Compressive creep of Fe3Al-type iron aluminide with Zr additions
High-temperature creep ofa Fe3Al-type iron aluminide alloyed by zirconium was studied in the temperature range 873-1073 K. The alloy contained (wt.%) 31.5% Al, 3.5% Cr, 0.25% Zr, 0.19% C (Fe balance). It was tested in two states: (i) as received after hot rolling and (ii) heat treated (1423 K/ 2 h/a...
Gespeichert in:
| Veröffentlicht in: | Проблемы прочности |
|---|---|
| Datum: | 2008 |
| Hauptverfasser: | , , |
| Format: | Artikel |
| Sprache: | Englisch |
| Veröffentlicht: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2008
|
| Schlagworte: | |
| Online Zugang: | https://nasplib.isofts.kiev.ua/handle/123456789/48439 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Compressive creep of Fe3Al-type iron aluminide with Zr additions / F. Dobes, P. Kratochvil, K. Milicka // Проблемы прочности. — 2008. — № 1. — С.117-120. — Бібліогр.: 8 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862538261945122816 |
|---|---|
| author | Dobes, F. Kratochvil, P. Milicka, K. |
| author_facet | Dobes, F. Kratochvil, P. Milicka, K. |
| citation_txt | Compressive creep of Fe3Al-type iron aluminide with Zr additions / F. Dobes, P. Kratochvil, K. Milicka // Проблемы прочности. — 2008. — № 1. — С.117-120. — Бібліогр.: 8 назв. — англ. |
| collection | DSpace DC |
| container_title | Проблемы прочности |
| description | High-temperature creep ofa Fe3Al-type iron aluminide alloyed by zirconium was studied in the temperature range 873-1073 K. The alloy contained (wt.%) 31.5% Al, 3.5% Cr, 0.25% Zr, 0.19% C (Fe balance). It was tested in two states: (i) as received after hot rolling and (ii) heat treated (1423 K/ 2 h/air). Creep tests were performed in compression at constant load with stepwise loading: in each step, the load was changed to a new value after steady state creep rate had been established. Stress exponent and activation energy of the creep rate were determined and possible creep mechanisms were discussed in terms ofthe threshold stress concept. A rapidfall ofthe stress exponent and ofthe threshold stress with the increasing temperature indicates that creep is impeded by the presence of precipitates only at temperature 873 K. The results were compared with the results oflong-term creep tests in tension performed recently on the same alloy.
Изучена высокотемпературная ползучесть
Изучена высокотемпературная ползучесть алюминида железа типа Fe3Al, легированного цирконием в диапазоне температур 873...1073 К. Сплав содержал (ат.%) 31,5 Al, 3,5 Сг, 0,25 Zг, 0,19 С (остальное Fе). Испытания проводили в двух состояниях: в состоянии поставки после горячей прокатки и после термообработки (1423 К/2 ч/воздух). Испытания на ползучесть выполняли при постоянной сжимающей нагрузке при ступенчатом нагружении: на каждой ступени использовали нагрузку другой величины после того, как наступала стадия установившейся скорости ползучести. Определена экспонента напряжения и энергия активации для скорости ползучести, обсуждены возможные механизмы ползучести с позиций концепции порогового напряжения. Резкое уменьшение экспоненты напряжения и порогового напряжения при увеличении температуры свидетельствует о том, что наличие вторичных фаз снижает скорость ползучести только при температуре 873 К. Полученные результаты сравнивали с данными длительных испытаний на ползучесть при растяжении, выполненных на том же сплаве.
|
| first_indexed | 2025-11-24T13:43:33Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-48439 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 0556-171X |
| language | English |
| last_indexed | 2025-11-24T13:43:33Z |
| publishDate | 2008 |
| publisher | Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| record_format | dspace |
| spelling | Dobes, F. Kratochvil, P. Milicka, K. 2013-08-19T15:31:46Z 2013-08-19T15:31:46Z 2008 Compressive creep of Fe3Al-type iron aluminide with Zr additions / F. Dobes, P. Kratochvil, K. Milicka // Проблемы прочности. — 2008. — № 1. — С.117-120. — Бібліогр.: 8 назв. — англ. 0556-171X https://nasplib.isofts.kiev.ua/handle/123456789/48439 539.4 High-temperature creep ofa Fe3Al-type iron aluminide alloyed by zirconium was studied in the temperature range 873-1073 K. The alloy contained (wt.%) 31.5% Al, 3.5% Cr, 0.25% Zr, 0.19% C (Fe balance). It was tested in two states: (i) as received after hot rolling and (ii) heat treated (1423 K/ 2 h/air). Creep tests were performed in compression at constant load with stepwise loading: in each step, the load was changed to a new value after steady state creep rate had been established. Stress exponent and activation energy of the creep rate were determined and possible creep mechanisms were discussed in terms ofthe threshold stress concept. A rapidfall ofthe stress exponent and ofthe threshold stress with the increasing temperature indicates that creep is impeded by the presence of precipitates only at temperature 873 K. The results were compared with the results oflong-term creep tests in tension performed recently on the same alloy.
 Изучена высокотемпературная ползучесть Изучена высокотемпературная ползучесть алюминида железа типа Fe3Al, легированного цирконием в диапазоне температур 873...1073 К. Сплав содержал (ат.%) 31,5 Al, 3,5 Сг, 0,25 Zг, 0,19 С (остальное Fе). Испытания проводили в двух состояниях: в состоянии поставки после горячей прокатки и после термообработки (1423 К/2 ч/воздух). Испытания на ползучесть выполняли при постоянной сжимающей нагрузке при ступенчатом нагружении: на каждой ступени использовали нагрузку другой величины после того, как наступала стадия установившейся скорости ползучести. Определена экспонента напряжения и энергия активации для скорости ползучести, обсуждены возможные механизмы ползучести с позиций концепции порогового напряжения. Резкое уменьшение экспоненты напряжения и порогового напряжения при увеличении температуры свидетельствует о том, что наличие вторичных фаз снижает скорость ползучести только при температуре 873 К. Полученные результаты сравнивали с данными длительных испытаний на ползучесть при растяжении, выполненных на том же сплаве. The paper is based on work supported by the Grant Agency of the Czech Republic within the project 106/05/0409. en Інститут проблем міцності ім. Г.С. Писаренко НАН України Проблемы прочности Научно-технический раздел Compressive creep of Fe3Al-type iron aluminide with Zr additions Ползучесть при сжатии алюминида железа типа Fe3Al с добавками Zr Article published earlier |
| spellingShingle | Compressive creep of Fe3Al-type iron aluminide with Zr additions Dobes, F. Kratochvil, P. Milicka, K. Научно-технический раздел |
| title | Compressive creep of Fe3Al-type iron aluminide with Zr additions |
| title_alt | Ползучесть при сжатии алюминида железа типа Fe3Al с добавками Zr |
| title_full | Compressive creep of Fe3Al-type iron aluminide with Zr additions |
| title_fullStr | Compressive creep of Fe3Al-type iron aluminide with Zr additions |
| title_full_unstemmed | Compressive creep of Fe3Al-type iron aluminide with Zr additions |
| title_short | Compressive creep of Fe3Al-type iron aluminide with Zr additions |
| title_sort | compressive creep of fe3al-type iron aluminide with zr additions |
| topic | Научно-технический раздел |
| topic_facet | Научно-технический раздел |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/48439 |
| work_keys_str_mv | AT dobesf compressivecreepoffe3altypeironaluminidewithzradditions AT kratochvilp compressivecreepoffe3altypeironaluminidewithzradditions AT milickak compressivecreepoffe3altypeironaluminidewithzradditions AT dobesf polzučestʹprisžatiialûminidaželezatipafe3alsdobavkamizr AT kratochvilp polzučestʹprisžatiialûminidaželezatipafe3alsdobavkamizr AT milickak polzučestʹprisžatiialûminidaželezatipafe3alsdobavkamizr |