Study on the Cracking Mechanism of YQ450NQR1 High-Strength Weathering Steel
YQ450NQR1 high-strength weathering steel is prone to cracking. The cracking patterns and morphology were detected by metallographic and scanning electron microscopies. The decarburized layer around the cracks is indicative of their origination in the continuous casting bloom. Then, the controlling f...
Saved in:
| Published in: | Проблемы прочности |
|---|---|
| Date: | 2018 |
| Main Authors: | , , , , , , |
| Format: | Article |
| Language: | English |
| Published: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2018
|
| Subjects: | |
| Online Access: | https://nasplib.isofts.kiev.ua/handle/123456789/173829 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Journal Title: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Cite this: | Study on the Cracking Mechanism of YQ450NQR1 High-Strength Weathering Steel / J.S. Qing, X.D. Duan, M.F. Xiao, J.Q. Li, M. Liu, Q. Liu, H.F. Shen // Проблемы прочности. — 2018. — № 1. — С. 193-201. — Бібліогр.: 18 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| id |
nasplib_isofts_kiev_ua-123456789-173829 |
|---|---|
| record_format |
dspace |
| spelling |
Qing, J.S. Duan, X.D. Xiao, M.F. Li, J.Q. Liu, M. Liu, Q. Shen, H.F. 2020-12-21T19:22:14Z 2020-12-21T19:22:14Z 2018 Study on the Cracking Mechanism of YQ450NQR1 High-Strength Weathering Steel / J.S. Qing, X.D. Duan, M.F. Xiao, J.Q. Li, M. Liu, Q. Liu, H.F. Shen // Проблемы прочности. — 2018. — № 1. — С. 193-201. — Бібліогр.: 18 назв. — англ. 0556-171X https://nasplib.isofts.kiev.ua/handle/123456789/173829 539.4 YQ450NQR1 high-strength weathering steel is prone to cracking. The cracking patterns and morphology were detected by metallographic and scanning electron microscopies. The decarburized layer around the cracks is indicative of their origination in the continuous casting bloom. Then, the controlling factors were established by analyzing the carbon content of molten steel, residual elements in the alloy, purity and performance of the mold powder, and secondary cooling water flow of the mold. Results show that the process optimization reduced the cracking reject ratio from 3.5 to 0.78%. Высокопрочная сталь YQ450NQR1, стойкая к атмосферной коррозии, проявляет склонность к образованию трещин. Исследованы характер трещинообразования и морфология с помощью металлографической и сканирующей электронной микроскопии. Образование обезуглероженного слоя вокруг трещин свидетельствует об их зарождении в непрерывной литой заготовке. Установлены регулирующие факторы путем анализа содержания углерода в расплавленной стали, остаточных элементов в сплаве, чистоты и эффективности пресс-порошка, расхода воды вторичного охлаждения формы. Показано, что оптимазация процесса снизила уровень отбраковки материала, содержащего трещины, с 3,50 до 0,78%. en Інститут проблем міцності ім. Г.С. Писаренко НАН України Проблемы прочности Научно-технический раздел Study on the Cracking Mechanism of YQ450NQR1 High-Strength Weathering Steel Изучение механизма образования трещин в высокопрочной стали YQ450NQR1, стойкой к атмосферной коррозии Article published earlier |
| institution |
Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| collection |
DSpace DC |
| title |
Study on the Cracking Mechanism of YQ450NQR1 High-Strength Weathering Steel |
| spellingShingle |
Study on the Cracking Mechanism of YQ450NQR1 High-Strength Weathering Steel Qing, J.S. Duan, X.D. Xiao, M.F. Li, J.Q. Liu, M. Liu, Q. Shen, H.F. Научно-технический раздел |
| title_short |
Study on the Cracking Mechanism of YQ450NQR1 High-Strength Weathering Steel |
| title_full |
Study on the Cracking Mechanism of YQ450NQR1 High-Strength Weathering Steel |
| title_fullStr |
Study on the Cracking Mechanism of YQ450NQR1 High-Strength Weathering Steel |
| title_full_unstemmed |
Study on the Cracking Mechanism of YQ450NQR1 High-Strength Weathering Steel |
| title_sort |
study on the cracking mechanism of yq450nqr1 high-strength weathering steel |
| author |
Qing, J.S. Duan, X.D. Xiao, M.F. Li, J.Q. Liu, M. Liu, Q. Shen, H.F. |
| author_facet |
Qing, J.S. Duan, X.D. Xiao, M.F. Li, J.Q. Liu, M. Liu, Q. Shen, H.F. |
| topic |
Научно-технический раздел |
| topic_facet |
Научно-технический раздел |
| publishDate |
2018 |
| language |
English |
| container_title |
Проблемы прочности |
| publisher |
Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| format |
Article |
| title_alt |
Изучение механизма образования трещин в высокопрочной стали YQ450NQR1, стойкой к атмосферной коррозии |
| description |
YQ450NQR1 high-strength weathering steel is prone to cracking. The cracking patterns and morphology were detected by metallographic and scanning electron microscopies. The decarburized layer around the cracks is indicative of their origination in the continuous casting bloom. Then, the controlling factors were established by analyzing the carbon content of molten steel, residual elements in the alloy, purity and performance of the mold powder, and secondary cooling water flow of the mold. Results show that the process optimization reduced the cracking reject ratio from 3.5 to 0.78%.
Высокопрочная сталь YQ450NQR1, стойкая к атмосферной коррозии, проявляет склонность к образованию трещин. Исследованы характер трещинообразования и морфология с помощью металлографической и сканирующей электронной микроскопии. Образование обезуглероженного слоя вокруг трещин свидетельствует об их зарождении в непрерывной литой заготовке. Установлены регулирующие факторы путем анализа содержания углерода в расплавленной стали, остаточных элементов в сплаве, чистоты и эффективности пресс-порошка, расхода воды вторичного охлаждения формы. Показано, что оптимазация процесса снизила уровень отбраковки материала, содержащего трещины, с 3,50 до 0,78%.
|
| issn |
0556-171X |
| url |
https://nasplib.isofts.kiev.ua/handle/123456789/173829 |
| citation_txt |
Study on the Cracking Mechanism of YQ450NQR1 High-Strength Weathering Steel / J.S. Qing, X.D. Duan, M.F. Xiao, J.Q. Li, M. Liu, Q. Liu, H.F. Shen // Проблемы прочности. — 2018. — № 1. — С. 193-201. — Бібліогр.: 18 назв. — англ. |
| work_keys_str_mv |
AT qingjs studyonthecrackingmechanismofyq450nqr1highstrengthweatheringsteel AT duanxd studyonthecrackingmechanismofyq450nqr1highstrengthweatheringsteel AT xiaomf studyonthecrackingmechanismofyq450nqr1highstrengthweatheringsteel AT lijq studyonthecrackingmechanismofyq450nqr1highstrengthweatheringsteel AT lium studyonthecrackingmechanismofyq450nqr1highstrengthweatheringsteel AT liuq studyonthecrackingmechanismofyq450nqr1highstrengthweatheringsteel AT shenhf studyonthecrackingmechanismofyq450nqr1highstrengthweatheringsteel AT qingjs izučeniemehanizmaobrazovaniâtreŝinvvysokopročnoistaliyq450nqr1stoikoikatmosfernoikorrozii AT duanxd izučeniemehanizmaobrazovaniâtreŝinvvysokopročnoistaliyq450nqr1stoikoikatmosfernoikorrozii AT xiaomf izučeniemehanizmaobrazovaniâtreŝinvvysokopročnoistaliyq450nqr1stoikoikatmosfernoikorrozii AT lijq izučeniemehanizmaobrazovaniâtreŝinvvysokopročnoistaliyq450nqr1stoikoikatmosfernoikorrozii AT lium izučeniemehanizmaobrazovaniâtreŝinvvysokopročnoistaliyq450nqr1stoikoikatmosfernoikorrozii AT liuq izučeniemehanizmaobrazovaniâtreŝinvvysokopročnoistaliyq450nqr1stoikoikatmosfernoikorrozii AT shenhf izučeniemehanizmaobrazovaniâtreŝinvvysokopročnoistaliyq450nqr1stoikoikatmosfernoikorrozii |
| first_indexed |
2025-12-01T10:52:22Z |
| last_indexed |
2025-12-01T10:52:22Z |
| _version_ |
1850859955804962816 |