Effect of chromate conversion coatings on the adhesion and corrosion resistance of painted 5083 aluminum alloy
The 5083 aluminum alloy surfaces were coated with chromate conversion coatings. Then epoxy paints were applied on the chromate and non-chromate treatment surfaces. The adhesion, hardness and corrosion resistance of the coated samples were evaluated using adhesion tape test, pencil hardness test, sal...
Збережено в:
| Опубліковано в: : | Фізико-хімічна механіка матеріалів |
|---|---|
| Дата: | 2012 |
| Автори: | , |
| Формат: | Стаття |
| Мова: | English |
| Опубліковано: |
Фізико-механічний інститут ім. Г.В. Карпенка НАН України
2012
|
| Онлайн доступ: | https://nasplib.isofts.kiev.ua/handle/123456789/139353 |
| Теги: |
Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Цитувати: | Effect of chromate conversion coatings on the adhesion and corrosion resistance of painted 5083 aluminum alloy / Eshaghi Ameneh, Eshaghi Akbar // Фізико-хімічна механіка матеріалів. — 2012. — Т. 48, № 2. — С. 47-50. — Бібліогр.: 10 назв. — англ. |
Репозитарії
Digital Library of Periodicals of National Academy of Sciences of Ukraine| id |
nasplib_isofts_kiev_ua-123456789-139353 |
|---|---|
| record_format |
dspace |
| spelling |
Eshaghi Ameneh Eshaghi Akbar 2018-06-20T05:51:32Z 2018-06-20T05:51:32Z 2012 Effect of chromate conversion coatings on the adhesion and corrosion resistance of painted 5083 aluminum alloy / Eshaghi Ameneh, Eshaghi Akbar // Фізико-хімічна механіка матеріалів. — 2012. — Т. 48, № 2. — С. 47-50. — Бібліогр.: 10 назв. — англ. 0430-6252 https://nasplib.isofts.kiev.ua/handle/123456789/139353 The 5083 aluminum alloy surfaces were coated with chromate conversion coatings. Then epoxy paints were applied on the chromate and non-chromate treatment surfaces. The adhesion, hardness and corrosion resistance of the coated samples were evaluated using adhesion tape test, pencil hardness test, salt spray and electrochemical technique. The results indicated that the adhesion of the coating systems including chromate treatments was better than that of non-chromate conversion coatings, whereas the hardness of the coating systems was equal. Salt spray results showed that corrosion propagation from the scratched area in the painted samples with chromate treatment was lower than that of nonchromate coated surfaces. In addition, electrochemical corrosion measurements indicated that the coating system including chromate treatment presented lower corrosion current density, bigger polarization resistance and less negative corrosion potential than those of the non-chromate conversion coated surfaces. Досліджено вплив хроматної конверсійної обробки алюмінієвого сплаву 5083 на адгезію епоксидних лакофарбових покривів та їх захисні властивості. Встановлено, що адгезія покривів по поверхні сплаву з хроматним конверсійним шаром більша, ніж за безхроматної обробки, а їх твердість в обох випадках однакова. Корозія металу під плівкою біля дефекту лакофарбового покриву за умов попереднього хроматування протікає не так інтенсивно, як після безхроматної обробки. Зразки сплаву зі системою покриву, яка охоплювала хроматну обробку, мали нижчі густини струму корозії, більший поляризаційний опір та менш негативний потенціал корозії, ніж безхроматно оброблені. Исследовано влияние хроматной конверсионной обработки алюминиевого сплава 5083 на адгезию эпоксидных лакокрасочных покрытий и их защитные свойства. Установлено, что адгезия покрытий по поверхности сплава с хроматным конверсионным слоем больше, нежели после безхроматной обработки, а их твердость в обеих случаях одинакова. Коррозия металла под пленкой возле дефекта лакокрасочного покрытия после предварительного хромирования протекает не так интенсивно, как после безхроматной обработки. Образцы сплава с системой покрытия, которая охватывала хроматную обработку, имели меньшую плотность тока коррозии, большее поляризационное сопротивление и менее негативный потенциал коррозии, нежели безхроматно обработанные. en Фізико-механічний інститут ім. Г.В. Карпенка НАН України Фізико-хімічна механіка матеріалів Effect of chromate conversion coatings on the adhesion and corrosion resistance of painted 5083 aluminum alloy Влияние хроматных конверсионных покрытий на адгезию и коррозионную стойкость лакокрасочного покрытия на алюминиевом сплаве 508 Вплив хроматних конверсійних покривів на адгезію та корозійну тривкість лакофарбового покриву на алюмінієвому сплаві 5083 Article published earlier |
| institution |
Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| collection |
DSpace DC |
| title |
Effect of chromate conversion coatings on the adhesion and corrosion resistance of painted 5083 aluminum alloy |
| spellingShingle |
Effect of chromate conversion coatings on the adhesion and corrosion resistance of painted 5083 aluminum alloy Eshaghi Ameneh Eshaghi Akbar |
| title_short |
Effect of chromate conversion coatings on the adhesion and corrosion resistance of painted 5083 aluminum alloy |
| title_full |
Effect of chromate conversion coatings on the adhesion and corrosion resistance of painted 5083 aluminum alloy |
| title_fullStr |
Effect of chromate conversion coatings on the adhesion and corrosion resistance of painted 5083 aluminum alloy |
| title_full_unstemmed |
Effect of chromate conversion coatings on the adhesion and corrosion resistance of painted 5083 aluminum alloy |
| title_sort |
effect of chromate conversion coatings on the adhesion and corrosion resistance of painted 5083 aluminum alloy |
| author |
Eshaghi Ameneh Eshaghi Akbar |
| author_facet |
Eshaghi Ameneh Eshaghi Akbar |
| publishDate |
2012 |
| language |
English |
| container_title |
Фізико-хімічна механіка матеріалів |
| publisher |
Фізико-механічний інститут ім. Г.В. Карпенка НАН України |
| format |
Article |
| title_alt |
Влияние хроматных конверсионных покрытий на адгезию и коррозионную стойкость лакокрасочного покрытия на алюминиевом сплаве 508 Вплив хроматних конверсійних покривів на адгезію та корозійну тривкість лакофарбового покриву на алюмінієвому сплаві 5083 |
| description |
The 5083 aluminum alloy surfaces were coated with chromate conversion coatings. Then epoxy paints were applied on the chromate and non-chromate treatment surfaces. The adhesion, hardness and corrosion resistance of the coated samples were evaluated using adhesion tape test, pencil hardness test, salt spray and electrochemical technique. The results indicated that the adhesion of the coating systems including chromate treatments was better than that of non-chromate conversion coatings, whereas the hardness of the coating systems was equal. Salt spray results showed that corrosion propagation from the scratched area in the painted samples with chromate treatment was lower than that of nonchromate coated surfaces. In addition, electrochemical corrosion measurements indicated that the coating system including chromate treatment presented lower corrosion current density, bigger polarization resistance and less negative corrosion potential than those of the non-chromate conversion coated surfaces.
Досліджено вплив хроматної конверсійної обробки алюмінієвого сплаву 5083 на адгезію епоксидних лакофарбових покривів та їх захисні властивості. Встановлено, що адгезія покривів по поверхні сплаву з хроматним конверсійним шаром більша, ніж за безхроматної обробки, а їх твердість в обох випадках однакова. Корозія металу під плівкою біля дефекту лакофарбового покриву за умов попереднього хроматування протікає не так інтенсивно, як після безхроматної обробки. Зразки сплаву зі системою покриву, яка охоплювала хроматну обробку, мали нижчі густини струму корозії, більший поляризаційний опір та менш негативний потенціал корозії, ніж безхроматно оброблені.
Исследовано влияние хроматной конверсионной обработки алюминиевого сплава 5083 на адгезию эпоксидных лакокрасочных покрытий и их защитные свойства. Установлено, что адгезия покрытий по поверхности сплава с хроматным конверсионным слоем больше, нежели после безхроматной обработки, а их твердость в обеих случаях одинакова. Коррозия металла под пленкой возле дефекта лакокрасочного покрытия после предварительного хромирования протекает не так интенсивно, как после безхроматной обработки. Образцы сплава с системой покрытия, которая охватывала хроматную обработку, имели меньшую плотность тока коррозии, большее поляризационное сопротивление и менее негативный потенциал коррозии, нежели безхроматно обработанные.
|
| issn |
0430-6252 |
| url |
https://nasplib.isofts.kiev.ua/handle/123456789/139353 |
| citation_txt |
Effect of chromate conversion coatings on the adhesion and corrosion resistance of painted 5083 aluminum alloy / Eshaghi Ameneh, Eshaghi Akbar // Фізико-хімічна механіка матеріалів. — 2012. — Т. 48, № 2. — С. 47-50. — Бібліогр.: 10 назв. — англ. |
| work_keys_str_mv |
AT eshaghiameneh effectofchromateconversioncoatingsontheadhesionandcorrosionresistanceofpainted5083aluminumalloy AT eshaghiakbar effectofchromateconversioncoatingsontheadhesionandcorrosionresistanceofpainted5083aluminumalloy AT eshaghiameneh vliâniehromatnyhkonversionnyhpokrytiinaadgeziûikorrozionnuûstoikostʹlakokrasočnogopokrytiânaalûminievomsplave508 AT eshaghiakbar vliâniehromatnyhkonversionnyhpokrytiinaadgeziûikorrozionnuûstoikostʹlakokrasočnogopokrytiânaalûminievomsplave508 AT eshaghiameneh vplivhromatnihkonversíinihpokrivívnaadgezíûtakorozíinutrivkístʹlakofarbovogopokrivunaalûmíníêvomusplaví5083 AT eshaghiakbar vplivhromatnihkonversíinihpokrivívnaadgezíûtakorozíinutrivkístʹlakofarbovogopokrivunaalûmíníêvomusplaví5083 |
| first_indexed |
2025-12-07T17:06:09Z |
| last_indexed |
2025-12-07T17:06:09Z |
| _version_ |
1850869987394191360 |