Short Fatigue Crack Behavior of LZ50 Axle Steel under Rotating-Bending Cyclic Loading
The short fatigue short crack replica tests using LZ50 axle steel hourglass-shaped specimens of were carried out under rotating-bending cyclic load. Seven sets of effective test data were obtained. The analysis demonstrated that short fatigue cracks generally originate in ferrite grains or on their...
Saved in:
| Published in: | Проблемы прочности |
|---|---|
| Date: | 2018 |
| Main Authors: | , , , , , |
| Format: | Article |
| Language: | English |
| Published: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2018
|
| Subjects: | |
| Online Access: | https://nasplib.isofts.kiev.ua/handle/123456789/173831 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Journal Title: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Cite this: | Short Fatigue Crack Behavior of LZ50 Axle Steel under Rotating-Bending Cyclic Loading / B. Yang, S. Dai, Y.Y. Wu, Z. Liao, S. Liang, S.N. Xiao // Проблемы прочности. — 2018. — № 1. — С. 212-222.. — Бібліогр.: 14 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862597234657329152 |
|---|---|
| author | Yang, B. Dai, S. Wu, Y.Y. Liao, Z. Liang, S. Xiao, S.N. |
| author_facet | Yang, B. Dai, S. Wu, Y.Y. Liao, Z. Liang, S. Xiao, S.N. |
| citation_txt | Short Fatigue Crack Behavior of LZ50 Axle Steel under Rotating-Bending Cyclic Loading / B. Yang, S. Dai, Y.Y. Wu, Z. Liao, S. Liang, S.N. Xiao // Проблемы прочности. — 2018. — № 1. — С. 212-222.. — Бібліогр.: 14 назв. — англ. |
| collection | DSpace DC |
| container_title | Проблемы прочности |
| description | The short fatigue short crack replica tests using LZ50 axle steel hourglass-shaped specimens of were carried out under rotating-bending cyclic load. Seven sets of effective test data were obtained. The analysis demonstrated that short fatigue cracks generally originate in ferrite grains or on their boundaries, and then short cracks start propagating, which is strongly influenced by the microstructure of the material. The crack growth rate increases serratically, followed by its decrease double-fold because of the limit of ferrite grain boundaries and the banded pearlite structure. Based on the three principles of the best fit, which include the overall fitting effect, correlation with fatigue physics, and safety of residual strength prediction, the statistical evolution of the dominant effective short fatigue crack length and life share were analyzed. The statistical results show that the minimum value distribution exhibit the best fit of the dominant effective fatigue short crack length and the life share. The short fatigue crack growth model, which includes various microstructure barriers, provides a good fitting result and reflects the cyclic effect of the microstructure on the short fatigue crack behavior
Выполнены испытания на репликах короткой усталостной трещины с использованием образцов осевой стали LZ50 в форме песочных часов в условиях циклического нагружения при изгибе с вращением. Выполнены семь серий испытаний. Показано, что короткие усталостные трещины возникают в ферритных зернах или на их границах, затем они начинают расти под влиянием микроструктуры материала. Скорость роста трещин увеличивается скачкообразно, затем снижается вдвое за счет барьера, создаваемого границами ферритных зерен и полосчатой структурой перлита. Проанализированы статистическая эволюция длины доминирующей эффективной короткой усталостной трещины и доля остаточного ресурса на основании трех принципов наилучшего соответствия, включающих общий эффект соответствия, соответствие принципам физики усталости и надежность прогнозирования остаточной прочности. Установлено, что статистическое распределение минимальных величин выявляет наилучшее соответствие для длины доминирующей эффективной короткой усталостной трещины и доли остаточного ресурса. Модель роста короткой усталостной трещины, включающая различные барьеры в микроструктуре, обеспечивает хороший результат подгонки и отражает циклическое влияние микроструктуры на ее поведение.
|
| first_indexed | 2025-11-27T17:19:08Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-173831 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 0556-171X |
| language | English |
| last_indexed | 2025-11-27T17:19:08Z |
| publishDate | 2018 |
| publisher | Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| record_format | dspace |
| spelling | Yang, B. Dai, S. Wu, Y.Y. Liao, Z. Liang, S. Xiao, S.N. 2020-12-21T19:31:46Z 2020-12-21T19:31:46Z 2018 Short Fatigue Crack Behavior of LZ50 Axle Steel under Rotating-Bending Cyclic Loading / B. Yang, S. Dai, Y.Y. Wu, Z. Liao, S. Liang, S.N. Xiao // Проблемы прочности. — 2018. — № 1. — С. 212-222.. — Бібліогр.: 14 назв. — англ. 0556-171X https://nasplib.isofts.kiev.ua/handle/123456789/173831 539.4 The short fatigue short crack replica tests using LZ50 axle steel hourglass-shaped specimens of were carried out under rotating-bending cyclic load. Seven sets of effective test data were obtained. The analysis demonstrated that short fatigue cracks generally originate in ferrite grains or on their boundaries, and then short cracks start propagating, which is strongly influenced by the microstructure of the material. The crack growth rate increases serratically, followed by its decrease double-fold because of the limit of ferrite grain boundaries and the banded pearlite structure. Based on the three principles of the best fit, which include the overall fitting effect, correlation with fatigue physics, and safety of residual strength prediction, the statistical evolution of the dominant effective short fatigue crack length and life share were analyzed. The statistical results show that the minimum value distribution exhibit the best fit of the dominant effective fatigue short crack length and the life share. The short fatigue crack growth model, which includes various microstructure barriers, provides a good fitting result and reflects the cyclic effect of the microstructure on the short fatigue crack behavior Выполнены испытания на репликах короткой усталостной трещины с использованием образцов осевой стали LZ50 в форме песочных часов в условиях циклического нагружения при изгибе с вращением. Выполнены семь серий испытаний. Показано, что короткие усталостные трещины возникают в ферритных зернах или на их границах, затем они начинают расти под влиянием микроструктуры материала. Скорость роста трещин увеличивается скачкообразно, затем снижается вдвое за счет барьера, создаваемого границами ферритных зерен и полосчатой структурой перлита. Проанализированы статистическая эволюция длины доминирующей эффективной короткой усталостной трещины и доля остаточного ресурса на основании трех принципов наилучшего соответствия, включающих общий эффект соответствия, соответствие принципам физики усталости и надежность прогнозирования остаточной прочности. Установлено, что статистическое распределение минимальных величин выявляет наилучшее соответствие для длины доминирующей эффективной короткой усталостной трещины и доли остаточного ресурса. Модель роста короткой усталостной трещины, включающая различные барьеры в микроструктуре, обеспечивает хороший результат подгонки и отражает циклическое влияние микроструктуры на ее поведение. Present work is supported by the National Key R&D Program of China (2016YFB1200403), the National Natural Science Foundation of China (51675446 and U1534209), and the Opening Project of State Key Laboratory of Traction Power (grant No. 2015TPL_T13). en Інститут проблем міцності ім. Г.С. Писаренко НАН України Проблемы прочности Научно-технический раздел Short Fatigue Crack Behavior of LZ50 Axle Steel under Rotating-Bending Cyclic Loading Поведение короткой усталостной трещины осевой стали LZ50 в условиях циклического нагружения при изгибе с вращением Article published earlier |
| spellingShingle | Short Fatigue Crack Behavior of LZ50 Axle Steel under Rotating-Bending Cyclic Loading Yang, B. Dai, S. Wu, Y.Y. Liao, Z. Liang, S. Xiao, S.N. Научно-технический раздел |
| title | Short Fatigue Crack Behavior of LZ50 Axle Steel under Rotating-Bending Cyclic Loading |
| title_alt | Поведение короткой усталостной трещины осевой стали LZ50 в условиях циклического нагружения при изгибе с вращением |
| title_full | Short Fatigue Crack Behavior of LZ50 Axle Steel under Rotating-Bending Cyclic Loading |
| title_fullStr | Short Fatigue Crack Behavior of LZ50 Axle Steel under Rotating-Bending Cyclic Loading |
| title_full_unstemmed | Short Fatigue Crack Behavior of LZ50 Axle Steel under Rotating-Bending Cyclic Loading |
| title_short | Short Fatigue Crack Behavior of LZ50 Axle Steel under Rotating-Bending Cyclic Loading |
| title_sort | short fatigue crack behavior of lz50 axle steel under rotating-bending cyclic loading |
| topic | Научно-технический раздел |
| topic_facet | Научно-технический раздел |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/173831 |
| work_keys_str_mv | AT yangb shortfatiguecrackbehavioroflz50axlesteelunderrotatingbendingcyclicloading AT dais shortfatiguecrackbehavioroflz50axlesteelunderrotatingbendingcyclicloading AT wuyy shortfatiguecrackbehavioroflz50axlesteelunderrotatingbendingcyclicloading AT liaoz shortfatiguecrackbehavioroflz50axlesteelunderrotatingbendingcyclicloading AT liangs shortfatiguecrackbehavioroflz50axlesteelunderrotatingbendingcyclicloading AT xiaosn shortfatiguecrackbehavioroflz50axlesteelunderrotatingbendingcyclicloading AT yangb povedeniekorotkoiustalostnoitreŝinyosevoistalilz50vusloviâhcikličeskogonagruženiâpriizgibesvraŝeniem AT dais povedeniekorotkoiustalostnoitreŝinyosevoistalilz50vusloviâhcikličeskogonagruženiâpriizgibesvraŝeniem AT wuyy povedeniekorotkoiustalostnoitreŝinyosevoistalilz50vusloviâhcikličeskogonagruženiâpriizgibesvraŝeniem AT liaoz povedeniekorotkoiustalostnoitreŝinyosevoistalilz50vusloviâhcikličeskogonagruženiâpriizgibesvraŝeniem AT liangs povedeniekorotkoiustalostnoitreŝinyosevoistalilz50vusloviâhcikličeskogonagruženiâpriizgibesvraŝeniem AT xiaosn povedeniekorotkoiustalostnoitreŝinyosevoistalilz50vusloviâhcikličeskogonagruženiâpriizgibesvraŝeniem |