Template-based approach in the preparation of nanoporous silicas and titania-silicas
Mesoporous silicas and titania-silicas were synthesized with use as a template quaternary ammonium salts and their hydroxides. Fumed silica, tetraethyl orthosilicate and titanium(IV) tetraisopropoxide were applied as presursors. Syntheses were carried out in presence HCl and NH4OH. Mesoporous titani...
Gespeichert in:
| Datum: | 2001 |
|---|---|
| Hauptverfasser: | , , , , |
| Format: | Artikel |
| Sprache: | Englisch |
| Veröffentlicht: |
Chuiko Institute of Surface Chemistry National Academy of Sciences of Ukraine
2001
|
| Online Zugang: | https://surfacezbir.com.ua/index.php/surface/article/view/48 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Surface |
| Завантажити файл: |  |
Institution
Surface| Zusammenfassung: | Mesoporous silicas and titania-silicas were synthesized with use as a template quaternary ammonium salts and their hydroxides. Fumed silica, tetraethyl orthosilicate and titanium(IV) tetraisopropoxide were applied as presursors. Syntheses were carried out in presence HCl and NH4OH. Mesoporous titania-silicas with TiO2 contents from 1 up to 70 mol. % were prepared. Obtained samples have been characterized by the powder X-ray diffraction data and nitrogen adsorption at 77 K. Specific surface area, total pore volume, pore volume and area distribution were determined from nitrogen adsorption isotherm for synthesized titania-silicas. It was demonstrated that the ordered structures of MCM-41 type and bimodal porous materials with maximum pore diameter of 3 and 30 nm may be prepared depending of a synthesis conditions and a precursor nature. |
|---|