Damaging of pure tungsten with different microstructure under sequential QSPA and LHD plasma loads

Damaging of pure tungsten with different microstructure under sequential QSPA and LHD plasma loads

The cracking thresholds were evaluated for tungsten samples with different microstructure in the course of QSPA Kh – 50 repetitive plasma loads. No damage has been observed on the exposed surfaces under 0.1 MJ/m². Nevertheless, cracks were detected in the bulk of irradiated tungsten (with longitudin...

Full description

Saved in:
Bibliographic Details
Published in:Вопросы атомной науки и техники
Date:2020
Main Authors: Herashchenko, S.S., Byrka, O.V., Makhlaj, V.A., Wirtz, M., Aksenov, N.N., Garkusha, I.E., Petrov, Yu.V., Malykhin, S.V., Surovitskiy, S.V., Masuzaki, S., Tokitani, M., Lebedev, S.I., Shevchuk, P.B.
Format: Article
Language:English
Published: Національний науковий центр «Харківський фізико-технічний інститут» НАН України 2020
Subjects:
Plasma dynamics and plasma-wall interaction
Online Access:https://nasplib.isofts.kiev.ua/handle/123456789/194648
Tags: Add Tag
No Tags, Be the first to tag this record!
Journal Title:Digital Library of Periodicals of National Academy of Sciences of Ukraine
Cite this:Damaging of pure tungsten with different microstructure under sequential QSPA and LHD plasma loads / S.S. Herashchenko, O.V. Byrka, V.A. Makhlaj, M. Wirtz, N.N. Aksenov, I.E. Garkusha, Yu.V. Petrov, S.V. Malykhin, S.V. Surovitskiy, S. Masuzaki, M. Tokitani, S.I. Lebedev, P.B. Shevchuk // Problems of atomic science and tecnology. — 2020. — № 6. — С. 78-82. — Бібліогр.: 17 назв. — англ.

Institution

Digital Library of Periodicals of National Academy of Sciences of Ukraine
id nasplib_isofts_kiev_ua-123456789-194648
record_format dspace
spelling Herashchenko, S.S.
Byrka, O.V.
Makhlaj, V.A.
Wirtz, M.
Aksenov, N.N.
Garkusha, I.E.
Petrov, Yu.V.
Malykhin, S.V.
Surovitskiy, S.V.
Masuzaki, S.
Tokitani, M.
Lebedev, S.I.
Shevchuk, P.B.
2023-11-28T10:42:59Z
2023-11-28T10:42:59Z
2020
Damaging of pure tungsten with different microstructure under sequential QSPA and LHD plasma loads / S.S. Herashchenko, O.V. Byrka, V.A. Makhlaj, M. Wirtz, N.N. Aksenov, I.E. Garkusha, Yu.V. Petrov, S.V. Malykhin, S.V. Surovitskiy, S. Masuzaki, M. Tokitani, S.I. Lebedev, P.B. Shevchuk // Problems of atomic science and tecnology. — 2020. — № 6. — С. 78-82. — Бібліогр.: 17 назв. — англ.
1562-6016
PACS: 52.40.Hf
https://nasplib.isofts.kiev.ua/handle/123456789/194648
The cracking thresholds were evaluated for tungsten samples with different microstructure in the course of QSPA Kh – 50 repetitive plasma loads. No damage has been observed on the exposed surfaces under 0.1 MJ/m². Nevertheless, cracks were detected in the bulk of irradiated tungsten (with longitudinal grain orientation). Increasing heat load up to 0.2 MJ/m² caused the damaging of all types of tungsten targets. The observed cracks propagate to the bulk mainly transversely and parallel to the irradiated surface. The effect of the subsequent exposure with LHD divertor plasma on the tungsten samples was analyzed. The obtained results are discussed.
Було оцінено пороги розтріскування для зразків вольфраму з різною мікроструктурою в процесі повторюваних плазмових навантажень КСПП Х–50. При навантаженнях менше 0,1 МДж/м², на відкритих поверхнях зразків вольфраму ушкоджень не спостерігається. Проте, тріщини спостерігаються в обсязі опроміненого зразка вольфраму з поздовжньою орієнтацією зерен. Підвищення теплового навантаження до 0,2 МДж/м² призводить до пошкодження всіх типів вольфрамових мішеней. Тріщини поширюються в обсязі в основному поперечно і паралельно до опромінюваної поверхні. Проаналізовано вплив діверторної плазми LHD на поверхню зразків вольфраму. Порівнюються результати впливу на зразки вольфраму з різною мікроструктурою.
Были оценены пороги растрескивания для образцов вольфрама с различной микроструктурой в процессе повторяющихся плазменных нагрузок КСПУ Х–50. При нагрузках менее 0,1 МДж/м² на открытых поверхностях образцов вольфрама повреждений не наблюдается. Тем не менее трещины наблюдаются в объеме облученного образца вольфрама с продольной ориентацией зерен. Повышение тепловой нагрузки до 0,2 МДж/м² приводит к повреждению всех типов вольфрамовых мишеней. Наблюдаемые трещины распространяются в объеме в основном поперечно и параллельно облучаемой поверхности. Проанализировано влияние диверторной плазмы LHD на поверхность образцов вольфрама. Сравниваются результаты воздействия на образцы вольфрама с различной микроструктурой.
This work has been carried out within the framework of the EUROfusion Consortium and has received funding from the Euratom research and training programme 2014-2018 and 2019-2020 under grant agreement № 633053. The views and opinions expressed herein do not necessarily reflect those of the European Commission. This work has also been supported by National Academy Science of Ukraine projects Х-2-11-10/2020 and П-2/24-2020.
en
Національний науковий центр «Харківський фізико-технічний інститут» НАН України
Вопросы атомной науки и техники
Plasma dynamics and plasma-wall interaction
Damaging of pure tungsten with different microstructure under sequential QSPA and LHD plasma loads
Пошкодження чистого вольфраму з різною мікроструктурою при послідовних плазмових навантаженнях у КСПП і LHD
Повреждения чистого вольфрама с разной микроструктурой при последовательных плазменных нагрузках в КСПУ и LHD
Article
published earlier
institution Digital Library of Periodicals of National Academy of Sciences of Ukraine
collection DSpace DC
title Damaging of pure tungsten with different microstructure under sequential QSPA and LHD plasma loads
spellingShingle Damaging of pure tungsten with different microstructure under sequential QSPA and LHD plasma loads
Herashchenko, S.S.
Byrka, O.V.
Makhlaj, V.A.
Wirtz, M.
Aksenov, N.N.
Garkusha, I.E.
Petrov, Yu.V.
Malykhin, S.V.
Surovitskiy, S.V.
Masuzaki, S.
Tokitani, M.
Lebedev, S.I.
Shevchuk, P.B.
Plasma dynamics and plasma-wall interaction
title_short Damaging of pure tungsten with different microstructure under sequential QSPA and LHD plasma loads
title_full Damaging of pure tungsten with different microstructure under sequential QSPA and LHD plasma loads
title_fullStr Damaging of pure tungsten with different microstructure under sequential QSPA and LHD plasma loads
title_full_unstemmed Damaging of pure tungsten with different microstructure under sequential QSPA and LHD plasma loads
title_sort damaging of pure tungsten with different microstructure under sequential qspa and lhd plasma loads
author Herashchenko, S.S.
Byrka, O.V.
Makhlaj, V.A.
Wirtz, M.
Aksenov, N.N.
Garkusha, I.E.
Petrov, Yu.V.
Malykhin, S.V.
Surovitskiy, S.V.
Masuzaki, S.
Tokitani, M.
Lebedev, S.I.
Shevchuk, P.B.
author_facet Herashchenko, S.S.
Byrka, O.V.
Makhlaj, V.A.
Wirtz, M.
Aksenov, N.N.
Garkusha, I.E.
Petrov, Yu.V.
Malykhin, S.V.
Surovitskiy, S.V.
Masuzaki, S.
Tokitani, M.
Lebedev, S.I.
Shevchuk, P.B.
topic Plasma dynamics and plasma-wall interaction
topic_facet Plasma dynamics and plasma-wall interaction
publishDate 2020
language English
container_title Вопросы атомной науки и техники
publisher Національний науковий центр «Харківський фізико-технічний інститут» НАН України
format Article
title_alt Пошкодження чистого вольфраму з різною мікроструктурою при послідовних плазмових навантаженнях у КСПП і LHD
Повреждения чистого вольфрама с разной микроструктурой при последовательных плазменных нагрузках в КСПУ и LHD
description The cracking thresholds were evaluated for tungsten samples with different microstructure in the course of QSPA Kh – 50 repetitive plasma loads. No damage has been observed on the exposed surfaces under 0.1 MJ/m². Nevertheless, cracks were detected in the bulk of irradiated tungsten (with longitudinal grain orientation). Increasing heat load up to 0.2 MJ/m² caused the damaging of all types of tungsten targets. The observed cracks propagate to the bulk mainly transversely and parallel to the irradiated surface. The effect of the subsequent exposure with LHD divertor plasma on the tungsten samples was analyzed. The obtained results are discussed. Було оцінено пороги розтріскування для зразків вольфраму з різною мікроструктурою в процесі повторюваних плазмових навантажень КСПП Х–50. При навантаженнях менше 0,1 МДж/м², на відкритих поверхнях зразків вольфраму ушкоджень не спостерігається. Проте, тріщини спостерігаються в обсязі опроміненого зразка вольфраму з поздовжньою орієнтацією зерен. Підвищення теплового навантаження до 0,2 МДж/м² призводить до пошкодження всіх типів вольфрамових мішеней. Тріщини поширюються в обсязі в основному поперечно і паралельно до опромінюваної поверхні. Проаналізовано вплив діверторної плазми LHD на поверхню зразків вольфраму. Порівнюються результати впливу на зразки вольфраму з різною мікроструктурою. Были оценены пороги растрескивания для образцов вольфрама с различной микроструктурой в процессе повторяющихся плазменных нагрузок КСПУ Х–50. При нагрузках менее 0,1 МДж/м² на открытых поверхностях образцов вольфрама повреждений не наблюдается. Тем не менее трещины наблюдаются в объеме облученного образца вольфрама с продольной ориентацией зерен. Повышение тепловой нагрузки до 0,2 МДж/м² приводит к повреждению всех типов вольфрамовых мишеней. Наблюдаемые трещины распространяются в объеме в основном поперечно и параллельно облучаемой поверхности. Проанализировано влияние диверторной плазмы LHD на поверхность образцов вольфрама. Сравниваются результаты воздействия на образцы вольфрама с различной микроструктурой.
issn 1562-6016
url https://nasplib.isofts.kiev.ua/handle/123456789/194648
citation_txt Damaging of pure tungsten with different microstructure under sequential QSPA and LHD plasma loads / S.S. Herashchenko, O.V. Byrka, V.A. Makhlaj, M. Wirtz, N.N. Aksenov, I.E. Garkusha, Yu.V. Petrov, S.V. Malykhin, S.V. Surovitskiy, S. Masuzaki, M. Tokitani, S.I. Lebedev, P.B. Shevchuk // Problems of atomic science and tecnology. — 2020. — № 6. — С. 78-82. — Бібліогр.: 17 назв. — англ.
work_keys_str_mv AT herashchenkoss damagingofpuretungstenwithdifferentmicrostructureundersequentialqspaandlhdplasmaloads
AT byrkaov damagingofpuretungstenwithdifferentmicrostructureundersequentialqspaandlhdplasmaloads
AT makhlajva damagingofpuretungstenwithdifferentmicrostructureundersequentialqspaandlhdplasmaloads
AT wirtzm damagingofpuretungstenwithdifferentmicrostructureundersequentialqspaandlhdplasmaloads
AT aksenovnn damagingofpuretungstenwithdifferentmicrostructureundersequentialqspaandlhdplasmaloads
AT garkushaie damagingofpuretungstenwithdifferentmicrostructureundersequentialqspaandlhdplasmaloads
AT petrovyuv damagingofpuretungstenwithdifferentmicrostructureundersequentialqspaandlhdplasmaloads
AT malykhinsv damagingofpuretungstenwithdifferentmicrostructureundersequentialqspaandlhdplasmaloads
AT surovitskiysv damagingofpuretungstenwithdifferentmicrostructureundersequentialqspaandlhdplasmaloads
AT masuzakis damagingofpuretungstenwithdifferentmicrostructureundersequentialqspaandlhdplasmaloads
AT tokitanim damagingofpuretungstenwithdifferentmicrostructureundersequentialqspaandlhdplasmaloads
AT lebedevsi damagingofpuretungstenwithdifferentmicrostructureundersequentialqspaandlhdplasmaloads
AT shevchukpb damagingofpuretungstenwithdifferentmicrostructureundersequentialqspaandlhdplasmaloads
AT herashchenkoss poškodžennâčistogovolʹframuzríznoûmíkrostrukturoûpriposlídovnihplazmovihnavantažennâhuksppílhd
AT byrkaov poškodžennâčistogovolʹframuzríznoûmíkrostrukturoûpriposlídovnihplazmovihnavantažennâhuksppílhd
AT makhlajva poškodžennâčistogovolʹframuzríznoûmíkrostrukturoûpriposlídovnihplazmovihnavantažennâhuksppílhd
AT wirtzm poškodžennâčistogovolʹframuzríznoûmíkrostrukturoûpriposlídovnihplazmovihnavantažennâhuksppílhd
AT aksenovnn poškodžennâčistogovolʹframuzríznoûmíkrostrukturoûpriposlídovnihplazmovihnavantažennâhuksppílhd
AT garkushaie poškodžennâčistogovolʹframuzríznoûmíkrostrukturoûpriposlídovnihplazmovihnavantažennâhuksppílhd
AT petrovyuv poškodžennâčistogovolʹframuzríznoûmíkrostrukturoûpriposlídovnihplazmovihnavantažennâhuksppílhd
AT malykhinsv poškodžennâčistogovolʹframuzríznoûmíkrostrukturoûpriposlídovnihplazmovihnavantažennâhuksppílhd
AT surovitskiysv poškodžennâčistogovolʹframuzríznoûmíkrostrukturoûpriposlídovnihplazmovihnavantažennâhuksppílhd
AT masuzakis poškodžennâčistogovolʹframuzríznoûmíkrostrukturoûpriposlídovnihplazmovihnavantažennâhuksppílhd
AT tokitanim poškodžennâčistogovolʹframuzríznoûmíkrostrukturoûpriposlídovnihplazmovihnavantažennâhuksppílhd
AT lebedevsi poškodžennâčistogovolʹframuzríznoûmíkrostrukturoûpriposlídovnihplazmovihnavantažennâhuksppílhd
AT shevchukpb poškodžennâčistogovolʹframuzríznoûmíkrostrukturoûpriposlídovnihplazmovihnavantažennâhuksppílhd
AT herashchenkoss povreždeniâčistogovolʹframasraznoimikrostrukturoipriposledovatelʹnyhplazmennyhnagruzkahvkspuilhd
AT byrkaov povreždeniâčistogovolʹframasraznoimikrostrukturoipriposledovatelʹnyhplazmennyhnagruzkahvkspuilhd
AT makhlajva povreždeniâčistogovolʹframasraznoimikrostrukturoipriposledovatelʹnyhplazmennyhnagruzkahvkspuilhd
AT wirtzm povreždeniâčistogovolʹframasraznoimikrostrukturoipriposledovatelʹnyhplazmennyhnagruzkahvkspuilhd
AT aksenovnn povreždeniâčistogovolʹframasraznoimikrostrukturoipriposledovatelʹnyhplazmennyhnagruzkahvkspuilhd
AT garkushaie povreždeniâčistogovolʹframasraznoimikrostrukturoipriposledovatelʹnyhplazmennyhnagruzkahvkspuilhd
AT petrovyuv povreždeniâčistogovolʹframasraznoimikrostrukturoipriposledovatelʹnyhplazmennyhnagruzkahvkspuilhd
AT malykhinsv povreždeniâčistogovolʹframasraznoimikrostrukturoipriposledovatelʹnyhplazmennyhnagruzkahvkspuilhd
AT surovitskiysv povreždeniâčistogovolʹframasraznoimikrostrukturoipriposledovatelʹnyhplazmennyhnagruzkahvkspuilhd
AT masuzakis povreždeniâčistogovolʹframasraznoimikrostrukturoipriposledovatelʹnyhplazmennyhnagruzkahvkspuilhd
AT tokitanim povreždeniâčistogovolʹframasraznoimikrostrukturoipriposledovatelʹnyhplazmennyhnagruzkahvkspuilhd
AT lebedevsi povreždeniâčistogovolʹframasraznoimikrostrukturoipriposledovatelʹnyhplazmennyhnagruzkahvkspuilhd
AT shevchukpb povreždeniâčistogovolʹframasraznoimikrostrukturoipriposledovatelʹnyhplazmennyhnagruzkahvkspuilhd
first_indexed 2025-12-01T15:02:45Z
last_indexed 2025-12-01T15:02:45Z
_version_ 1850860525671415808

Similar Items