The low-temperature specific heat of MWCNTs

• Дата: 2019
• Автори: Sumarokov, V.V., Jeżowski, A., Szewczyk, D., Bagatski, M.I., Barabashko, M.S., Ponomarev, A.N., Kuznetsov, V.L., Moseenkov, S.I.
• Формат: Стаття
• Мова: English
• Опубліковано: Фізико-технічний інститут низьких температур ім. Б.І. Вєркіна НАН України 2019
• Назва видання: Физика низких температур
• Теми: Спеціальний випуск. “Proceedings of 12th International Conference on Cryocrystals and Quantum Crystals (CC-2018)” (Wrocław, Poland, August 26–31, 2018)
• Онлайн доступ: https://nasplib.isofts.kiev.ua/handle/123456789/176086
• Назва журналу: Digital Library of Periodicals of National Academy of Sciences of Ukraine
• Цитувати: The low-temperature specific heat of MWCNTs / V.V. Sumarokov, A. Jeżowski, D. Szewczyk, M.I. Bagatski, M.S. Barabashko, A.N. Ponomarev, V.L. Kuznetsov, S.I. Moseenkov // Физика низких температур. — 2019. — Т. 45, № 3. — С. 395-403. — Бібліогр.: 55 назв. — англ.

The specific heat of multi-walled carbon nanotubes (MWCNTs) with a low defectiveness and with a low content of inorganic impurities has been measured in the temperature range from 1.8 to 275 K by the thermal relaxation method. The elemental composition and morphology of the MWCNTs were determined using scanning electron microscopy analysis and energy dispersion x-ray spectroscopy. The MWCNTs were prepared by chemical catalytic vapor deposition and have mean diameters from 7 nm up to 18 nm and lengths in some tens of microns. MWCNTs purity is over 99.4 at.%. The mass of the samples ranged from 2–4 mg. It was found that the temperature dependence of the specific heat of the MWCNTs differs significantly from other carbon materials (graphene, bundles of SWCNTs, graphite, diamond) at low temperatures. The specific heat of MWCNTs systematically decreases with increasing diameter of the tubes at low temperatures. The character of the temperature dependence of the specific heat of the MWCNTs with different diameters demonstrates the manifestation of different dimensions from 1D to 3D, depending on the temperature regions. The crossover temperatures are about 6 and 40 K. In the vicinity of these temperatures, a hysteresis is observed.