Fracture Criterion for the Tensile Test of 7075 Aluminum Alloy
True stress-strain values were obtained from the tensile tests of 7075 aluminum alloy and finite element analysis. The results revealed that different ductile fracture criteria resulted in different accuracy of analysis. Moreover, factors affecting ductile fracture, such as effective stress, effecti...
Gespeichert in:
| Veröffentlicht in: | Проблемы прочности |
|---|---|
| Datum: | 2015 |
| Hauptverfasser: | , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2015
|
| Schlagworte: | |
| Online Zugang: | https://nasplib.isofts.kiev.ua/handle/123456789/173274 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Fracture Criterion for the Tensile Test of 7075 Aluminum Alloy / D.C. Chen, C.S. You // Проблемы прочности. — 2015. — № 1. — С. 141-147. — Бібліогр.: 11 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| id |
nasplib_isofts_kiev_ua-123456789-173274 |
|---|---|
| record_format |
dspace |
| spelling |
Chen, D.C. You, C.S. 2020-11-28T15:21:03Z 2020-11-28T15:21:03Z 2015 Fracture Criterion for the Tensile Test of 7075 Aluminum Alloy / D.C. Chen, C.S. You // Проблемы прочности. — 2015. — № 1. — С. 141-147. — Бібліогр.: 11 назв. — англ. 0556-171X https://nasplib.isofts.kiev.ua/handle/123456789/173274 539.4 True stress-strain values were obtained from the tensile tests of 7075 aluminum alloy and finite element analysis. The results revealed that different ductile fracture criteria resulted in different accuracy of analysis. Moreover, factors affecting ductile fracture, such as effective stress, effective strain, and damage were analyzed. The maximum damage level occurred in the center, with its value reaching 0.454. The break happened in 12.9 s in the P1 point. In the P3 point, fracture was not revealed. It can be seen that the maximum damage was observed over the fracture area in the P1 point. Finite element analysis as applied to the 7075 aluminum alloy fracture criteria can be used for forging, drawing, and stamping of the materials. Истинные значения деформации при напряжении были получены при испытаниях на растяжение образцов алюминиевого сплава 7075 и на основании конечноэлементного анализа. Результаты показали, что использование различных критериев вязкого разрушения приводит к разной точности анализа. Проанализированы факторы, влияющие на вязкое разрушение, а именно: эффективное напряжение, эффективная деформация, повреждение. Максимальный уровень повреждения наблюдается в центре, достигая значения 0,454. Разрушение наступало через 12,9 с в точке Р1. В точке Р3 разрушение не обнаруживалось. Видно, что максимальное повреждение имеет место в зоне разрушения (точка Р1). Конечноэлементный анализ применительно к критериям разрушения алюминиевого сплава А7075 может использоваться для ковки, волочения и штамповки материалов. en Інститут проблем міцності ім. Г.С. Писаренко НАН України Проблемы прочности Научно-технический раздел Fracture Criterion for the Tensile Test of 7075 Aluminum Alloy Критерий разрушения для испытания на растяжение алюминиевого сплава 7075 Article published earlier |
| institution |
Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| collection |
DSpace DC |
| title |
Fracture Criterion for the Tensile Test of 7075 Aluminum Alloy |
| spellingShingle |
Fracture Criterion for the Tensile Test of 7075 Aluminum Alloy Chen, D.C. You, C.S. Научно-технический раздел |
| title_short |
Fracture Criterion for the Tensile Test of 7075 Aluminum Alloy |
| title_full |
Fracture Criterion for the Tensile Test of 7075 Aluminum Alloy |
| title_fullStr |
Fracture Criterion for the Tensile Test of 7075 Aluminum Alloy |
| title_full_unstemmed |
Fracture Criterion for the Tensile Test of 7075 Aluminum Alloy |
| title_sort |
fracture criterion for the tensile test of 7075 aluminum alloy |
| author |
Chen, D.C. You, C.S. |
| author_facet |
Chen, D.C. You, C.S. |
| topic |
Научно-технический раздел |
| topic_facet |
Научно-технический раздел |
| publishDate |
2015 |
| language |
English |
| container_title |
Проблемы прочности |
| publisher |
Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| format |
Article |
| title_alt |
Критерий разрушения для испытания на растяжение алюминиевого сплава 7075 |
| description |
True stress-strain values were obtained from the tensile tests of 7075 aluminum alloy and finite element analysis. The results revealed that different ductile fracture criteria resulted in different accuracy of analysis. Moreover, factors affecting ductile fracture, such as effective stress, effective strain, and damage were analyzed. The maximum damage level occurred in the center, with its value reaching 0.454. The break happened in 12.9 s in the P1 point. In the P3 point, fracture was not revealed. It can be seen that the maximum damage was observed over the fracture area in the P1 point. Finite element analysis as applied to the 7075 aluminum alloy fracture criteria can be used for forging, drawing, and stamping of the materials.
Истинные значения деформации при напряжении были получены при испытаниях на растяжение образцов алюминиевого сплава 7075 и на основании конечноэлементного анализа. Результаты показали, что использование различных критериев вязкого разрушения приводит к разной точности анализа. Проанализированы факторы, влияющие на вязкое разрушение, а именно: эффективное напряжение, эффективная деформация, повреждение. Максимальный уровень повреждения наблюдается в центре, достигая значения 0,454. Разрушение наступало через 12,9 с в точке Р1. В точке Р3 разрушение не обнаруживалось. Видно, что максимальное повреждение имеет место в зоне разрушения (точка Р1). Конечноэлементный анализ применительно к критериям разрушения алюминиевого сплава А7075 может использоваться для ковки, волочения и штамповки материалов.
|
| issn |
0556-171X |
| url |
https://nasplib.isofts.kiev.ua/handle/123456789/173274 |
| citation_txt |
Fracture Criterion for the Tensile Test of 7075 Aluminum Alloy / D.C. Chen, C.S. You // Проблемы прочности. — 2015. — № 1. — С. 141-147. — Бібліогр.: 11 назв. — англ. |
| work_keys_str_mv |
AT chendc fracturecriterionforthetensiletestof7075aluminumalloy AT youcs fracturecriterionforthetensiletestof7075aluminumalloy AT chendc kriteriirazrušeniâdlâispytaniânarastâženiealûminievogosplava7075 AT youcs kriteriirazrušeniâdlâispytaniânarastâženiealûminievogosplava7075 |
| first_indexed |
2025-12-07T16:21:15Z |
| last_indexed |
2025-12-07T16:21:15Z |
| _version_ |
1850867162317586432 |