Long-Term Aging Effect on the Crack Growth in the of Main Circulating Pump Casing Material
Fatigue crack growth (FCG) tests on the main circulating pump casing material were conducted at room temperature to investigate the effect of long-term aging at 400°C. It was found that the FCG rate increased with aging time. However, there were similar ∆Kth values for both the virgin material and a...
Збережено в:
| Опубліковано в: : | Проблемы прочности |
|---|---|
| Дата: | 2015 |
| Автори: | , , , , |
| Формат: | Стаття |
| Мова: | Англійська |
| Опубліковано: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2015
|
| Теми: | |
| Онлайн доступ: | https://nasplib.isofts.kiev.ua/handle/123456789/173271 |
| Теги: |
Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Цитувати: | Long-Term Aging Effect on the Crack Growth in the of Main Circulating Pump Casing Material / F. Xue, W. Yu, M. Yu, W. Liu, G. Shu // Проблемы прочности. — 2015. — № 1. — С. 116-123. — Бібліогр.: 12 назв. — англ. |
Репозитарії
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862605810979307520 |
|---|---|
| author | Xue, F. Yu, W. Yu, M. Liu, W. Shu, G. |
| author_facet | Xue, F. Yu, W. Yu, M. Liu, W. Shu, G. |
| citation_txt | Long-Term Aging Effect on the Crack Growth in the of Main Circulating Pump Casing Material / F. Xue, W. Yu, M. Yu, W. Liu, G. Shu // Проблемы прочности. — 2015. — № 1. — С. 116-123. — Бібліогр.: 12 назв. — англ. |
| collection | DSpace DC |
| container_title | Проблемы прочности |
| description | Fatigue crack growth (FCG) tests on the main circulating pump casing material were conducted at room temperature to investigate the effect of long-term aging at 400°C. It was found that the FCG rate increased with aging time. However, there were similar ∆Kth values for both the virgin material and aged material at the same stress ratios R. At room temperature, ∆Kth was observed to decrease with an increase in R. An equation incorporating the Kmax and ∆K effects was proposed to describe FCG rates over the linear portion of the curve (Paris equation) for all stress ratios. Additionally, fatigue fracture patterns near crack initiation sites reveals quasi-cleavage fracture in thermally aged specimens.
Испытания на сопротивление росту усталостных трещин в материале корпуса главного циркуляционного насоса при комнатной температуре были проведены с целью изучения влияния долговременного старения при 400°С. Установлено, что скорость роста трещин возрастает по мере увеличения времени старения. Однако при одинаковых коэффициентах асимметрии R получены близкие значения ∆Kth для исходного и состаренного материала. Установлено, что при комнатной температуре ∆Kth снижается с увеличением R. Для описания скорости роста усталостных трещин на линейном участке кривой (уравнение Париса) для всех значений коэффициента асимметрии предложено уравнение, учитывающее влияние величин Kmax и ∆K. Характер усталостного разрушения вблизи области зарождения трещин соответствует квазихрупкому излому образцов, подвергшихся термическому старению.
|
| first_indexed | 2025-11-28T12:22:32Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-173271 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 0556-171X |
| language | English |
| last_indexed | 2025-11-28T12:22:32Z |
| publishDate | 2015 |
| publisher | Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| record_format | dspace |
| spelling | Xue, F. Yu, W. Yu, M. Liu, W. Shu, G. 2020-11-28T15:11:30Z 2020-11-28T15:11:30Z 2015 Long-Term Aging Effect on the Crack Growth in the of Main Circulating Pump Casing Material / F. Xue, W. Yu, M. Yu, W. Liu, G. Shu // Проблемы прочности. — 2015. — № 1. — С. 116-123. — Бібліогр.: 12 назв. — англ. 0556-171X https://nasplib.isofts.kiev.ua/handle/123456789/173271 539.4 Fatigue crack growth (FCG) tests on the main circulating pump casing material were conducted at room temperature to investigate the effect of long-term aging at 400°C. It was found that the FCG rate increased with aging time. However, there were similar ∆Kth values for both the virgin material and aged material at the same stress ratios R. At room temperature, ∆Kth was observed to decrease with an increase in R. An equation incorporating the Kmax and ∆K effects was proposed to describe FCG rates over the linear portion of the curve (Paris equation) for all stress ratios. Additionally, fatigue fracture patterns near crack initiation sites reveals quasi-cleavage fracture in thermally aged specimens. Испытания на сопротивление росту усталостных трещин в материале корпуса главного циркуляционного насоса при комнатной температуре были проведены с целью изучения влияния долговременного старения при 400°С. Установлено, что скорость роста трещин возрастает по мере увеличения времени старения. Однако при одинаковых коэффициентах асимметрии R получены близкие значения ∆Kth для исходного и состаренного материала. Установлено, что при комнатной температуре ∆Kth снижается с увеличением R. Для описания скорости роста усталостных трещин на линейном участке кривой (уравнение Париса) для всех значений коэффициента асимметрии предложено уравнение, учитывающее влияние величин Kmax и ∆K. Характер усталостного разрушения вблизи области зарождения трещин соответствует квазихрупкому излому образцов, подвергшихся термическому старению. The financial support from National Science and Technology Major Project (2011ZX06004-009) is greatly acknowledged. en Інститут проблем міцності ім. Г.С. Писаренко НАН України Проблемы прочности Научно-технический раздел Long-Term Aging Effect on the Crack Growth in the of Main Circulating Pump Casing Material Влияние долговременного старения на рост трещин в материале корпуса главного циркуляционного насоса Article published earlier |
| spellingShingle | Long-Term Aging Effect on the Crack Growth in the of Main Circulating Pump Casing Material Xue, F. Yu, W. Yu, M. Liu, W. Shu, G. Научно-технический раздел |
| title | Long-Term Aging Effect on the Crack Growth in the of Main Circulating Pump Casing Material |
| title_alt | Влияние долговременного старения на рост трещин в материале корпуса главного циркуляционного насоса |
| title_full | Long-Term Aging Effect on the Crack Growth in the of Main Circulating Pump Casing Material |
| title_fullStr | Long-Term Aging Effect on the Crack Growth in the of Main Circulating Pump Casing Material |
| title_full_unstemmed | Long-Term Aging Effect on the Crack Growth in the of Main Circulating Pump Casing Material |
| title_short | Long-Term Aging Effect on the Crack Growth in the of Main Circulating Pump Casing Material |
| title_sort | long-term aging effect on the crack growth in the of main circulating pump casing material |
| topic | Научно-технический раздел |
| topic_facet | Научно-технический раздел |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/173271 |
| work_keys_str_mv | AT xuef longtermagingeffectonthecrackgrowthintheofmaincirculatingpumpcasingmaterial AT yuw longtermagingeffectonthecrackgrowthintheofmaincirculatingpumpcasingmaterial AT yum longtermagingeffectonthecrackgrowthintheofmaincirculatingpumpcasingmaterial AT liuw longtermagingeffectonthecrackgrowthintheofmaincirculatingpumpcasingmaterial AT shug longtermagingeffectonthecrackgrowthintheofmaincirculatingpumpcasingmaterial AT xuef vliâniedolgovremennogostareniânarosttreŝinvmaterialekorpusaglavnogocirkulâcionnogonasosa AT yuw vliâniedolgovremennogostareniânarosttreŝinvmaterialekorpusaglavnogocirkulâcionnogonasosa AT yum vliâniedolgovremennogostareniânarosttreŝinvmaterialekorpusaglavnogocirkulâcionnogonasosa AT liuw vliâniedolgovremennogostareniânarosttreŝinvmaterialekorpusaglavnogocirkulâcionnogonasosa AT shug vliâniedolgovremennogostareniânarosttreŝinvmaterialekorpusaglavnogocirkulâcionnogonasosa |