Deformation and fracture of high-temperature steels at different temperatures and loading rates

• Veröffentlicht in: Проблемы прочности
• Datum: 2009
• Hauptverfasser: Kondryakov, E.A., Lenzion, S.V., Kharchenko, V.V.
• Format: Artikel
• Sprache: English
• Veröffentlicht: Інститут проблем міцності ім. Г.С. Писаренко НАН України 2009
• Schlagworte: Научно-технический раздел
• Online Zugang: https://nasplib.isofts.kiev.ua/handle/123456789/48479
• Назва журналу: Digital Library of Periodicals of National Academy of Sciences of Ukraine
• Zitieren: Deformation and fracture of high-temperature steels at different temperatures and loading rates / E.A. Kondryakov, S.V. Lenzion, V.V. Kharchenko // Проблемы прочности. — 2009. — № 1. — С. 29-34. — Бібліогр.: 11 назв. — англ.

Charpy impact tests were conducted at different temperatures and loading rates. Temperature dependences of the crack initiation and propagation energies were determinedfor carbon steel 45, steels St. 3 and 15Kh2NMFA from the load-time curves obtained with due account of the impact test results. The effect o f the loading rate on the temperature dependence o f the impact toughness was analyzed within the range from 1 to 4.4 m/s. Выполнены ударные испытания образцов типа Шарпи при различных температурах и скоростях нагружения. Для малоуглеродис­тых сталей 45 и Ст. 3, а также для стали 15Х2НМФА определены температурные зависимости энергий инициирования и рас­пространения трещин по диаграммам на­грузка-время, полученным с учетом резуль­татов ударных испытаний. Проанализирова­но влияние скорости нагружения на температурную зависимость ударной вязкости разрушения в диапазоне скоростей нагру­жения 1...4,4 м/с.