Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States
Premature fracture of steam pipelines from 14MoV6 3 steel designed for 1000,000 h service life at 540°C has been studied. Test specimens are manufactured from steel in the initial state and after 117 h of operation. Application of the local approach to fracture and the metallographic analysis,...
Збережено в:
| Опубліковано в: : | Проблемы прочности |
|---|---|
| Дата: | 2004 |
| Автори: | , , |
| Формат: | Стаття |
| Мова: | English |
| Опубліковано: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2004
|
| Теми: | |
| Онлайн доступ: | https://nasplib.isofts.kiev.ua/handle/123456789/47064 |
| Теги: |
Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Цитувати: | Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States / M. Zrilic, Z. Burzic, Z. Cvijovic // Проблемы прочности. — 2004. — № 1. — С. 68-83. — Бібліогр.: 12 назв. — англ. |
Репозитарії
Digital Library of Periodicals of National Academy of Sciences of Ukraine| id |
nasplib_isofts_kiev_ua-123456789-47064 |
|---|---|
| record_format |
dspace |
| spelling |
Zrilic, M. Burzic, Z. Cvijovic, Z. 2013-07-09T15:52:29Z 2013-07-09T15:52:29Z 2004 Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States / M. Zrilic, Z. Burzic, Z. Cvijovic // Проблемы прочности. — 2004. — № 1. — С. 68-83. — Бібліогр.: 12 назв. — англ. 0556-171X https://nasplib.isofts.kiev.ua/handle/123456789/47064 539.4 Premature fracture of steam pipelines from 14MoV6 3 steel designed for 1000,000 h service life at 540°C has been studied. Test specimens are manufactured from steel in the initial state and after 117 h of operation. Application of the local approach to fracture and the metallographic analysis, in addition to classical methods (tensile, crack resistance, and fatigue strength tests), provided a more precise evaluation of steel properties degradation due to elevated temperatures and stresses. Urgency of further development of the local approach to predicting material fracture after long-term operation at high temperatures has been substantiated. Исследуется проблема преждевременного разрушения паропроводов (сталь 14MoV6 3) с расчетным ресурсом 100 тыс. ч при температуре 540°С. При изготовлении экспериментальных образцов использовалась сталь в исходном состоянии и после 117 тыс. ч эксплуатации. Применение локального подхода механики разрушения и металлографического анализа наряду с классическими методами (испытания на растяжение, трещиностойкость, усталостную прочность) позволило более точно оценить деградацию свойств стали под действием высоких температур и напряжений. Обоснована необходимость дальнейшего развития локального подхода к прогнозированию условий разрушения материалов при длительной эксплуатации в условиях высоких температур. Досліджується проблема передчасного руйнування паропроводів (сталь 14MoV6 3) із розрахунковим ресурсом 100 тис. год за температури 540оС. При виготовленні експериментальних зразків використовувалася сталь у первинному стані та після 117 тис. год експлуатації. Використання локального підходу механіки руйнування і металографічного аналізу поряд із класичними методами (випробування на розтяг, тріщиностійкість, міцність від утомленості) дозволило більш точно оцінити деградацію властивостей сталі під дією високих температур і напружень. Обгрунтовано необхідність подальшого розвитку локального підходу до прогнозування умов руйнування матеріалів при тривалій експлуатації в умовах високих температур. en Інститут проблем міцності ім. Г.С. Писаренко НАН України Проблемы прочности Научно-технический раздел Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States Вязкость разрушения и трещиностойкость стали паропровода в исходном состоянии и после эксплуатации Article published earlier |
| institution |
Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| collection |
DSpace DC |
| title |
Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States |
| spellingShingle |
Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States Zrilic, M. Burzic, Z. Cvijovic, Z. Научно-технический раздел |
| title_short |
Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States |
| title_full |
Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States |
| title_fullStr |
Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States |
| title_full_unstemmed |
Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States |
| title_sort |
fracture toughness and crack resistance of steam pipeline steel in initial and used states |
| author |
Zrilic, M. Burzic, Z. Cvijovic, Z. |
| author_facet |
Zrilic, M. Burzic, Z. Cvijovic, Z. |
| topic |
Научно-технический раздел |
| topic_facet |
Научно-технический раздел |
| publishDate |
2004 |
| language |
English |
| container_title |
Проблемы прочности |
| publisher |
Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| format |
Article |
| title_alt |
Вязкость разрушения и трещиностойкость стали паропровода в исходном состоянии и после эксплуатации |
| description |
Premature fracture of steam pipelines from
14MoV6 3 steel designed for 1000,000 h service
life at 540°C has been studied. Test specimens are
manufactured from steel in the initial state and after
117 h of operation. Application of the local approach
to fracture and the metallographic analysis,
in addition to classical methods (tensile, crack resistance,
and fatigue strength tests), provided a
more precise evaluation of steel properties degradation
due to elevated temperatures and stresses.
Urgency of further development of the local approach
to predicting material fracture after
long-term operation at high temperatures has been
substantiated.
Исследуется проблема преждевременного разрушения паропроводов (сталь 14MoV6 3) с
расчетным ресурсом 100 тыс. ч при температуре 540°С. При изготовлении экспериментальных
образцов использовалась сталь в исходном состоянии и после 117 тыс. ч эксплуатации.
Применение локального подхода механики разрушения и металлографического анализа
наряду с классическими методами (испытания на растяжение, трещиностойкость,
усталостную прочность) позволило более точно оценить деградацию свойств стали под
действием высоких температур и напряжений. Обоснована необходимость дальнейшего
развития локального подхода к прогнозированию условий разрушения материалов при длительной
эксплуатации в условиях высоких температур.
Досліджується проблема передчасного руйнування паропроводів (сталь
14MoV6 3) із розрахунковим ресурсом 100 тис. год за температури 540оС. При
виготовленні експериментальних зразків використовувалася сталь у
первинному стані та після 117 тис. год експлуатації. Використання локального
підходу механіки руйнування і металографічного аналізу поряд із класичними
методами (випробування на розтяг, тріщиностійкість, міцність від
утомленості) дозволило більш точно оцінити деградацію властивостей сталі
під дією високих температур і напружень. Обгрунтовано необхідність
подальшого розвитку локального підходу до прогнозування умов руйнування
матеріалів при тривалій експлуатації в умовах високих температур.
|
| issn |
0556-171X |
| url |
https://nasplib.isofts.kiev.ua/handle/123456789/47064 |
| fulltext |
|
| citation_txt |
Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States / M. Zrilic, Z. Burzic, Z. Cvijovic // Проблемы прочности. — 2004. — № 1. — С. 68-83. — Бібліогр.: 12 назв. — англ. |
| work_keys_str_mv |
AT zrilicm fracturetoughnessandcrackresistanceofsteampipelinesteelininitialandusedstates AT burzicz fracturetoughnessandcrackresistanceofsteampipelinesteelininitialandusedstates AT cvijovicz fracturetoughnessandcrackresistanceofsteampipelinesteelininitialandusedstates AT zrilicm vâzkostʹrazrušeniâitreŝinostoikostʹstaliparoprovodavishodnomsostoâniiiposleékspluatacii AT burzicz vâzkostʹrazrušeniâitreŝinostoikostʹstaliparoprovodavishodnomsostoâniiiposleékspluatacii AT cvijovicz vâzkostʹrazrušeniâitreŝinostoikostʹstaliparoprovodavishodnomsostoâniiiposleékspluatacii |
| first_indexed |
2025-11-24T11:50:38Z |
| last_indexed |
2025-11-24T11:50:38Z |
| _version_ |
1850846445463142400 |