Mechanisms of Fracture in Neutron-Irradiated 15Ch2MFA Steel
The influence of irradiation on fracture properties of 15Ch2MFA pressure vessel steel is studied. The distribution of inclusions and carbides is characterized. The quantitative fractography of broken Charpy specimens is carried out. The correlation of crack initiation energy and the area of ductile...
Gespeichert in:
| Veröffentlicht in: | Проблемы прочности |
|---|---|
| Datum: | 2008 |
| Hauptverfasser: | , , |
| Format: | Artikel |
| Sprache: | Englisch |
| Veröffentlicht: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2008
|
| Schlagworte: | |
| Online Zugang: | https://nasplib.isofts.kiev.ua/handle/123456789/48441 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Mechanisms of Fracture in Neutron-Irradiated 15Ch2MFA Steel / S. Valek, P. Hausild, M. Kytka // Проблемы прочности. — 2008. — № 1. — С. 113-116. — Бібліогр.: 4 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| _version_ | 1862747271933722624 |
|---|---|
| author | Valek, S. Hausild, P. Kytka, M. |
| author_facet | Valek, S. Hausild, P. Kytka, M. |
| citation_txt | Mechanisms of Fracture in Neutron-Irradiated 15Ch2MFA Steel / S. Valek, P. Hausild, M. Kytka // Проблемы прочности. — 2008. — № 1. — С. 113-116. — Бібліогр.: 4 назв. — англ. |
| collection | DSpace DC |
| container_title | Проблемы прочности |
| description | The influence of irradiation on fracture properties of 15Ch2MFA pressure vessel steel is studied. The distribution of inclusions and carbides is characterized. The quantitative fractography of broken Charpy specimens is carried out. The correlation of crack initiation energy and the area of ductile fracture adjacent to the notch is identified. It is shown that most of the absorbed energy belongs to the stage preceding the cleavage crack initiation. From the fracture surface of Charpy specimens the distribution of ductile dimples is investigated. The relationship between the distributions of ductile dimples and second phase particles is discussed.
Изучено влияние облучения на разрушение корпусной стали 15Х2МФА. Показано распределение включений и карбидов. Выполнен анализ образцов, разрушенных по методу Шарпи, с помощью количественной фрактографии. Выявлена корреляция между энергией зарождения трещины и зоной вязкого разрушения вблизи надреза. Установлено, что большая часть энергии поглощается на стадии, предшествующей возникновению трещины скола. Исследовано распределение ямок вязкого разрушения на поверхности образцов Шарпи. Оценена зависимость между распределением ямок и частицами вторичных фаз.
|
| first_indexed | 2025-12-07T20:50:06Z |
| format | Article |
| fulltext | |
| id | nasplib_isofts_kiev_ua-123456789-48441 |
| institution | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| issn | 0556-171X |
| language | English |
| last_indexed | 2025-12-07T20:50:06Z |
| publishDate | 2008 |
| publisher | Інститут проблем міцності ім. Г.С. Писаренко НАН України |
| record_format | dspace |
| spelling | Valek, S. Hausild, P. Kytka, M. 2013-08-19T15:38:34Z 2013-08-19T15:38:34Z 2008 Mechanisms of Fracture in Neutron-Irradiated 15Ch2MFA Steel / S. Valek, P. Hausild, M. Kytka // Проблемы прочности. — 2008. — № 1. — С. 113-116. — Бібліогр.: 4 назв. — англ. 0556-171X https://nasplib.isofts.kiev.ua/handle/123456789/48441 539.4 The influence of irradiation on fracture properties of 15Ch2MFA pressure vessel steel is studied. The distribution of inclusions and carbides is characterized. The quantitative fractography of broken Charpy specimens is carried out. The correlation of crack initiation energy and the area of ductile fracture adjacent to the notch is identified. It is shown that most of the absorbed energy belongs to the stage preceding the cleavage crack initiation. From the fracture surface of Charpy specimens the distribution of ductile dimples is investigated. The relationship between the distributions of ductile dimples and second phase particles is discussed. Изучено влияние облучения на разрушение корпусной стали 15Х2МФА. Показано распределение включений и карбидов. Выполнен анализ образцов, разрушенных по методу Шарпи, с помощью количественной фрактографии. Выявлена корреляция между энергией зарождения трещины и зоной вязкого разрушения вблизи надреза. Установлено, что большая часть энергии поглощается на стадии, предшествующей возникновению трещины скола. Исследовано распределение ямок вязкого разрушения на поверхности образцов Шарпи. Оценена зависимость между распределением ямок и частицами вторичных фаз. This project has been financially supported by the Ministry of Education, Youth, and Sports of the Czech Republic in the frame of the project No. MSM 6840770020. en Інститут проблем міцності ім. Г.С. Писаренко НАН України Проблемы прочности Научно-технический раздел Mechanisms of Fracture in Neutron-Irradiated 15Ch2MFA Steel Механизмы разрушения облученной нейтронами стали 15Х2МФА Article published earlier |
| spellingShingle | Mechanisms of Fracture in Neutron-Irradiated 15Ch2MFA Steel Valek, S. Hausild, P. Kytka, M. Научно-технический раздел |
| title | Mechanisms of Fracture in Neutron-Irradiated 15Ch2MFA Steel |
| title_alt | Механизмы разрушения облученной нейтронами стали 15Х2МФА |
| title_full | Mechanisms of Fracture in Neutron-Irradiated 15Ch2MFA Steel |
| title_fullStr | Mechanisms of Fracture in Neutron-Irradiated 15Ch2MFA Steel |
| title_full_unstemmed | Mechanisms of Fracture in Neutron-Irradiated 15Ch2MFA Steel |
| title_short | Mechanisms of Fracture in Neutron-Irradiated 15Ch2MFA Steel |
| title_sort | mechanisms of fracture in neutron-irradiated 15ch2mfa steel |
| topic | Научно-технический раздел |
| topic_facet | Научно-технический раздел |
| url | https://nasplib.isofts.kiev.ua/handle/123456789/48441 |
| work_keys_str_mv | AT valeks mechanismsoffractureinneutronirradiated15ch2mfasteel AT hausildp mechanismsoffractureinneutronirradiated15ch2mfasteel AT kytkam mechanismsoffractureinneutronirradiated15ch2mfasteel AT valeks mehanizmyrazrušeniâoblučennoineitronamistali15h2mfa AT hausildp mehanizmyrazrušeniâoblučennoineitronamistali15h2mfa AT kytkam mehanizmyrazrušeniâoblučennoineitronamistali15h2mfa |