Mechanical Behavior of the Weld Joints of Thick Steel Plates Produced by Various Welding Processes
The effect of a welding process (electrogas welding (EGW) and flux cored arc welding (FCAW)) on the fracture toughness, CTOD (crack tip opening displacement), and mechanical properties (tensile, bending, impact strengths and hardness) of thick weld joints is examined. The CTOD value of the FCAW weld...
Gespeichert in:
| Veröffentlicht in: | Проблемы прочности |
|---|---|
| Datum: | 2015 |
| Hauptverfasser: | , , , |
| Format: | Artikel |
| Sprache: | Englisch |
| Veröffentlicht: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2015
|
| Schlagworte: | |
| Online Zugang: | https://nasplib.isofts.kiev.ua/handle/123456789/173287 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Mechanical Behavior of the Weld Joints of Thick Steel Plates Produced by Various Welding Processes / HanSur Bang, HeeSeon Bang, ChanSeung Ro, SuOk Jeong // Проблемы прочности. — 2015. — № 1. — С. 240-249. — Бібліогр.: 14 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862580910888583168 |
|---|---|
| author | Bang, HanSur Bang, HeeSeon Ro, ChanSeung Jeong, SuOk |
| author_facet | Bang, HanSur Bang, HeeSeon Ro, ChanSeung Jeong, SuOk |
| citation_txt | Mechanical Behavior of the Weld Joints of Thick Steel Plates Produced by Various Welding Processes / HanSur Bang, HeeSeon Bang, ChanSeung Ro, SuOk Jeong // Проблемы прочности. — 2015. — № 1. — С. 240-249. — Бібліогр.: 14 назв. — англ. |
| collection | DSpace DC |
| container_title | Проблемы прочности |
| description | The effect of a welding process (electrogas welding (EGW) and flux cored arc welding (FCAW)) on the fracture toughness, CTOD (crack tip opening displacement), and mechanical properties (tensile, bending, impact strengths and hardness) of thick weld joints is examined. The CTOD value of the FCAW weld joints was higher than that of the EGW ones. The fractured welded specimen after the CTOD test reveals ductile and cleavage fractures of the weld joint faces after flux cored arc and electrogas weldings, respectively. The mechanical properties of the EGW welded specimens satisfied relevant classification rules. These results suggest that the EGW process is an effective substitute for the current welding process (FCAW) used for high-strength thick steel plates.
Рассмотрено влияние способа сварки (электрогазовая и дуговая порошковой проволокой) на вязкость разрушения, раскрытие вершины трещины и механические свойства (предел прочности при растяжении, изгибе, ударная вязкость и твердость) сварных швов. Значение раскрытия вершины трещины для швов, полученных дуговой сваркой, было выше такового для швов, полученных электрогазовой сваркой. Разрушенный сварной образец после испытания по определению раскрытия вершины трещины обнаруживает вязкое разрушение и хрупкий излом лицевых поверхностей швов после дуговой и электрогазовой сварки соответственно. Механические свойства сварных образцов после электрогазовой сварки удовлетворяют соответствующим критериям классификации. Эти результаты свидетельствуют о том, что электрогазовая сварка может эффективно заменять используемую в настоящее время дуговую сварку для высокопрочной толстолистовой стали.
|
| first_indexed | 2025-11-26T21:40:58Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-173287 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 0556-171X |
| language | English |
| last_indexed | 2025-11-26T21:40:58Z |
| publishDate | 2015 |
| publisher | Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| record_format | dspace |
| spelling | Bang, HanSur Bang, HeeSeon Ro, ChanSeung Jeong, SuOk 2020-11-28T16:12:52Z 2020-11-28T16:12:52Z 2015 Mechanical Behavior of the Weld Joints of Thick Steel Plates Produced by Various Welding Processes / HanSur Bang, HeeSeon Bang, ChanSeung Ro, SuOk Jeong // Проблемы прочности. — 2015. — № 1. — С. 240-249. — Бібліогр.: 14 назв. — англ. 0556-171X https://nasplib.isofts.kiev.ua/handle/123456789/173287 539.4 The effect of a welding process (electrogas welding (EGW) and flux cored arc welding (FCAW)) on the fracture toughness, CTOD (crack tip opening displacement), and mechanical properties (tensile, bending, impact strengths and hardness) of thick weld joints is examined. The CTOD value of the FCAW weld joints was higher than that of the EGW ones. The fractured welded specimen after the CTOD test reveals ductile and cleavage fractures of the weld joint faces after flux cored arc and electrogas weldings, respectively. The mechanical properties of the EGW welded specimens satisfied relevant classification rules. These results suggest that the EGW process is an effective substitute for the current welding process (FCAW) used for high-strength thick steel plates. Рассмотрено влияние способа сварки (электрогазовая и дуговая порошковой проволокой) на вязкость разрушения, раскрытие вершины трещины и механические свойства (предел прочности при растяжении, изгибе, ударная вязкость и твердость) сварных швов. Значение раскрытия вершины трещины для швов, полученных дуговой сваркой, было выше такового для швов, полученных электрогазовой сваркой. Разрушенный сварной образец после испытания по определению раскрытия вершины трещины обнаруживает вязкое разрушение и хрупкий излом лицевых поверхностей швов после дуговой и электрогазовой сварки соответственно. Механические свойства сварных образцов после электрогазовой сварки удовлетворяют соответствующим критериям классификации. Эти результаты свидетельствуют о том, что электрогазовая сварка может эффективно заменять используемую в настоящее время дуговую сварку для высокопрочной толстолистовой стали. This research was financally supported by the Ministry of Education, Science Technology (MEST) and National Research Foundation of Korea (NRF) through the human resource training project for regional innovation (2012H1B8A2026193). en Інститут проблем міцності ім. Г.С. Писаренко НАН України Проблемы прочности Научно-технический раздел Mechanical Behavior of the Weld Joints of Thick Steel Plates Produced by Various Welding Processes Механическое поведение сварных соединений толстолистовой стали, получаемых различными способами сварки Article published earlier |
| spellingShingle | Mechanical Behavior of the Weld Joints of Thick Steel Plates Produced by Various Welding Processes Bang, HanSur Bang, HeeSeon Ro, ChanSeung Jeong, SuOk Научно-технический раздел |
| title | Mechanical Behavior of the Weld Joints of Thick Steel Plates Produced by Various Welding Processes |
| title_alt | Механическое поведение сварных соединений толстолистовой стали, получаемых различными способами сварки |
| title_full | Mechanical Behavior of the Weld Joints of Thick Steel Plates Produced by Various Welding Processes |
| title_fullStr | Mechanical Behavior of the Weld Joints of Thick Steel Plates Produced by Various Welding Processes |
| title_full_unstemmed | Mechanical Behavior of the Weld Joints of Thick Steel Plates Produced by Various Welding Processes |
| title_short | Mechanical Behavior of the Weld Joints of Thick Steel Plates Produced by Various Welding Processes |
| title_sort | mechanical behavior of the weld joints of thick steel plates produced by various welding processes |
| topic | Научно-технический раздел |
| topic_facet | Научно-технический раздел |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/173287 |
| work_keys_str_mv | AT banghansur mechanicalbehavioroftheweldjointsofthicksteelplatesproducedbyvariousweldingprocesses AT bangheeseon mechanicalbehavioroftheweldjointsofthicksteelplatesproducedbyvariousweldingprocesses AT rochanseung mechanicalbehavioroftheweldjointsofthicksteelplatesproducedbyvariousweldingprocesses AT jeongsuok mechanicalbehavioroftheweldjointsofthicksteelplatesproducedbyvariousweldingprocesses AT banghansur mehaničeskoepovedeniesvarnyhsoedineniitolstolistovoistalipolučaemyhrazličnymisposobamisvarki AT bangheeseon mehaničeskoepovedeniesvarnyhsoedineniitolstolistovoistalipolučaemyhrazličnymisposobamisvarki AT rochanseung mehaničeskoepovedeniesvarnyhsoedineniitolstolistovoistalipolučaemyhrazličnymisposobamisvarki AT jeongsuok mehaničeskoepovedeniesvarnyhsoedineniitolstolistovoistalipolučaemyhrazličnymisposobamisvarki |