Dilatometric study of ordered structures in Fe-AI alloys

• Veröffentlicht in: Functional Materials
• Datum: 2004
• Hauptverfasser: Boufenghour, M., Hayoune, A., Rokhmanov, N.Ya., Bouchear, M., Hamana, D.
• Format: Artikel
• Sprache: English
• Veröffentlicht: НТК «Інститут монокристалів» НАН України 2004
• Online Zugang: https://nasplib.isofts.kiev.ua/handle/123456789/138836
• Назва журналу: Digital Library of Periodicals of National Academy of Sciences of Ukraine
• Zitieren: Dilatometric study of ordered structures in Fe-AI alloys / M. Boufenghour, A. Hayoune, N.Ya. Rokhmanov, M. Bouchear, D. Hamana // Functional Materials. — 2004. — Т. 11, № 2. — С. 397-401. — Бібліогр.: 12 назв. — англ.

The order-disorder transformations in iron based alloys containing 21.5 and 25 at. % Al have been studied. Consideration of results obtained using dilatometry allowed us to assert that the ordering reaction in Fe-Al alloys after quenching from disordered state is a rather rapid process and ageing at moderate temperatures results in increased extent of the DO₃ type ordering. Изучено превращение порядок-беспорядок в сплавах на основе жєлєзи, содержащих 21.5 и 25 aT. % Al. Анализ результатов, полученных путем дилатометрии, позволяет утверждать, что реакция упорядочения в Fe-Al сплавах после закалки из области неупорядоченного состояния является довольно быстрым процессом и старение при умеренных температурах приводит к повышению степени дальнего порядка типа DO₃. Досліджєно перетворення порядок-невпорядокованість у сплавах на основі залiза, що містили 21.5 та 25 at. % Al. Аналіз результатів, одержаних методом дилатометрії, дозволяє стверджувати, що реакція впорядкування в Fe-Al сплавах після загартування з області невпорядкованого стану є досить швидким процесом, а старіння при помірних температурах спричиняє підвищення ступеня дальнього порядку типу DO₃.