Fracture resistance of ceramics: edge fracture method
Fracture resistance o f macrohomogeneous line
 ar elastic yttria, scandia, alumina, zirconia, and silicon nitride ceramics was studied upon
 flaking of the edges of rectangular specimens
 with the Rockwell indenter. The correlation between
 the obtained estimates and...
Збережено в:
| Опубліковано в: : | Проблемы прочности |
|---|---|
| Дата: | 2005 |
| Автори: | , , , |
| Формат: | Стаття |
| Мова: | Англійська |
| Опубліковано: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2005
|
| Теми: | |
| Онлайн доступ: | https://nasplib.isofts.kiev.ua/handle/123456789/47774 |
| Теги: |
Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Цитувати: | Fracture resistance of ceramics: edge fracture method / G.A. Gogotsi, V.I. Galenko, B.I. Ozerskii, T.A. Khristevich // Проблемы прочности. — 2005. — № 5. — С. 84-92. — Бібліогр.: 20 назв. — англ. |
Репозитарії
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862634238045585408 |
|---|---|
| author | Gogotsi, G.A. Galenko, V.I. Ozerskii, B.I. Khristevich, T.A. |
| author_facet | Gogotsi, G.A. Galenko, V.I. Ozerskii, B.I. Khristevich, T.A. |
| citation_txt | Fracture resistance of ceramics: edge fracture method / G.A. Gogotsi, V.I. Galenko, B.I. Ozerskii, T.A. Khristevich // Проблемы прочности. — 2005. — № 5. — С. 84-92. — Бібліогр.: 20 назв. — англ. |
| collection | DSpace DC |
| container_title | Проблемы прочности |
| description | Fracture resistance o f macrohomogeneous line
ar elastic yttria, scandia, alumina, zirconia, and silicon nitride ceramics was studied upon
flaking of the edges of rectangular specimens
with the Rockwell indenter. The correlation between
the obtained estimates and fracture toughness
test results gained by the single-edge
V-notched beam method was demonstrated.
Loads giving rise to the flaking of a part of the
edge and distances from this edge to the chip
scar on the specimen surface were measured.
The ratio of those values was considered as a
flaking toughness characteristic. The data obtained
were statististically reliable (based on
more than a hundred determinations). This procedure
termed the edge fracture method can be
used along with other known fracture toughness
test methods for ceramics, its application
is especially advantageous when ceramic item
sizes are comparable with those of the standard
specimens or when expensive materials (e.g.,
nanoceramics) are tested.
Вивчено опір руйнуванню макрооднорідних пружно-лінійних керамічних
матеріалів з оксидів ітрію, скандію й алюмінію, а також із діоксиду цирконію
та нітриду кремнію при сколюванні кромок прямокутних зразків індентором Роквелла. Показано, що отримані оцінки збігаються з результатами
випробувань на в’язкість руйнування, які проводяться за допомогою методу
випробування зразків балочного типу з одностороннім V-подібним надрізом.
При випробуваннях вимірювалося навантаження, яке призводило до
відколу частини кромки, і відстань на поверхні зразка від цієї кромки до
місця формування відколу. Відношення цих величин розглядалося як характеристика
в’язкості відколу. Аналіз даних, що базуються більш як на 100
визначеннях, свідчить про їх статистичну достовірність. Такий метод випробувань,
названий методом сколювання кромок, може використовуватися
нарівні з відомими методами визначення тріщиностійкості кераміки. Його
використання особливо доцільно у випадку, якщо виріб із кераміки за
розмірами можна порівняти зі стандартними зразками, або при проведенні
досліджень дорогих матеріалів (наприклад, нанокераміка).
Изучено сопротивление разрушению макрооднородных линейно-упругих керамических материалов
из оксидов иттрия, скандия и алюминия, а также из диоксида циркония и нитрида
кремния при скалывании кромок прямоугольных образцов индентором Роквелла. Показано
совпадение полученных оценок с результатами испытаний на вязкость разрушения, выполненных
по методу испытания образцов балочного типа с односторонним V-образным надрезом.
При испытаниях измерялась нагрузка, вызывавшая откол части кромки, и расстояние
на поверхности образца от этой кромки до места формирования откола. Отношение
этих величин рассматривалось как характеристика вязкости откола. Анализ данных,
базирующийся более чем на 100 определениях, показал, что они статистически достоверны.
Такой метод испытаний, называемый методом скалывания кромки, может использоваться
наравне с известными методами определения трещиностойкости керамики. Его применение
особенно целесообразно в случае если керамическое изделие по размеру сопоставимо со
стандартными образцами или при проведении исследований дорогостоящих материалов
(например, нанокерамика).
|
| first_indexed | 2025-11-30T16:23:49Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-47774 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 0556-171X |
| language | English |
| last_indexed | 2025-11-30T16:23:49Z |
| publishDate | 2005 |
| publisher | Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| record_format | dspace |
| spelling | Gogotsi, G.A. Galenko, V.I. Ozerskii, B.I. Khristevich, T.A. 2013-07-31T19:22:08Z 2013-07-31T19:22:08Z 2005 Fracture resistance of ceramics: edge fracture method / G.A. Gogotsi, V.I. Galenko, B.I. Ozerskii, T.A. Khristevich // Проблемы прочности. — 2005. — № 5. — С. 84-92. — Бібліогр.: 20 назв. — англ. 0556-171X https://nasplib.isofts.kiev.ua/handle/123456789/47774 539.4 Fracture resistance o f macrohomogeneous line
 ar elastic yttria, scandia, alumina, zirconia, and silicon nitride ceramics was studied upon
 flaking of the edges of rectangular specimens
 with the Rockwell indenter. The correlation between
 the obtained estimates and fracture toughness
 test results gained by the single-edge
 V-notched beam method was demonstrated.
 Loads giving rise to the flaking of a part of the
 edge and distances from this edge to the chip
 scar on the specimen surface were measured.
 The ratio of those values was considered as a
 flaking toughness characteristic. The data obtained
 were statististically reliable (based on
 more than a hundred determinations). This procedure
 termed the edge fracture method can be
 used along with other known fracture toughness
 test methods for ceramics, its application
 is especially advantageous when ceramic item
 sizes are comparable with those of the standard
 specimens or when expensive materials (e.g.,
 nanoceramics) are tested. Вивчено опір руйнуванню макрооднорідних пружно-лінійних керамічних
 матеріалів з оксидів ітрію, скандію й алюмінію, а також із діоксиду цирконію
 та нітриду кремнію при сколюванні кромок прямокутних зразків індентором Роквелла. Показано, що отримані оцінки збігаються з результатами
 випробувань на в’язкість руйнування, які проводяться за допомогою методу
 випробування зразків балочного типу з одностороннім V-подібним надрізом.
 При випробуваннях вимірювалося навантаження, яке призводило до
 відколу частини кромки, і відстань на поверхні зразка від цієї кромки до
 місця формування відколу. Відношення цих величин розглядалося як характеристика
 в’язкості відколу. Аналіз даних, що базуються більш як на 100
 визначеннях, свідчить про їх статистичну достовірність. Такий метод випробувань,
 названий методом сколювання кромок, може використовуватися
 нарівні з відомими методами визначення тріщиностійкості кераміки. Його
 використання особливо доцільно у випадку, якщо виріб із кераміки за
 розмірами можна порівняти зі стандартними зразками, або при проведенні
 досліджень дорогих матеріалів (наприклад, нанокераміка). Изучено сопротивление разрушению макрооднородных линейно-упругих керамических материалов
 из оксидов иттрия, скандия и алюминия, а также из диоксида циркония и нитрида
 кремния при скалывании кромок прямоугольных образцов индентором Роквелла. Показано
 совпадение полученных оценок с результатами испытаний на вязкость разрушения, выполненных
 по методу испытания образцов балочного типа с односторонним V-образным надрезом.
 При испытаниях измерялась нагрузка, вызывавшая откол части кромки, и расстояние
 на поверхности образца от этой кромки до места формирования откола. Отношение
 этих величин рассматривалось как характеристика вязкости откола. Анализ данных,
 базирующийся более чем на 100 определениях, показал, что они статистически достоверны.
 Такой метод испытаний, называемый методом скалывания кромки, может использоваться
 наравне с известными методами определения трещиностойкости керамики. Его применение
 особенно целесообразно в случае если керамическое изделие по размеру сопоставимо со
 стандартными образцами или при проведении исследований дорогостоящих материалов
 (например, нанокерамика). en Інститут проблем міцності ім. Г.С. Писаренко НАН України Проблемы прочности Научно-технический раздел Fracture resistance of ceramics: edge fracture method Сопротивление керамики разрушению: метод скалывания кромки Article published earlier |
| spellingShingle | Fracture resistance of ceramics: edge fracture method Gogotsi, G.A. Galenko, V.I. Ozerskii, B.I. Khristevich, T.A. Научно-технический раздел |
| title | Fracture resistance of ceramics: edge fracture method |
| title_alt | Сопротивление керамики разрушению: метод скалывания кромки |
| title_full | Fracture resistance of ceramics: edge fracture method |
| title_fullStr | Fracture resistance of ceramics: edge fracture method |
| title_full_unstemmed | Fracture resistance of ceramics: edge fracture method |
| title_short | Fracture resistance of ceramics: edge fracture method |
| title_sort | fracture resistance of ceramics: edge fracture method |
| topic | Научно-технический раздел |
| topic_facet | Научно-технический раздел |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/47774 |
| work_keys_str_mv | AT gogotsiga fractureresistanceofceramicsedgefracturemethod AT galenkovi fractureresistanceofceramicsedgefracturemethod AT ozerskiibi fractureresistanceofceramicsedgefracturemethod AT khristevichta fractureresistanceofceramicsedgefracturemethod AT gogotsiga soprotivleniekeramikirazrušeniûmetodskalyvaniâkromki AT galenkovi soprotivleniekeramikirazrušeniûmetodskalyvaniâkromki AT ozerskiibi soprotivleniekeramikirazrušeniûmetodskalyvaniâkromki AT khristevichta soprotivleniekeramikirazrušeniûmetodskalyvaniâkromki |