Comparison of fatigue criteria for combined bending-torsion loading of nitrided and virgin specimens

• Veröffentlicht in: Проблемы прочности
• Datum: 2008
• Hauptverfasser: Major, S., Papuga, J., Hornikova, J., Pokluda, J.
• Format: Artikel
• Sprache: English
• Veröffentlicht: Інститут проблем міцності ім. Г.С. Писаренко НАН України 2008
• Schlagworte: Научно-технический раздел
• Online Zugang: https://nasplib.isofts.kiev.ua/handle/123456789/48456
• Назва журналу: Digital Library of Periodicals of National Academy of Sciences of Ukraine
• Zitieren: Comparison of fatigue criteria for combined bending-torsion loading of nitrided and virgin specimens / S. Major, J. Papuga, J. Hornikova, J. Pokluda // Проблемы прочности. — 2008. — № 1. — С. 73-76. — Бібліогр.: 10 назв. — англ.

This work deals with fatigue life of plasma-nitrided and virgin specimens made of a low-alloy high strength steel. Specimens were subjected to an in-phase combined bending-torsion loading. The plasma-nitrided specimens exhibited a significantly improved fatigue resistance. The criterion proposed by McDiarmid was found to be the most precise in the fatigue life prediction fo r virgin specimens. On the other hand, the Matake criterion was the most successful fo r nitrided specimens. Исследована усталостная долговечность азотированных в плазме образцов и исходных образцов из низколегированной высокопрочной стали. Испытания образцов проводились при синфазном совмещенном изгибе с кручением. Показано, что азотированные в плазме образцы обладают более высокой усталостной стойкостью. Установлено, что для образцов в исходном состоянии наибольшая точность прогнозирования усталостной долговечности обеспечивается при использовании критерия, предложенного Мак-Диармидом. С другой стороны, для азотированных образцов наиболее подходящим оказался критерий Матаке.