Environmentally-assisted fatigue crack growth in prestressing steel wires
This paper presents the evolution of the surface crack front in prestressing reinforced concrete steel wires subjected to fatigue in air and to corrosion-fatigue in Ca(OH)₂+NaCl. To this end, a numerical modelling was made on the basis of a discretization of the crack front (with elliptical shape),...
Gespeichert in:
| Veröffentlicht in: | Фізико-хімічна механіка матеріалів |
|---|---|
| Datum: | 2011 |
| Hauptverfasser: | , , , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Фізико-механічний інститут ім. Г.В. Карпенка НАН України
2011
|
| Online Zugang: | https://nasplib.isofts.kiev.ua/handle/123456789/138393 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Environmentally-assisted fatigue crack growth in prestressing steel wires / J. Toribio, J.C. Matos, В. González, J. Escuadra // Фізико-хімічна механіка матеріалів. — 2011. — Т. 47, № 6. — С. 45-51. — Бібліогр.: 19 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| id |
nasplib_isofts_kiev_ua-123456789-138393 |
|---|---|
| record_format |
dspace |
| spelling |
Toribio, J. Matos, J.C. González, В. Escuadra, J. 2018-06-18T20:17:30Z 2018-06-18T20:17:30Z 2011 Environmentally-assisted fatigue crack growth in prestressing steel wires / J. Toribio, J.C. Matos, В. González, J. Escuadra // Фізико-хімічна механіка матеріалів. — 2011. — Т. 47, № 6. — С. 45-51. — Бібліогр.: 19 назв. — англ. 0430-6252 https://nasplib.isofts.kiev.ua/handle/123456789/138393 This paper presents the evolution of the surface crack front in prestressing reinforced concrete steel wires subjected to fatigue in air and to corrosion-fatigue in Ca(OH)₂+NaCl. To this end, a numerical modelling was made on the basis of a discretization of the crack front (with elliptical shape), considering that the crack advance at each point is perpendicular to such a front according to a Paris-Erdogan law, and using a threeparameter solution for stress intensity factor (SIF). Each analyzed case (a particular initial crack geometry) was characterized by the evolution of the semielliptical crack aspect ratio (relation between the semiaxes of the ellipse) with the relative crack depth and by the variation of the maximum dimensionless SIF at the crack front. Описано еволюцію фронту поверхневої тріщини в сталевих дротах для переднапруженого стану залізобетону, підданих втомному навантаженню на повітрі і корозійній втомі в середовищі Ca(OH)₂ + NaCl. На основі дискретизації чисельно змодельовано фронт тріщини, який приймали еліптичним, і вважали, що тріщина в кожній точці просувається перпендикулярно до її фронту згідно з законом Періса–Ердогана. Використовували трипараметричний розв’язок для коефіцієнта інтенсивності напружень (КІН). Кожний з аналізованих випадків, якому відповідала певна початкова геометрія тріщини, характеризувався еволюцією форми напівеліптичної тріщини (відношення півосей еліпса) і відносної її глибини, а також варіацією значень максимального безрозмірного КІН вздовж фронту тріщини. Описана эволюция фронта поверхностной трещины в стальных проволоках для преднапряженного состояния железобетона, подвергаемых усталости на воздухе и коррозионной усталости в среде Ca(OH)₂+ NaCl. На основе дискретизации численно смоделирован фронт трещины, который принимали полуэллиптическим, и считали, что трещина в каждой точке движется перпендикулярно к ее фронту согласно закону Пэриса– Эрдогана. Использовали трехпараметрическое решение для коэффициента интенсивности напряжений (КИН). Каждый из анализированных случаев, которому соответствовала определенная начальная геометрия трещины, характеризовался эволюцией формы полуэллиптической трещины (отношение полуосей эллипса) и относительной ее глубины, а также изменением значений максимального безразмерного КИН вдоль фронта трещины. The authors wish to acknowledge the financial support provided by the following Spanish Institutions: Ministry for Science and Technology (MCYT; Grant MAT2002-01831), Ministry for Education and Science (MEC; Grant BIA2005-08965), Ministry for Science and Innovation (MICINN; Grant BIA2008-06810), Junta de Castilla y León (JCyL; Grants SA067A05, SA111A07 and SA039A08). en Фізико-механічний інститут ім. Г.В. Карпенка НАН України Фізико-хімічна механіка матеріалів Environmentally-assisted fatigue crack growth in prestressing steel wires Рост усталостной трещины в предварительно напряженных стальных проволоках под влиянием сред Ріст втомної тріщини у попередньо напружених сталевих дротах під впливом середовищ Article published earlier |
| institution |
Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| collection |
DSpace DC |
| title |
Environmentally-assisted fatigue crack growth in prestressing steel wires |
| spellingShingle |
Environmentally-assisted fatigue crack growth in prestressing steel wires Toribio, J. Matos, J.C. González, В. Escuadra, J. |
| title_short |
Environmentally-assisted fatigue crack growth in prestressing steel wires |
| title_full |
Environmentally-assisted fatigue crack growth in prestressing steel wires |
| title_fullStr |
Environmentally-assisted fatigue crack growth in prestressing steel wires |
| title_full_unstemmed |
Environmentally-assisted fatigue crack growth in prestressing steel wires |
| title_sort |
environmentally-assisted fatigue crack growth in prestressing steel wires |
| author |
Toribio, J. Matos, J.C. González, В. Escuadra, J. |
| author_facet |
Toribio, J. Matos, J.C. González, В. Escuadra, J. |
| publishDate |
2011 |
| language |
English |
| container_title |
Фізико-хімічна механіка матеріалів |
| publisher |
Фізико-механічний інститут ім. Г.В. Карпенка НАН України |
| format |
Article |
| title_alt |
Рост усталостной трещины в предварительно напряженных стальных проволоках под влиянием сред Ріст втомної тріщини у попередньо напружених сталевих дротах під впливом середовищ |
| description |
This paper presents the evolution of the surface crack front in prestressing reinforced concrete steel wires subjected to fatigue in air and to corrosion-fatigue in Ca(OH)₂+NaCl. To this end, a numerical modelling was made on the basis of a discretization of the crack front (with elliptical shape), considering that the crack advance at each point is perpendicular to such a front according to a Paris-Erdogan law, and using a threeparameter solution for stress intensity factor (SIF). Each analyzed case (a particular initial crack geometry) was characterized by the evolution of the semielliptical crack aspect ratio (relation between the semiaxes of the ellipse) with the relative crack depth and by the variation of the maximum dimensionless SIF at the crack front.
Описано еволюцію фронту поверхневої тріщини в сталевих дротах для переднапруженого стану залізобетону, підданих втомному навантаженню на повітрі і корозійній втомі в середовищі Ca(OH)₂ + NaCl. На основі дискретизації чисельно змодельовано фронт тріщини, який приймали еліптичним, і вважали, що тріщина в кожній точці просувається перпендикулярно до її фронту згідно з законом Періса–Ердогана. Використовували трипараметричний розв’язок для коефіцієнта інтенсивності напружень (КІН). Кожний з аналізованих випадків, якому відповідала певна початкова геометрія тріщини, характеризувався еволюцією форми напівеліптичної тріщини (відношення півосей еліпса) і відносної її глибини, а також варіацією значень максимального безрозмірного КІН вздовж фронту тріщини.
Описана эволюция фронта поверхностной трещины в стальных проволоках для преднапряженного состояния железобетона, подвергаемых усталости на воздухе и коррозионной усталости в среде Ca(OH)₂+ NaCl. На основе дискретизации численно смоделирован фронт трещины, который принимали полуэллиптическим, и считали, что трещина в каждой точке движется перпендикулярно к ее фронту согласно закону Пэриса– Эрдогана. Использовали трехпараметрическое решение для коэффициента интенсивности напряжений (КИН). Каждый из анализированных случаев, которому соответствовала определенная начальная геометрия трещины, характеризовался эволюцией формы полуэллиптической трещины (отношение полуосей эллипса) и относительной ее глубины, а также изменением значений максимального безразмерного КИН вдоль фронта трещины.
|
| issn |
0430-6252 |
| url |
https://nasplib.isofts.kiev.ua/handle/123456789/138393 |
| citation_txt |
Environmentally-assisted fatigue crack growth in prestressing steel wires / J. Toribio, J.C. Matos, В. González, J. Escuadra // Фізико-хімічна механіка матеріалів. — 2011. — Т. 47, № 6. — С. 45-51. — Бібліогр.: 19 назв. — англ. |
| work_keys_str_mv |
AT toribioj environmentallyassistedfatiguecrackgrowthinprestressingsteelwires AT matosjc environmentallyassistedfatiguecrackgrowthinprestressingsteelwires AT gonzalezv environmentallyassistedfatiguecrackgrowthinprestressingsteelwires AT escuadraj environmentallyassistedfatiguecrackgrowthinprestressingsteelwires AT toribioj rostustalostnoitreŝinyvpredvaritelʹnonaprâžennyhstalʹnyhprovolokahpodvliâniemsred AT matosjc rostustalostnoitreŝinyvpredvaritelʹnonaprâžennyhstalʹnyhprovolokahpodvliâniemsred AT gonzalezv rostustalostnoitreŝinyvpredvaritelʹnonaprâžennyhstalʹnyhprovolokahpodvliâniemsred AT escuadraj rostustalostnoitreŝinyvpredvaritelʹnonaprâžennyhstalʹnyhprovolokahpodvliâniemsred AT toribioj rístvtomnoítríŝiniupoperednʹonapruženihstalevihdrotahpídvplivomseredoviŝ AT matosjc rístvtomnoítríŝiniupoperednʹonapruženihstalevihdrotahpídvplivomseredoviŝ AT gonzalezv rístvtomnoítríŝiniupoperednʹonapruženihstalevihdrotahpídvplivomseredoviŝ AT escuadraj rístvtomnoítríŝiniupoperednʹonapruženihstalevihdrotahpídvplivomseredoviŝ |
| first_indexed |
2025-12-07T18:04:28Z |
| last_indexed |
2025-12-07T18:04:28Z |
| _version_ |
1850873656019779584 |