Вплив структурних характеристик на сорбційні властивості літій-селективних композиційних матеріалів на основі TiO2 та MnO2
Novel composite materials with equimolar ratio of TiO2 to MnO2 have been synthetized. Using the low-temperature N2 adsorption method their structural characteristics were calculated; and their influence on selectivity and kinetics of lithium sorption was shown. It was proved that sorption characteri...
Gespeichert in:
| Datum: | 2014 |
|---|---|
| Hauptverfasser: | , , , |
| Format: | Artikel |
| Sprache: | Englisch |
| Veröffentlicht: |
Chuiko Institute of Surface Chemistry National Academy of Sciences of Ukraine
2014
|
| Schlagworte: | |
| Online Zugang: | https://www.cpts.com.ua/index.php/cpts/article/view/290 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Chemistry, Physics and Technology of Surface |
Institution
Chemistry, Physics and Technology of Surface| Zusammenfassung: | Novel composite materials with equimolar ratio of TiO2 to MnO2 have been synthetized. Using the low-temperature N2 adsorption method their structural characteristics were calculated; and their influence on selectivity and kinetics of lithium sorption was shown. It was proved that sorption characteristics of the obtained materials are defermined by conditions of heat treatment during the synthesis. Higher temperatures provoke agglomeration of sorbent and decrease in its kinetic characteristics. At the same time, more lithium-selective sorption sites are formed and the selectivity of sorption increases. By the proposed synthesis method a highly selective to lithium ion-exchange material was obtained. |
|---|