Friction-wear behaviors of chemical vapor deposited diamond films at high temperatures
A diamond film was deposited on YT14 hard alloy cutting tool using a сhemical vapor deposition. The coefficients of friction and wear behaviors of the obtained diamond films at 500, 600, and 700 °C were investigated using a high temperature tribological tester. The results show that the C of diamond...
Збережено в:
| Опубліковано в: : | Сверхтвердые материалы |
|---|---|
| Дата: | 2019 |
| Автори: | , , |
| Формат: | Стаття |
| Мова: | Англійська |
| Опубліковано: |
Інститут надтвердих матеріалів ім. В.М. Бакуля НАН України
2019
|
| Теми: | |
| Онлайн доступ: | https://nasplib.isofts.kiev.ua/handle/123456789/167299 |
| Теги: |
Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Цитувати: | Friction-wear behaviors of chemical vapor deposited diamond films at high temperatures / Kong Dejun, Zhao Wen, Zhang Ling // Надтверді матеріали. — 2019. — № 2 (238). — С. 39-48. — Бібліогр.: 23 назв. — англ. |
Репозитарії
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862649882453475328 |
|---|---|
| author | Kong Dejun Zhao Wen Zhang Ling |
| author_facet | Kong Dejun Zhao Wen Zhang Ling |
| citation_txt | Friction-wear behaviors of chemical vapor deposited diamond films at high temperatures / Kong Dejun, Zhao Wen, Zhang Ling // Надтверді матеріали. — 2019. — № 2 (238). — С. 39-48. — Бібліогр.: 23 назв. — англ. |
| collection | DSpace DC |
| container_title | Сверхтвердые материалы |
| description | A diamond film was deposited on YT14 hard alloy cutting tool using a сhemical vapor deposition. The coefficients of friction and wear behaviors of the obtained diamond films at 500, 600, and 700 °C were investigated using a high temperature tribological tester. The results show that the C of diamond film is fully released at 700 °C, generating CO and CO₂2. The (220) plane of diamond film is oxidized fully at 500 °C, while the (110) plane of diamond film is oxidized at 700 °C. The average coefficients of friction of diamond film at 500, 600 and 700 °C are 0.55, 0.49, and 0.48, respectively, the wear mechanism is primarily oxidation wear, adhesive wear and abrasive wear, accompanied with fatigue wear.
Коефіцієнт тертя і характер зносу алмазних плівок, нанесених на ріжучий інструмент з твердого сплаву YT14 методом хімічного осадження з парової фази, досліджено високотемпературним трибометром при температурі 500, 600 і 700 °C. Результати показали, що вуглець алмазної плівки повністю вільний при 700 °C і утворює сполуки СО і СО₂. Площина (220) алмазної плівки окислюється при 500 °C, а площину (110) – при 700 °C. Середні коефіцієнти тертя алмазної плівки при 500, 600 і 700 °C становлять 0,55, 0,49 і 0,48 відповідно, механізмом зносу є переважно знос, викликаний окисленням, і абразивний знос, що супроводжується втомним і адгезійним зносом.
Коэффициент трения и характер износа алмазных пленок, нанесенных на режущий инструмент из твердого сплава YT14 методом химического осаждения из паровой фазы, были исследованы высокотемпературным трибометром при температуре 500, 600 и 700 °C. Результаты показали, что углерод алмазной пленки полностью свободен при 700 °C и образует соединения СО и СО₂. Плоскость (220) алмазной пленки окисляется при 500 °C, а плоскость (110) – при 700 °C. Средние коэффициенты трения алмазной пленки при 500, 600 и 700 °C составляют 0,55, 0,49 и 0,48 соответственно, механизмом износа является главным образом износ, вызванный окислением, и абразивный износ, сопровождаемый усталостным и адгезионным износом.
|
| first_indexed | 2025-12-01T16:59:50Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-167299 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 0203-3119 |
| language | English |
| last_indexed | 2025-12-01T16:59:50Z |
| publishDate | 2019 |
| publisher | Інститут надтвердих матеріалів ім. В.М. Бакуля НАН України |
| record_format | dspace |
| spelling | Kong Dejun Zhao Wen Zhang Ling 2020-03-23T19:51:04Z 2020-03-23T19:51:04Z 2019 Friction-wear behaviors of chemical vapor deposited diamond films at high temperatures / Kong Dejun, Zhao Wen, Zhang Ling // Надтверді матеріали. — 2019. — № 2 (238). — С. 39-48. — Бібліогр.: 23 назв. — англ. 0203-3119 https://nasplib.isofts.kiev.ua/handle/123456789/167299 620.178.16:621.921.34-488:621.793.3 A diamond film was deposited on YT14 hard alloy cutting tool using a сhemical vapor deposition. The coefficients of friction and wear behaviors of the obtained diamond films at 500, 600, and 700 °C were investigated using a high temperature tribological tester. The results show that the C of diamond film is fully released at 700 °C, generating CO and CO₂2. The (220) plane of diamond film is oxidized fully at 500 °C, while the (110) plane of diamond film is oxidized at 700 °C. The average coefficients of friction of diamond film at 500, 600 and 700 °C are 0.55, 0.49, and 0.48, respectively, the wear mechanism is primarily oxidation wear, adhesive wear and abrasive wear, accompanied with fatigue wear. Коефіцієнт тертя і характер зносу алмазних плівок, нанесених на ріжучий інструмент з твердого сплаву YT14 методом хімічного осадження з парової фази, досліджено високотемпературним трибометром при температурі 500, 600 і 700 °C. Результати показали, що вуглець алмазної плівки повністю вільний при 700 °C і утворює сполуки СО і СО₂. Площина (220) алмазної плівки окислюється при 500 °C, а площину (110) – при 700 °C. Середні коефіцієнти тертя алмазної плівки при 500, 600 і 700 °C становлять 0,55, 0,49 і 0,48 відповідно, механізмом зносу є переважно знос, викликаний окисленням, і абразивний знос, що супроводжується втомним і адгезійним зносом. Коэффициент трения и характер износа алмазных пленок, нанесенных на режущий инструмент из твердого сплава YT14 методом химического осаждения из паровой фазы, были исследованы высокотемпературным трибометром при температуре 500, 600 и 700 °C. Результаты показали, что углерод алмазной пленки полностью свободен при 700 °C и образует соединения СО и СО₂. Плоскость (220) алмазной пленки окисляется при 500 °C, а плоскость (110) – при 700 °C. Средние коэффициенты трения алмазной пленки при 500, 600 и 700 °C составляют 0,55, 0,49 и 0,48 соответственно, механизмом износа является главным образом износ, вызванный окислением, и абразивный износ, сопровождаемый усталостным и адгезионным износом. en Інститут надтвердих матеріалів ім. В.М. Бакуля НАН України Сверхтвердые материалы Одержання, структура, властивості Friction-wear behaviors of chemical vapor deposited diamond films at high temperatures Article published earlier |
| spellingShingle | Friction-wear behaviors of chemical vapor deposited diamond films at high temperatures Kong Dejun Zhao Wen Zhang Ling Одержання, структура, властивості |
| title | Friction-wear behaviors of chemical vapor deposited diamond films at high temperatures |
| title_full | Friction-wear behaviors of chemical vapor deposited diamond films at high temperatures |
| title_fullStr | Friction-wear behaviors of chemical vapor deposited diamond films at high temperatures |
| title_full_unstemmed | Friction-wear behaviors of chemical vapor deposited diamond films at high temperatures |
| title_short | Friction-wear behaviors of chemical vapor deposited diamond films at high temperatures |
| title_sort | friction-wear behaviors of chemical vapor deposited diamond films at high temperatures |
| topic | Одержання, структура, властивості |
| topic_facet | Одержання, структура, властивості |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/167299 |
| work_keys_str_mv | AT kongdejun frictionwearbehaviorsofchemicalvapordepositeddiamondfilmsathightemperatures AT zhaowen frictionwearbehaviorsofchemicalvapordepositeddiamondfilmsathightemperatures AT zhangling frictionwearbehaviorsofchemicalvapordepositeddiamondfilmsathightemperatures |