Short Fatigue Crack Growth at Different Maintenance Times for LZ50 Steel

Short Fatigue Crack Growth at Different Maintenance Times for LZ50 Steel

Based on the average fatigue life of LZ50 axle steel specimens without surface rolling, five maintenance times were determined. Accordingly, five groups of specimens were turned and rolled at above maintenance times and were fatigued using a replica technique. The results show that the crack growth...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Проблемы прочности
Datum:2015
Hauptverfasser: Yang, B., Ma, B.Q., Zhao, Y.X., Xiao, S.N.
Format: Artikel
Sprache:English
Veröffentlicht: Інститут проблем міцності ім. Г.С. Писаренко НАН України 2015
Schlagworte:
Научно-технический раздел
Online Zugang:https://nasplib.isofts.kiev.ua/handle/123456789/173273
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:Digital Library of Periodicals of National Academy of Sciences of Ukraine
Zitieren:Short Fatigue Crack Growth at Different Maintenance Times for LZ50 Steel / B. Yang, B.Q. Ma, Y.X. Zhao, S.N. Xiao // Проблемы прочности. — 2015. — № 1. — С. 131-140. — Бібліогр.: 18 назв. — англ.

Institution

Digital Library of Periodicals of National Academy of Sciences of Ukraine
id nasplib_isofts_kiev_ua-123456789-173273
record_format dspace
spelling Yang, B.
Ma, B.Q.
Zhao, Y.X.
Xiao, S.N.
2020-11-28T15:17:49Z
2020-11-28T15:17:49Z
2015
Short Fatigue Crack Growth at Different Maintenance Times for LZ50 Steel / B. Yang, B.Q. Ma, Y.X. Zhao, S.N. Xiao // Проблемы прочности. — 2015. — № 1. — С. 131-140. — Бібліогр.: 18 назв. — англ.
0556-171X
https://nasplib.isofts.kiev.ua/handle/123456789/173273
539.4
Based on the average fatigue life of LZ50 axle steel specimens without surface rolling, five maintenance times were determined. Accordingly, five groups of specimens were turned and rolled at above maintenance times and were fatigued using a replica technique. The results show that the crack growth rate is much lower than that before rolling at a given dominant short crack size. The effective short crack density of all specimens decreases significantly after maintenance. However, with the postponement of surface maintenance, the highest effective short crack density for the five studied groups of specimens increases continuously, while the average fatigue life decreases gradually. A maintenance time effect function is presented to refine a short crack growth model described previously. The revifined model can include a significant effect of the maintenance time on short crack growth and predict its patterns at different maintenance times with exiting test results for LZ50 axle steel.
На основании средней усталостной долговечности образцов осевой стали LZ50, не подвергавшихся поверхностной обкатке роликами, были определены пять модельных межремонтных циклов. Соответственно пять групп образцов были обточены и обкатаны роликами при вышеуказанных межремонтных циклах и подвергнуты испытанию на усталость по методу реплик. Результаты показывают, что скорость роста трещин гораздо ниже таковой до обкатки роликами при заданном преобладающем размере коротких трещин. Эффективная плотность коротких трещин для всех образцов значительно уменьшается после обработки. Однако если поверхностную обработку вовремя не выполняют, наибольшая эффективная плотность коротких трещин для пяти исследуемых групп образцов непрерывно возрастает, тогда как средняя усталостная долговечность постепенно снижается. Приведена функция, описывающая эффект межремонтных циклов, для уточнения предложенной ранее модели роста коротких трещин. Уточненная модель может учитывать существенное влияние межремонтного цикла на рост коротких трещин и прогнозировать характер их роста при различных межремонтных циклах на основании полученных результатов испытаний осевой стали LZ50.
This study is supported by the National Natural Science Foundation of China (51205326 and 51275432), the Fundamental Research Funds for the Central Universities (SWJTU11CX075), and the Opening Project of State Key Laboratory of Traction Power (Grant No. 2011TPL_T02).
en
Інститут проблем міцності ім. Г.С. Писаренко НАН України
Проблемы прочности
Научно-технический раздел
Short Fatigue Crack Growth at Different Maintenance Times for LZ50 Steel
Рост коротких усталостных трещин при различных межремонтных циклах для стали LZ50
Article
published earlier
institution Digital Library of Periodicals of National Academy of Sciences of Ukraine
collection DSpace DC
title Short Fatigue Crack Growth at Different Maintenance Times for LZ50 Steel
spellingShingle Short Fatigue Crack Growth at Different Maintenance Times for LZ50 Steel
Yang, B.
Ma, B.Q.
Zhao, Y.X.
Xiao, S.N.
Научно-технический раздел
title_short Short Fatigue Crack Growth at Different Maintenance Times for LZ50 Steel
title_full Short Fatigue Crack Growth at Different Maintenance Times for LZ50 Steel
title_fullStr Short Fatigue Crack Growth at Different Maintenance Times for LZ50 Steel
title_full_unstemmed Short Fatigue Crack Growth at Different Maintenance Times for LZ50 Steel
title_sort short fatigue crack growth at different maintenance times for lz50 steel
author Yang, B.
Ma, B.Q.
Zhao, Y.X.
Xiao, S.N.
author_facet Yang, B.
Ma, B.Q.
Zhao, Y.X.
Xiao, S.N.
topic Научно-технический раздел
topic_facet Научно-технический раздел
publishDate 2015
language English
container_title Проблемы прочности
publisher Інститут проблем міцності ім. Г.С. Писаренко НАН України
format Article
title_alt Рост коротких усталостных трещин при различных межремонтных циклах для стали LZ50
description Based on the average fatigue life of LZ50 axle steel specimens without surface rolling, five maintenance times were determined. Accordingly, five groups of specimens were turned and rolled at above maintenance times and were fatigued using a replica technique. The results show that the crack growth rate is much lower than that before rolling at a given dominant short crack size. The effective short crack density of all specimens decreases significantly after maintenance. However, with the postponement of surface maintenance, the highest effective short crack density for the five studied groups of specimens increases continuously, while the average fatigue life decreases gradually. A maintenance time effect function is presented to refine a short crack growth model described previously. The revifined model can include a significant effect of the maintenance time on short crack growth and predict its patterns at different maintenance times with exiting test results for LZ50 axle steel. На основании средней усталостной долговечности образцов осевой стали LZ50, не подвергавшихся поверхностной обкатке роликами, были определены пять модельных межремонтных циклов. Соответственно пять групп образцов были обточены и обкатаны роликами при вышеуказанных межремонтных циклах и подвергнуты испытанию на усталость по методу реплик. Результаты показывают, что скорость роста трещин гораздо ниже таковой до обкатки роликами при заданном преобладающем размере коротких трещин. Эффективная плотность коротких трещин для всех образцов значительно уменьшается после обработки. Однако если поверхностную обработку вовремя не выполняют, наибольшая эффективная плотность коротких трещин для пяти исследуемых групп образцов непрерывно возрастает, тогда как средняя усталостная долговечность постепенно снижается. Приведена функция, описывающая эффект межремонтных циклов, для уточнения предложенной ранее модели роста коротких трещин. Уточненная модель может учитывать существенное влияние межремонтного цикла на рост коротких трещин и прогнозировать характер их роста при различных межремонтных циклах на основании полученных результатов испытаний осевой стали LZ50.
issn 0556-171X
url https://nasplib.isofts.kiev.ua/handle/123456789/173273
citation_txt Short Fatigue Crack Growth at Different Maintenance Times for LZ50 Steel / B. Yang, B.Q. Ma, Y.X. Zhao, S.N. Xiao // Проблемы прочности. — 2015. — № 1. — С. 131-140. — Бібліогр.: 18 назв. — англ.
work_keys_str_mv AT yangb shortfatiguecrackgrowthatdifferentmaintenancetimesforlz50steel
AT mabq shortfatiguecrackgrowthatdifferentmaintenancetimesforlz50steel
AT zhaoyx shortfatiguecrackgrowthatdifferentmaintenancetimesforlz50steel
AT xiaosn shortfatiguecrackgrowthatdifferentmaintenancetimesforlz50steel
AT yangb rostkorotkihustalostnyhtreŝinprirazličnyhmežremontnyhciklahdlâstalilz50
AT mabq rostkorotkihustalostnyhtreŝinprirazličnyhmežremontnyhciklahdlâstalilz50
AT zhaoyx rostkorotkihustalostnyhtreŝinprirazličnyhmežremontnyhciklahdlâstalilz50
AT xiaosn rostkorotkihustalostnyhtreŝinprirazličnyhmežremontnyhciklahdlâstalilz50
first_indexed 2025-12-07T17:11:26Z
last_indexed 2025-12-07T17:11:26Z
_version_ 1850870319519105024

Ähnliche Einträge