapatite ceramics |
| title_alt | Вплив умов спікання на фізичні властивості карбонізованої гідроксилапатитної кераміки |
| title_full | Effect of sintering conditions on physical properties of carbonated hydroxyapatite ceramics |
| title_fullStr | Effect of sintering conditions on physical properties of carbonated hydroxyapatite ceramics |
| title_full_unstemmed | Effect of sintering conditions on physical properties of carbonated hydroxyapatite ceramics |
| title_short | Effect of sintering conditions on physical properties of carbonated hydroxyapatite ceramics |
| title_sort | effect of sintering conditions on physical properties of carbonated hydroxyapatite ceramics |
| topic | Technology |
| topic_facet | Technology |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/136550 |
| work_keys_str_mv | AT tkachenkomv effectofsinteringconditionsonphysicalpropertiesofcarbonatedhydroxyapatiteceramics AT zymanzz effectofsinteringconditionsonphysicalpropertiesofcarbonatedhydroxyapatiteceramics AT tkachenkomv vplivumovspíkannânafízičnívlastivostíkarbonízovanoígídroksilapatitnoíkeramíki AT zymanzz vplivumovspíkannânafízičnívlastivostíkarbonízovanoígídroksilapatitnoíkeramíki |