X-ray diffraction study of atomic long-range order of Fe-AI alloy

Temperature dependence of nonequilibrium values of Fe-AI alloy long-range order parameter has been studied using X-ray diffraction by comparing the integrated intensity of superstructure reflection and fundamental one at small Bragg angles. An additional atomic occupancy of corresponding sublattice...

Full description

Saved in:

Bibliographic Details
Published in:	Functional Materials
Date:	2005
Main Authors:	Repetsky, S.P., Yaremko, R.O.
Format:	Article
Language:	English
Published:	НТК «Інститут монокристалів» НАН України 2005
Online Access:	https://nasplib.isofts.kiev.ua/handle/123456789/139740
Tags:	Add Tag No Tags, Be the first to tag this record!
Journal Title:	Digital Library of Periodicals of National Academy of Sciences of Ukraine
Cite this:	X-ray diffraction study of atomic long-range order of Fe-AI alloy / S.P. Repetsky, R.O. Yaremko // Functional Materials. — 2005. — Т. 12, № 1. — С. 124-126. — Бібліогр.: 9 назв. — англ.

Institution

Digital Library of Periodicals of National Academy of Sciences of Ukraine

_version_	1860095761441619968
author	Repetsky, S.P. Yaremko, R.O.
author_facet	Repetsky, S.P. Yaremko, R.O.
citation_txt	X-ray diffraction study of atomic long-range order of Fe-AI alloy / S.P. Repetsky, R.O. Yaremko // Functional Materials. — 2005. — Т. 12, № 1. — С. 124-126. — Бібліогр.: 9 назв. — англ.
collection	DSpace DC
container_title	Functional Materials
description	Temperature dependence of nonequilibrium values of Fe-AI alloy long-range order parameter has been studied using X-ray diffraction by comparing the integrated intensity of superstructure reflection and fundamental one at small Bragg angles. An additional atomic occupancy of corresponding sublattice sites has been shown to occur as the annealing temperature increases. A partial disordering of the alloy was provided by mechanical polishing with diamond paste; it was manifested itself as a decreasing of superstructure reflection intensities. Such behavior of the long-range order parameter of Fe-50 at. % Al alloy shows that the second order phase transformations are typical of that alloy. Рентгенографически исследована температурная зависимость неравновесных значений параметра дальнего атомного порядка сплава Fe-50 ат.% AI по отношению интегральных интенсивностей надструктурного к структурному отражений на малых брег-говских углах. Обнаружено, что с повышением температуры отжига происходит дополнительное заполнение атомами узлов "своих подрешеток". Частично разупорядоченное состояние было достигнуто механическим полированием сплава, что наблюдалось по уменьшению интенсивностей надструктурных рефлексов. Такое поведение параметра дальнего порядка свидетельствует о том, что для сплава Fe-50 ат.% AI характерны фазовые превращения второго рода. Рентгенографічно досліджено температурну залежність нерівноважних значень параметра атомного далекого порядку сплаву Fe-50 ат.% АІ через відношення інтегральних інтенсивностей надструктурного до структурного відбиттів на малих бреггі-вських кутах. Виявлено, що із зростанням температур відпалу відбувається додаткове заповнення атомами "своїх вузлів" у гратці сплаву. Часткове розвпорядкування сплаву було досягнуто механічним поліруванням, що спостерігалося через зменшення інтенсивностей надструктурних рефлексів. Така поведінка параметра далекого порядку свідчить про те, що в сплаві Fe-50 ат.% АІ відбуваються фазові переходи другого роду.
first_indexed	2025-12-07T17:26:02Z
format	Article
fulltext	�� !! �� ! �� "#$%�#$&�'()�#+, ++-#�&.($( %#/0#'(%1'$(2 3(.+/&+%� $#'(.$&.#+$45 3$(�#� $6 0('(/#%'( �(-�$#�& (%&/$&�& 0&'2�,( +0-(.( �� %�! �� 0& &%$&�#$� $%#�� '(-�$45 $%#$+.$&+%#6 $(�+%'1,%1'$&�& , +%'1,%1'$&/1 &%'(7#$6 $( /(-45 8'#�� &.+,5 1�-(5� 98$('17#$&: �%& � 0&.4�#$#/ %#/0#'(%1'4 &%7�( 0'&+5&�% �&0&-� $%#-�$&# 3(0&-$#$# (%&/(/* 13-&. ;+.&5 0&�'#�#%&,;� <(+%�$& '�310&'2�&�#$$&# +&+%&2$# 84-& �&+%�$1%& /#5($�#+,/ 0&-'&.($#/ +0-(.(: �%& $(8-��(-&+� 0& 1/#$��#$� $%#$+.$&+%#6 $(�+%'1,%1'$45 '#)-#,+&.� =(,&# 0&.#�#$# 0('(/#%'( �(-�$#�& 0&'2�,( +.�#%#-�+%.1#% & %&/: �%& �-2 +0-(.( �� %�! �� 5('(,%#'$4 )(3&.4# 0'#.'(>#$2 .%&'&�& '&�(� �� ! �� "�� #�� β�� $�� %�� &� � � � �� "� � � �� &'!��(� � �� )�� " � �� #�� "� �� + , �� -&.� /�� $�� 0�� 0 �� -!.� 1� -�.� �� β�� + � ! �� , � �� 1� �� "�� "�� 1� �� "� � �� -23.� �� %�� 4�� &!� 5 �& �!++� 6 !++* 7 1�� 8�� 9�� 1� � �� " �� "�� + , �� + ��, �� &!++�9 �� !2 � 8�� &! � � � ��$�� % � :�� &+×&+×& �� +�+; �� , �� 2;�;& �� , �� :�� <=>5�� λ ? &�'; �� :�� "�� -@3A.� � � �� -@� ;.� � � �� -A.B � � �� = (��)� (��)� �−�� −�� C�� − �� η� 2C� �� + � �� C� � � �� DE� � � D ��$ � ��$�� F �� <��G�� F �� F �� F η� � � � �� F �� "�� 1� �� "�� ++� 2++� ++� �� @+�( � � � �� $�� '++�(� � �� " �� H�� "� �� 8�� + �� , �� #�� #�� "�� >�� "�� 1� �� "�� "�� % � � � �� " �"�� :�� !+ µ� � �� "�� %�� ! �� η ? +�'2�� 1� �� "�� ?�� @� A�� ?�� B� C�� !!� �� 0 �� 0�� $ �� "�� "�� + ��, �� "� � � � � �� :�� + �� , �� "��B +�A! ��++�(�� +�A@ �2++�(�� +�AA �++�(�� +�A; �@+�(�� % � � � �� "�� η ? +�'2 �� "�� #�� $�� + ��, �� B� D��E��F��: G�D�D��F� �� : �"�� #$%: ��: H�I JBKLBM� @� ��E��: G�A��: N�E� � ��F� �� : �"�� &� $: ��: BLO JBKKPM� I� Q�R��F��: ?�Q�� F�: S�C�T�� : ��'� (�� (�� &� �: ��: �HK JBKPBM� O� U�U��: N�E� ��: )� �"�� ) ��: ��: BH P JBKP@M� �� G�?�S��: ��C�V��F�: W�� A�� : R��F�� A��F�: E�� JBKK�M X� V�� Y� H� ��Z��F: S�R�V�� : �� A� � �� D�� W�� [ � C�� Z�� : W��: W�� JBKP M X� V�� Y� P� G�\�\�� : Z�C�V��F��: �� : WZ] C��: �� C��: W�� JBKPLM X� V�� Y� L� W�E��: �� : U�U�� : �� ( �� : ��: BH� J@ IM� K� S�\�W��F� : U� ��F � �� C��: �� C��: W�� JBKHBM X� V�� Y� �� !��"��!#�$��"��$�� "#$%�#$&�'()��$& �&+-��7#$& %#/0#'(%1'$1 3(-#7$�+%� $#'�.$&.(7$5 3$(�#$� 0('(/#%'( (%&/$&�& �(-#,&�& 0&'2�,1 +0-(.1 �� %�! �� #'#3 .��$&�#$$2 �$%#�'(� -�$5 �$%#$+.$&+%#6 $(�+%'1,%1'$&�& �& +%'1,%1'$&�& .��8%%�. $( /(-5 8'#�� .+�,5 ,1%(5� ^2.-#$&: >& �3 3'&+%($$2/ %#/0#'(%1' .��0(-1 .��81.(_%�+2 �&�(%,&.# 3(0&.$#$$2 (%&/(/ ;+.&`5 .13-�.; 1 �'(%�� +0-(.1� <(+%,&.# '&3.0&'2�,1.($$2 +0-(.1 81-& �&+2�$1%& /#5($��$/ 0&-�'1.($$2/: >& +0&+%#'��(-&+2 �#'#3 3/#$�#$$2 �$%#$+� .$&+%#6 $(�+%'1,%1'$5 '#)-#,+�.� =(,( 0&.#��$,( 0('(/#%'( �(-#,&�& 0&'2�,1 +.��%� 0'& %#: >& . +0-(.� �� %�! �� .��81.(�%�+2 )(3&.� 0#'#5&�* �'1�&�& '&�1� �� !!� �� + ��
id	nasplib_isofts_kiev_ua-123456789-139740
institution	Digital Library of Periodicals of National Academy of Sciences of Ukraine
issn	1027-5495
language	English
last_indexed	2025-12-07T17:26:02Z
publishDate	2005
publisher	НТК «Інститут монокристалів» НАН України
record_format	dspace
spelling	Repetsky, S.P. Yaremko, R.O. 2018-06-21T09:39:25Z 2018-06-21T09:39:25Z 2005 X-ray diffraction study of atomic long-range order of Fe-AI alloy / S.P. Repetsky, R.O. Yaremko // Functional Materials. — 2005. — Т. 12, № 1. — С. 124-126. — Бібліогр.: 9 назв. — англ. 1027-5495 https://nasplib.isofts.kiev.ua/handle/123456789/139740 Temperature dependence of nonequilibrium values of Fe-AI alloy long-range order parameter has been studied using X-ray diffraction by comparing the integrated intensity of superstructure reflection and fundamental one at small Bragg angles. An additional atomic occupancy of corresponding sublattice sites has been shown to occur as the annealing temperature increases. A partial disordering of the alloy was provided by mechanical polishing with diamond paste; it was manifested itself as a decreasing of superstructure reflection intensities. Such behavior of the long-range order parameter of Fe-50 at. % Al alloy shows that the second order phase transformations are typical of that alloy. Рентгенографически исследована температурная зависимость неравновесных значений параметра дальнего атомного порядка сплава Fe-50 ат.% AI по отношению интегральных интенсивностей надструктурного к структурному отражений на малых брег-говских углах. Обнаружено, что с повышением температуры отжига происходит дополнительное заполнение атомами узлов "своих подрешеток". Частично разупорядоченное состояние было достигнуто механическим полированием сплава, что наблюдалось по уменьшению интенсивностей надструктурных рефлексов. Такое поведение параметра дальнего порядка свидетельствует о том, что для сплава Fe-50 ат.% AI характерны фазовые превращения второго рода. Рентгенографічно досліджено температурну залежність нерівноважних значень параметра атомного далекого порядку сплаву Fe-50 ат.% АІ через відношення інтегральних інтенсивностей надструктурного до структурного відбиттів на малих бреггі-вських кутах. Виявлено, що із зростанням температур відпалу відбувається додаткове заповнення атомами "своїх вузлів" у гратці сплаву. Часткове розвпорядкування сплаву було досягнуто механічним поліруванням, що спостерігалося через зменшення інтенсивностей надструктурних рефлексів. Така поведінка параметра далекого порядку свідчить про те, що в сплаві Fe-50 ат.% АІ відбуваються фазові переходи другого роду. en НТК «Інститут монокристалів» НАН України Functional Materials X-ray diffraction study of atomic long-range order of Fe-AI alloy Рентгенографічне дослідження атомного далекого порядку в сплаві Fe-AI Article published earlier
spellingShingle	X-ray diffraction study of atomic long-range order of Fe-AI alloy Repetsky, S.P. Yaremko, R.O.
title	X-ray diffraction study of atomic long-range order of Fe-AI alloy
title_alt	Рентгенографічне дослідження атомного далекого порядку в сплаві Fe-AI
title_full	X-ray diffraction study of atomic long-range order of Fe-AI alloy
title_fullStr	X-ray diffraction study of atomic long-range order of Fe-AI alloy
title_full_unstemmed	X-ray diffraction study of atomic long-range order of Fe-AI alloy
title_short	X-ray diffraction study of atomic long-range order of Fe-AI alloy
title_sort	x-ray diffraction study of atomic long-range order of fe-ai alloy
url	https://nasplib.isofts.kiev.ua/handle/123456789/139740
work_keys_str_mv	AT repetskysp xraydiffractionstudyofatomiclongrangeorderoffeaialloy AT yaremkoro xraydiffractionstudyofatomiclongrangeorderoffeaialloy AT repetskysp rentgenografíčnedoslídžennâatomnogodalekogoporâdkuvsplavífeai AT yaremkoro rentgenografíčnedoslídžennâatomnogodalekogoporâdkuvsplavífeai

X-ray diffraction study of atomic long-range order of Fe-AI alloy

Institution

Similar Items