Study on a Cracked Single-Layer 2D Woven Composite Plate: Fracture Mode and Damage Analysis
An experimental study and numerical calculation are conducted to investigate the crack propagation in a 2D woven composite. Crack propagation tests of single-layer composite plate specimens permit this process to be directly followed. Analysis of their fracture surfaces reveals crack propagation pat...
Gespeichert in:
| Veröffentlicht in: | Проблемы прочности |
|---|---|
| Datum: | 2018 |
| Hauptverfasser: | , , , , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2018
|
| Schlagworte: | |
| Online Zugang: | https://nasplib.isofts.kiev.ua/handle/123456789/173999 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Study on a Cracked Single-Layer 2D Woven Composite Plate: Fracture Mode and Damage Analysis / Y.Q. Wang, P. Cheng, X.S. Liu, Y.J. Bao, H. Gao // Проблемы прочности. — 2018. — № 5. — С. 127-134. — Бібліогр.: 20 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| id |
nasplib_isofts_kiev_ua-123456789-173999 |
|---|---|
| record_format |
dspace |
| spelling |
Wang, Y.Q. Cheng, P. Liu, X.S. Bao, Y.J. Gao, H. 2020-12-28T19:05:18Z 2020-12-28T19:05:18Z 2018 Study on a Cracked Single-Layer 2D Woven Composite Plate: Fracture Mode and Damage Analysis / Y.Q. Wang, P. Cheng, X.S. Liu, Y.J. Bao, H. Gao // Проблемы прочности. — 2018. — № 5. — С. 127-134. — Бібліогр.: 20 назв. — англ. 0556-171X https://nasplib.isofts.kiev.ua/handle/123456789/173999 539.4 An experimental study and numerical calculation are conducted to investigate the crack propagation in a 2D woven composite. Crack propagation tests of single-layer composite plate specimens permit this process to be directly followed. Analysis of their fracture surfaces reveals crack propagation paths, fracture mode, and damage mechanisms. The load–deflection curve represents the crack propagation as a three-stage process. The stress intensity near the crack tip is evaluated with the critical stress intensity factor numerically calculated. The results demonstrate a good agreement between the calculations and experiment. Проведены экспериментальные исследования и численные расчеты для изучения распространения трещин плоского тканого композита. Благодаря испытанию на распространение трещин в однослойной композитной пластине можно непосредственно наблюдать процесс распространения трещин. Анализ поверхностей разрушенных образцов позволяет установить траекторию распространения трещин, характер разрушения и механизмы повреждения. Согласно кривой нагрузка–перемещение, процесс распространения трещин разделяется на три стадии. Для исследования интенсивности напряжений в вершине трещины образцов определяется критический коэффициент интенсивности напряжений путем численных расчетов. Полученные результаты демонстрируют хорошее соответствие расчетных данных с экспериментальными. This work was supported by the National Natural Science Foundation of China (Grant No. 51605076, Grant No. 51375068, and Grant No. 51475073), the National Key Basic Research Program of China (Grant No. 2014CB046504), and the Liaoning Province Natural Science Foundation of China (Grant No. 201602171). en Інститут проблем міцності ім. Г.С. Писаренко НАН України Проблемы прочности Научно-технический раздел Study on a Cracked Single-Layer 2D Woven Composite Plate: Fracture Mode and Damage Analysis Исследование однослойной пластины из плоского тканого композита с трещинами: характер разрушения и анализ повреждений Article published earlier |
| institution |
Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| collection |
DSpace DC |
| title |
Study on a Cracked Single-Layer 2D Woven Composite Plate: Fracture Mode and Damage Analysis |
| spellingShingle |
Study on a Cracked Single-Layer 2D Woven Composite Plate: Fracture Mode and Damage Analysis Wang, Y.Q. Cheng, P. Liu, X.S. Bao, Y.J. Gao, H. Научно-технический раздел |
| title_short |
Study on a Cracked Single-Layer 2D Woven Composite Plate: Fracture Mode and Damage Analysis |
| title_full |
Study on a Cracked Single-Layer 2D Woven Composite Plate: Fracture Mode and Damage Analysis |
| title_fullStr |
Study on a Cracked Single-Layer 2D Woven Composite Plate: Fracture Mode and Damage Analysis |
| title_full_unstemmed |
Study on a Cracked Single-Layer 2D Woven Composite Plate: Fracture Mode and Damage Analysis |
| title_sort |
study on a cracked single-layer 2d woven composite plate: fracture mode and damage analysis |
| author |
Wang, Y.Q. Cheng, P. Liu, X.S. Bao, Y.J. Gao, H. |
| author_facet |
Wang, Y.Q. Cheng, P. Liu, X.S. Bao, Y.J. Gao, H. |
| topic |
Научно-технический раздел |
| topic_facet |
Научно-технический раздел |
| publishDate |
2018 |
| language |
English |
| container_title |
Проблемы прочности |
| publisher |
Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| format |
Article |
| title_alt |
Исследование однослойной пластины из плоского тканого композита с трещинами: характер разрушения и анализ повреждений |
| description |
An experimental study and numerical calculation are conducted to investigate the crack propagation in a 2D woven composite. Crack propagation tests of single-layer composite plate specimens permit this process to be directly followed. Analysis of their fracture surfaces reveals crack propagation paths, fracture mode, and damage mechanisms. The load–deflection curve represents the crack propagation as a three-stage process. The stress intensity near the crack tip is evaluated with the critical stress intensity factor numerically calculated. The results demonstrate a good agreement between the calculations and experiment.
Проведены экспериментальные исследования и численные расчеты для изучения распространения трещин плоского тканого композита. Благодаря испытанию на распространение трещин в однослойной композитной пластине можно непосредственно наблюдать процесс распространения трещин. Анализ поверхностей разрушенных образцов позволяет установить траекторию распространения трещин, характер разрушения и механизмы повреждения. Согласно кривой нагрузка–перемещение, процесс распространения трещин разделяется на три стадии. Для исследования интенсивности напряжений в вершине трещины образцов определяется критический коэффициент интенсивности напряжений путем численных расчетов. Полученные результаты демонстрируют хорошее соответствие расчетных данных с экспериментальными.
|
| issn |
0556-171X |
| url |
https://nasplib.isofts.kiev.ua/handle/123456789/173999 |
| citation_txt |
Study on a Cracked Single-Layer 2D Woven Composite Plate: Fracture Mode and Damage Analysis / Y.Q. Wang, P. Cheng, X.S. Liu, Y.J. Bao, H. Gao // Проблемы прочности. — 2018. — № 5. — С. 127-134. — Бібліогр.: 20 назв. — англ. |
| work_keys_str_mv |
AT wangyq studyonacrackedsinglelayer2dwovencompositeplatefracturemodeanddamageanalysis AT chengp studyonacrackedsinglelayer2dwovencompositeplatefracturemodeanddamageanalysis AT liuxs studyonacrackedsinglelayer2dwovencompositeplatefracturemodeanddamageanalysis AT baoyj studyonacrackedsinglelayer2dwovencompositeplatefracturemodeanddamageanalysis AT gaoh studyonacrackedsinglelayer2dwovencompositeplatefracturemodeanddamageanalysis AT wangyq issledovanieodnosloinoiplastinyizploskogotkanogokompozitastreŝinamiharakterrazrušeniâianalizpovreždenii AT chengp issledovanieodnosloinoiplastinyizploskogotkanogokompozitastreŝinamiharakterrazrušeniâianalizpovreždenii AT liuxs issledovanieodnosloinoiplastinyizploskogotkanogokompozitastreŝinamiharakterrazrušeniâianalizpovreždenii AT baoyj issledovanieodnosloinoiplastinyizploskogotkanogokompozitastreŝinamiharakterrazrušeniâianalizpovreždenii AT gaoh issledovanieodnosloinoiplastinyizploskogotkanogokompozitastreŝinamiharakterrazrušeniâianalizpovreždenii |
| first_indexed |
2025-12-07T17:06:14Z |
| last_indexed |
2025-12-07T17:06:14Z |
| _version_ |
1850869991768850432 |