Strengthening of the surface of steel (9XФМ) exposed to a high-current electron beam
9ХФМ steel was irradiated with a high-current electron beam. The high-current electron beam was obtained in the TEMP-A accelerator. The irradiation was performed for various samples of the material of a ball mill drum. Part of the samples were taken from the surface of the balls, which had different...
Gespeichert in:
| Veröffentlicht in: | Вопросы атомной науки и техники |
|---|---|
| Datum: | 2020 |
| Hauptverfasser: | , , , , , , , , , , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Національний науковий центр «Харківський фізико-технічний інститут» НАН України
2020
|
| Schlagworte: | |
| Online Zugang: | https://nasplib.isofts.kiev.ua/handle/123456789/194752 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Strengthening of the surface of steel (9XФМ) exposed to a high-current electron beam / E.M. Prokhorenko, V.V. Lytvynenko, O.А. Melyakovа, Yu.F. Lonin, A.G. Ponomarev, V.T. Uvarov, N.A. Shul’gin, T.G. Prokhorenko, R.I. Starovoytov, A.I. Morozov, S.R. Artemev // Problems of atomic science and tecnology. — 2020. — № 1. — С. 167-172. — Бібліогр.: 16 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| id |
nasplib_isofts_kiev_ua-123456789-194752 |
|---|---|
| record_format |
dspace |
| spelling |
Prokhorenko, E.M. Lytvynenko, V.V. Melyakovа, O.А. Lonin, Yu.F. Ponomarev, A.G. Uvarov, V.T. Shulgin, N.A. Prokhorenko, T.G. Starovoytov, R.I. Morozov, A.I. Artemev, S.R. 2023-11-29T14:36:23Z 2023-11-29T14:36:23Z 2020 Strengthening of the surface of steel (9XФМ) exposed to a high-current electron beam / E.M. Prokhorenko, V.V. Lytvynenko, O.А. Melyakovа, Yu.F. Lonin, A.G. Ponomarev, V.T. Uvarov, N.A. Shul’gin, T.G. Prokhorenko, R.I. Starovoytov, A.I. Morozov, S.R. Artemev // Problems of atomic science and tecnology. — 2020. — № 1. — С. 167-172. — Бібліогр.: 16 назв. — англ. 1562-6016 PACS: 87.55N, 07.05.Tp, 44.90.+c, 61.80.Fe, 81.40.Wx https://nasplib.isofts.kiev.ua/handle/123456789/194752 9ХФМ steel was irradiated with a high-current electron beam. The high-current electron beam was obtained in the TEMP-A accelerator. The irradiation was performed for various samples of the material of a ball mill drum. Part of the samples were taken from the surface of the balls, which had different degrees of wear. Samples taken from the depth of the balls, which is equal to half the diameter, were also irradiated. Microhardness measurements, metallographic, and fractographic analysis were used to study mechanical and microstructural changes. In all cases, a change in hardness was detected. The degree of change in hardness is different for different samples. Based on fractographic analysis, using SEM microscopy, one of the mechanisms that contribute to increasing the surface hardness is determined. This mechanism is the cleaning of the surface of samples from impurities of phosphorus and sulfur using a high-current electron beam. Сталь 9ХФМ була опромінена сильнострумовим електронним пучком, який отримано в прискорювачі ТЕМП-А. Опромінення проводили для різних зразків матеріалу кулі барабанного млина. Частина зразків була взята з поверхонь куль, які мали різний ступінь зносу. Також опромінювали зразки, узяті з глибини куль, яка була рівна половині діаметра. Для вивчення механічних і мікроструктурних змін застосовували виміри мікротвердості, металографічний і фрактографічний аналізи. У всіх випадках виявлена зміна твердості та пластичності. Для різних зразків ступінь зміни твердості та пластичності різна. На основі фрактогрaфічного аналізу з використанням РЕМ-мікроскопії визначений один з механізмів, який сприяє підвищенню твердості поверхні. Цим механізмом є очищення поверхні зразків за допомогою сильнострумового пучка електронів від домішок фосфору і сірки. Сталь 9ХФМ была облучена сильноточным электронным пучком, который получен в ускорителе ТЕМПА. Облучение проводили для различных образцов материала шара барабанной мельницы. Часть образцов взята с поверхности шаров, которые имели различную степень износа. Также облучали образцы, взятые из глубины шаров, которая равна половине диаметра. Для изучения механических и микроструктурных изменений применяли измерения микротвердости, металлографический и фрактографический анализы. Во всех случаях обнаружено изменение твердости. Для различных образцов степень изменения твердости различна. На основе фрактогрaфического анализа с использованием РЭМ-микроскопии определен один из механизмов, который способствует повышению твердости поверхности. Этим механизмом является очистка поверхности образцов с помощью сильноточного пучка электронов от примесей фосфора и серы. en Національний науковий центр «Харківський фізико-технічний інститут» НАН України Вопросы атомной науки и техники Physics and the technology of construction materials Strengthening of the surface of steel (9XФМ) exposed to a high-current electron beam Зміцнення поверхні сталі (9ХФМ) при дії сильнострумового електронного пучка Упрочнение поверхности стали (9ХФМ) при воздействии сильноточного электронного пучка Article published earlier |
| institution |
Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| collection |
DSpace DC |
| title |
Strengthening of the surface of steel (9XФМ) exposed to a high-current electron beam |
| spellingShingle |
Strengthening of the surface of steel (9XФМ) exposed to a high-current electron beam Prokhorenko, E.M. Lytvynenko, V.V. Melyakovа, O.А. Lonin, Yu.F. Ponomarev, A.G. Uvarov, V.T. Shulgin, N.A. Prokhorenko, T.G. Starovoytov, R.I. Morozov, A.I. Artemev, S.R. Physics and the technology of construction materials |
| title_short |
Strengthening of the surface of steel (9XФМ) exposed to a high-current electron beam |
| title_full |
Strengthening of the surface of steel (9XФМ) exposed to a high-current electron beam |
| title_fullStr |
Strengthening of the surface of steel (9XФМ) exposed to a high-current electron beam |
| title_full_unstemmed |
Strengthening of the surface of steel (9XФМ) exposed to a high-current electron beam |
| title_sort |
strengthening of the surface of steel (9xфм) exposed to a high-current electron beam |
| author |
Prokhorenko, E.M. Lytvynenko, V.V. Melyakovа, O.А. Lonin, Yu.F. Ponomarev, A.G. Uvarov, V.T. Shulgin, N.A. Prokhorenko, T.G. Starovoytov, R.I. Morozov, A.I. Artemev, S.R. |
| author_facet |
Prokhorenko, E.M. Lytvynenko, V.V. Melyakovа, O.А. Lonin, Yu.F. Ponomarev, A.G. Uvarov, V.T. Shulgin, N.A. Prokhorenko, T.G. Starovoytov, R.I. Morozov, A.I. Artemev, S.R. |
| topic |
Physics and the technology of construction materials |
| topic_facet |
Physics and the technology of construction materials |
| publishDate |
2020 |
| language |
English |
| container_title |
Вопросы атомной науки и техники |
| publisher |
Національний науковий центр «Харківський фізико-технічний інститут» НАН України |
| format |
Article |
| title_alt |
Зміцнення поверхні сталі (9ХФМ) при дії сильнострумового електронного пучка Упрочнение поверхности стали (9ХФМ) при воздействии сильноточного электронного пучка |
| description |
9ХФМ steel was irradiated with a high-current electron beam. The high-current electron beam was obtained in the TEMP-A accelerator. The irradiation was performed for various samples of the material of a ball mill drum. Part of the samples were taken from the surface of the balls, which had different degrees of wear. Samples taken from the depth of the balls, which is equal to half the diameter, were also irradiated. Microhardness measurements, metallographic, and fractographic analysis were used to study mechanical and microstructural changes. In all cases, a change in hardness was detected. The degree of change in hardness is different for different samples. Based on fractographic analysis, using SEM microscopy, one of the mechanisms that contribute to increasing the surface hardness is determined. This mechanism is the cleaning of the surface of samples from impurities of phosphorus and sulfur using a high-current electron beam.
Сталь 9ХФМ була опромінена сильнострумовим електронним пучком, який отримано в прискорювачі ТЕМП-А. Опромінення проводили для різних зразків матеріалу кулі барабанного млина. Частина зразків була взята з поверхонь куль, які мали різний ступінь зносу. Також опромінювали зразки, узяті з глибини куль, яка була рівна половині діаметра. Для вивчення механічних і мікроструктурних змін застосовували виміри мікротвердості, металографічний і фрактографічний аналізи. У всіх випадках виявлена зміна твердості та пластичності. Для різних зразків ступінь зміни твердості та пластичності різна. На основі фрактогрaфічного аналізу з використанням РЕМ-мікроскопії визначений один з механізмів, який сприяє підвищенню твердості поверхні. Цим механізмом є очищення поверхні зразків за допомогою сильнострумового пучка електронів від домішок фосфору і сірки.
Сталь 9ХФМ была облучена сильноточным электронным пучком, который получен в ускорителе ТЕМПА. Облучение проводили для различных образцов материала шара барабанной мельницы. Часть образцов взята с поверхности шаров, которые имели различную степень износа. Также облучали образцы, взятые из глубины шаров, которая равна половине диаметра. Для изучения механических и микроструктурных изменений применяли измерения микротвердости, металлографический и фрактографический анализы. Во всех случаях обнаружено изменение твердости. Для различных образцов степень изменения твердости различна. На основе фрактогрaфического анализа с использованием РЭМ-микроскопии определен один из механизмов, который способствует повышению твердости поверхности. Этим механизмом является очистка поверхности образцов с помощью сильноточного пучка электронов от примесей фосфора и серы.
|
| issn |
1562-6016 |
| url |
https://nasplib.isofts.kiev.ua/handle/123456789/194752 |
| citation_txt |
Strengthening of the surface of steel (9XФМ) exposed to a high-current electron beam / E.M. Prokhorenko, V.V. Lytvynenko, O.А. Melyakovа, Yu.F. Lonin, A.G. Ponomarev, V.T. Uvarov, N.A. Shul’gin, T.G. Prokhorenko, R.I. Starovoytov, A.I. Morozov, S.R. Artemev // Problems of atomic science and tecnology. — 2020. — № 1. — С. 167-172. — Бібліогр.: 16 назв. — англ. |
| work_keys_str_mv |
AT prokhorenkoem strengtheningofthesurfaceofsteel9xfmexposedtoahighcurrentelectronbeam AT lytvynenkovv strengtheningofthesurfaceofsteel9xfmexposedtoahighcurrentelectronbeam AT melyakovaoa strengtheningofthesurfaceofsteel9xfmexposedtoahighcurrentelectronbeam AT loninyuf strengtheningofthesurfaceofsteel9xfmexposedtoahighcurrentelectronbeam AT ponomarevag strengtheningofthesurfaceofsteel9xfmexposedtoahighcurrentelectronbeam AT uvarovvt strengtheningofthesurfaceofsteel9xfmexposedtoahighcurrentelectronbeam AT shulginna strengtheningofthesurfaceofsteel9xfmexposedtoahighcurrentelectronbeam AT prokhorenkotg strengtheningofthesurfaceofsteel9xfmexposedtoahighcurrentelectronbeam AT starovoytovri strengtheningofthesurfaceofsteel9xfmexposedtoahighcurrentelectronbeam AT morozovai strengtheningofthesurfaceofsteel9xfmexposedtoahighcurrentelectronbeam AT artemevsr strengtheningofthesurfaceofsteel9xfmexposedtoahighcurrentelectronbeam AT prokhorenkoem zmícnennâpoverhnístalí9hfmpridíísilʹnostrumovogoelektronnogopučka AT lytvynenkovv zmícnennâpoverhnístalí9hfmpridíísilʹnostrumovogoelektronnogopučka AT melyakovaoa zmícnennâpoverhnístalí9hfmpridíísilʹnostrumovogoelektronnogopučka AT loninyuf zmícnennâpoverhnístalí9hfmpridíísilʹnostrumovogoelektronnogopučka AT ponomarevag zmícnennâpoverhnístalí9hfmpridíísilʹnostrumovogoelektronnogopučka AT uvarovvt zmícnennâpoverhnístalí9hfmpridíísilʹnostrumovogoelektronnogopučka AT shulginna zmícnennâpoverhnístalí9hfmpridíísilʹnostrumovogoelektronnogopučka AT prokhorenkotg zmícnennâpoverhnístalí9hfmpridíísilʹnostrumovogoelektronnogopučka AT starovoytovri zmícnennâpoverhnístalí9hfmpridíísilʹnostrumovogoelektronnogopučka AT morozovai zmícnennâpoverhnístalí9hfmpridíísilʹnostrumovogoelektronnogopučka AT artemevsr zmícnennâpoverhnístalí9hfmpridíísilʹnostrumovogoelektronnogopučka AT prokhorenkoem upročneniepoverhnostistali9hfmprivozdeistviisilʹnotočnogoélektronnogopučka AT lytvynenkovv upročneniepoverhnostistali9hfmprivozdeistviisilʹnotočnogoélektronnogopučka AT melyakovaoa upročneniepoverhnostistali9hfmprivozdeistviisilʹnotočnogoélektronnogopučka AT loninyuf upročneniepoverhnostistali9hfmprivozdeistviisilʹnotočnogoélektronnogopučka AT ponomarevag upročneniepoverhnostistali9hfmprivozdeistviisilʹnotočnogoélektronnogopučka AT uvarovvt upročneniepoverhnostistali9hfmprivozdeistviisilʹnotočnogoélektronnogopučka AT shulginna upročneniepoverhnostistali9hfmprivozdeistviisilʹnotočnogoélektronnogopučka AT prokhorenkotg upročneniepoverhnostistali9hfmprivozdeistviisilʹnotočnogoélektronnogopučka AT starovoytovri upročneniepoverhnostistali9hfmprivozdeistviisilʹnotočnogoélektronnogopučka AT morozovai upročneniepoverhnostistali9hfmprivozdeistviisilʹnotočnogoélektronnogopučka AT artemevsr upročneniepoverhnostistali9hfmprivozdeistviisilʹnotočnogoélektronnogopučka |
| first_indexed |
2025-12-07T16:11:02Z |
| last_indexed |
2025-12-07T16:11:02Z |
| _version_ |
1850866519269965824 |