Study of the stressed state near the crack that initiates at the inclusion under longitudinal shift wave influence
Modern elements of building structures and machine parts often contain structural elements or technological defects that can be considered as thin inclusions of high rigidity. Reinforcing elements of composite materials can also be thin rigid inclusions. But studies show that thin rigid inclusions c...
Збережено в:
| Дата: | 2019 |
|---|---|
| Автори: | , |
| Формат: | Стаття |
| Мова: | English Ukrainian |
| Опубліковано: |
Інститут енергетичних машин і систем ім. А. М. Підгорного Національної академії наук України
2019
|
| Теми: | |
| Онлайн доступ: | https://journals.uran.ua/jme/article/view/153943 |
| Теги: |
Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
|
| Назва журналу: | Energy Technologies & Resource Saving |
Репозитарії
Energy Technologies & Resource Saving| Резюме: | Modern elements of building structures and machine parts often contain structural elements or technological defects that can be considered as thin inclusions of high rigidity. Reinforcing elements of composite materials can also be thin rigid inclusions. But studies show that thin rigid inclusions cause a significant stress concentration in the environment, which can lead to the formation of cracks at the inclusion. The problems of determining the stress state in the vicinity of complex defects were solved, as a rule, in a static formulation and for the case of rectilinear defects. This is due to the difficulties that arise in the case of their solution by the common method of boundary integral equations, which consists in reducing such problems to singular integral or integro-differential equations with fixed singularities. Such equations require that special methods be created for their numerical solution. Recently, there has been a continuous growth in the number of papers where special quadrature formulas are used for singular integrals with fixed singularities, for example, for cracks or inclusions in the form of broken or branched defects. These works propose a collocation method that takes into account the real feature of the solution, and in order to calculate integrals with fixed singularities special quadrature formulas are used. The problems of determining the stress state around the defects, which are thin inclusions from whose edge a crack propagates at a certain angle, have been barely solved. The purpose of this paper is to study the stress state near the crack that initiates at the inclusion when subjected to a longitudinal shear wave. The formulated problem is reduced to a system of singular integro-differential equations with fixed singularities with respect to the unknown voltage surges and displacements on the surface of a defect. To solve this system, a similar collocation method is used. There have been shown dependences of the change in the dimensionless values of the stress intensity factors (SIF) on the dimensionless value of the wave number in the case of wave propagation at different angles. For numerical experiments, different values of the angle between the inclusion and crack were taken. In all cases, there was found the value of the dimensionless wave number at which SIFs for the crack reach their peaks. With an increase in the angle between the inclusion and crack, SIF values for the inclusion, up to certain oscillation frequency values, decrease. For the case when the defects are on the same straight line, SIF values for the inclusion are smallest. Conversely, when the angle between the defects increases, SIF values for the crack increase too. In general, as a result of the complexity of the wave field created by the reflection of waves from a defect, SIF dependence on frequency has significant maxima, whose magnitude and position are influenced by the configuration of the defect. |
|---|