Capacitor and resonator ceramics with low sintering temperature

• Published in: Functional Materials
• Date: 2004
• Main Authors: Vovk, E.A., Deineka, T.G., Ishchuk, V.M., Mateichenko, P.V.
• Format: Article
• Language: English
• Published: НТК «Інститут монокристалів» НАН України 2004
• Online Access: https://nasplib.isofts.kiev.ua/handle/123456789/139480
• Journal Title: Digital Library of Periodicals of National Academy of Sciences of Ukraine
• Cite this: Capacitor and resonator ceramics with low sintering temperature / E.A. Vovk, T.G. Deineka, V.M. Ishchuk, P.V. Mateichenko // Functional Materials. — 2004. — Т. 11, № 3. — С. 595-597. — Бібліогр.: 4 назв. — англ.

A complex-composition ceramic condenser material based on barium titanate and a ceramic resonator material based on barium-neodymium titanate are obtained and investigated. Developed are glass technological additions which introduction into the raw material lowers the ceramics sintering temperature by 200-250°C, increases the density and diminishes the porosity of the ceramics samples, their electrophysical parameters remaining unchanged. Получен и исследован керамический конденсаторный материал сложного состава на основе титаната бария и керамический резонаторный материал на основе титаната бария-неодима. Разработаны стекловидные технологические добавки, введение которых в шихту снижает температуру спекания керамики на 200-250°C, увеличивает плотность и уменьшает пористость керамических образцов без ухудшения их электрофизических параметров. Одержано та досліджєно керамiчний матерiал на основі титанату барію та керамічний резонаторний матеріал на основі титанату барію-неодиму. Розроблено скловидні технологічні домішки, додавання яких у шихту знижує температуру спікання кераміки на 200-250°C, збільшує густину та пористість керамічних зразків без погіршення їх електрофізичних параметрів.