Large-Scale Yielding Failure Prediction of Notched Ductile Plates by Means of the Linear Elastic Notch Fracture Mechanics
The main goal of this research is to propose a failure criterion based on the linear elastic notch fracture mechanics (LENFM) for predicting tensile crack initiation from a blunt V-notch, encountering large plasticity at the notch vicinity. First, some most recently published experimental results on...
Gespeichert in:
| Veröffentlicht in: | Проблемы прочности |
|---|---|
| Datum: | 2017 |
| Hauptverfasser: | , , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2017
|
| Schlagworte: | |
| Online Zugang: | https://nasplib.isofts.kiev.ua/handle/123456789/173623 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Large-Scale Yielding Failure Prediction of Notched Ductile Plates by Means of the Linear Elastic Notch Fracture Mechanics / A.R. Torabi, A. Campagnolo, F. Berto // Проблемы прочности. — 2017. — № 2. — С. 18-29. — Бібліогр.: 39 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| id |
nasplib_isofts_kiev_ua-123456789-173623 |
|---|---|
| record_format |
dspace |
| spelling |
Torabi, A.R. Campagnolo, A. Berto, F. 2020-12-13T17:51:20Z 2020-12-13T17:51:20Z 2017 Large-Scale Yielding Failure Prediction of Notched Ductile Plates by Means of the Linear Elastic Notch Fracture Mechanics / A.R. Torabi, A. Campagnolo, F. Berto // Проблемы прочности. — 2017. — № 2. — С. 18-29. — Бібліогр.: 39 назв. — англ. 0556-171X https://nasplib.isofts.kiev.ua/handle/123456789/173623 539.4 The main goal of this research is to propose a failure criterion based on the linear elastic notch fracture mechanics (LENFM) for predicting tensile crack initiation from a blunt V-notch, encountering large plasticity at the notch vicinity. First, some most recently published experimental results on tensile failure of V-notched ductile aluminum plates are briefly described. Then, with the aim to avoid complex and time-consuming elastic-plastic analyses, the equivalent material concept (EMC) is employed together with a LENFM-based fracture criterion, namely the averaged strain energy density (ASED) criterion, for predicting the load-carrying capacity of the V-notched aluminum plates. A very good agreement is shown to exist between the experimental results and theoretical predictions of the EMC-ASED criterion. Предложен критерий разрушения, основанный на линейной упругой механике разрушения, для прогнозирования инициирования трещины растяжения от затупленного V-образного надреза при большой пластичности вблизи надреза. Описаны некоторые современные экспериментальные результаты по разрушению при растяжении пластичных алюминиевых пластин с V-образным надрезом. С целью избежания сложного и трудоемкого упругопластического анализа для прогнозирования несущей способности алюминиевых пластин с V-образным надрезом используются концепция эквивалентного материала и критерий усредненной плотности энергии деформации, базирующийся на линейной упругой механике разрушения. Показано хорошее соответствие между экспериментальными данными и результатами прогнозирования на основе концепции эквивалентного материала и критерия усредненной плотности энергии деформации. Запропоновано критерій руйнування, що базується на лінійній пружній механіці руйнування, для прогнозування ініціювання тріщини розтягу від затупленого V-подібного надрізу при значній пластичності поблизу надрізу. Описано деякі сучасні експериментальні результати щодо руйнування при розтязі пластичних алюмінієвих пластин із V-подібним надрізом. Із метою запобігання складного і трудомісткого аналізу для прогнозування несівної здатності алюмінієвих пластин із V-подібним надрізом використовуються концепція еквівалентного матеріалу і критерій усереднено ї щільності енергії деформації, що базується на лінійній пружній механіці руйнування. Показано хороший збіг експериментальних даних із результатами прогнозування на основі концепції еквівалентного матеріалу і критерію усередненої щільності енергії деформації. en Інститут проблем міцності ім. Г.С. Писаренко НАН України Проблемы прочности Научно-технический раздел Large-Scale Yielding Failure Prediction of Notched Ductile Plates by Means of the Linear Elastic Notch Fracture Mechanics Прогнозирование разрушения при полномасштабном течении в пластинах с надрезом на основе линейной упругой механики разрушения Article published earlier |
| institution |
Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| collection |
DSpace DC |
| title |
Large-Scale Yielding Failure Prediction of Notched Ductile Plates by Means of the Linear Elastic Notch Fracture Mechanics |
| spellingShingle |
Large-Scale Yielding Failure Prediction of Notched Ductile Plates by Means of the Linear Elastic Notch Fracture Mechanics Torabi, A.R. Campagnolo, A. Berto, F. Научно-технический раздел |
| title_short |
Large-Scale Yielding Failure Prediction of Notched Ductile Plates by Means of the Linear Elastic Notch Fracture Mechanics |
| title_full |
Large-Scale Yielding Failure Prediction of Notched Ductile Plates by Means of the Linear Elastic Notch Fracture Mechanics |
| title_fullStr |
Large-Scale Yielding Failure Prediction of Notched Ductile Plates by Means of the Linear Elastic Notch Fracture Mechanics |
| title_full_unstemmed |
Large-Scale Yielding Failure Prediction of Notched Ductile Plates by Means of the Linear Elastic Notch Fracture Mechanics |
| title_sort |
large-scale yielding failure prediction of notched ductile plates by means of the linear elastic notch fracture mechanics |
| author |
Torabi, A.R. Campagnolo, A. Berto, F. |
| author_facet |
Torabi, A.R. Campagnolo, A. Berto, F. |
| topic |
Научно-технический раздел |
| topic_facet |
Научно-технический раздел |
| publishDate |
2017 |
| language |
English |
| container_title |
Проблемы прочности |
| publisher |
Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| format |
Article |
| title_alt |
Прогнозирование разрушения при полномасштабном течении в пластинах с надрезом на основе линейной упругой механики разрушения |
| description |
The main goal of this research is to propose a failure criterion based on the linear elastic notch fracture mechanics (LENFM) for predicting tensile crack initiation from a blunt V-notch, encountering large plasticity at the notch vicinity. First, some most recently published experimental results on tensile failure of V-notched ductile aluminum plates are briefly described. Then, with the aim to avoid complex and time-consuming elastic-plastic analyses, the equivalent material concept (EMC) is employed together with a LENFM-based fracture criterion, namely the averaged strain energy density (ASED) criterion, for predicting the load-carrying capacity of the V-notched aluminum plates. A very good agreement is shown to exist between the experimental results and theoretical predictions of the EMC-ASED criterion.
Предложен критерий разрушения, основанный на линейной упругой механике разрушения, для прогнозирования инициирования трещины растяжения от затупленного V-образного надреза при большой пластичности вблизи надреза. Описаны некоторые современные экспериментальные результаты по разрушению при растяжении пластичных алюминиевых пластин с V-образным надрезом. С целью избежания сложного и трудоемкого упругопластического анализа для прогнозирования несущей способности алюминиевых пластин с V-образным надрезом используются концепция эквивалентного материала и критерий усредненной плотности энергии деформации, базирующийся на линейной упругой механике разрушения. Показано хорошее соответствие между экспериментальными данными и результатами прогнозирования на основе концепции эквивалентного материала и критерия усредненной плотности энергии деформации.
Запропоновано критерій руйнування, що базується на лінійній пружній механіці руйнування, для прогнозування ініціювання тріщини розтягу від затупленого V-подібного надрізу при значній пластичності поблизу надрізу. Описано деякі сучасні експериментальні результати щодо руйнування при розтязі пластичних алюмінієвих пластин із V-подібним надрізом. Із метою запобігання складного і трудомісткого аналізу для прогнозування несівної здатності алюмінієвих пластин із V-подібним надрізом використовуються концепція еквівалентного матеріалу і критерій усереднено ї щільності енергії деформації, що базується на лінійній пружній механіці руйнування. Показано хороший збіг експериментальних даних із результатами прогнозування на основі концепції еквівалентного матеріалу і критерію усередненої щільності енергії деформації.
|
| issn |
0556-171X |
| url |
https://nasplib.isofts.kiev.ua/handle/123456789/173623 |
| citation_txt |
Large-Scale Yielding Failure Prediction of Notched Ductile Plates by Means of the Linear Elastic Notch Fracture Mechanics / A.R. Torabi, A. Campagnolo, F. Berto // Проблемы прочности. — 2017. — № 2. — С. 18-29. — Бібліогр.: 39 назв. — англ. |
| work_keys_str_mv |
AT torabiar largescaleyieldingfailurepredictionofnotchedductileplatesbymeansofthelinearelasticnotchfracturemechanics AT campagnoloa largescaleyieldingfailurepredictionofnotchedductileplatesbymeansofthelinearelasticnotchfracturemechanics AT bertof largescaleyieldingfailurepredictionofnotchedductileplatesbymeansofthelinearelasticnotchfracturemechanics AT torabiar prognozirovanierazrušeniâpripolnomasštabnomtečeniivplastinahsnadrezomnaosnovelineinoiuprugoimehanikirazrušeniâ AT campagnoloa prognozirovanierazrušeniâpripolnomasštabnomtečeniivplastinahsnadrezomnaosnovelineinoiuprugoimehanikirazrušeniâ AT bertof prognozirovanierazrušeniâpripolnomasštabnomtečeniivplastinahsnadrezomnaosnovelineinoiuprugoimehanikirazrušeniâ |
| first_indexed |
2025-12-07T17:27:29Z |
| last_indexed |
2025-12-07T17:27:29Z |
| _version_ |
1850871328923451392 |