ВПЛИВ ДОБАВКИ VC-Al НА СТРУКТУРУ ТА ФАЗОВИЙ СКЛАД НАДТВЕРДИХ МАТЕРІАЛІВ НА ОСНОВІ cBN

ВПЛИВ ДОБАВКИ VC-Al НА СТРУКТУРУ ТА ФАЗОВИЙ СКЛАД НАДТВЕРДИХ МАТЕРІАЛІВ НА ОСНОВІ cBN

Ceramic matrix materials based on cubic boron nitride with additives of vanadium carbide and aluminum were obtained by high pressure high temperature sintering. Sintering was carried out under pressure 7.7 GPa, in the wide temperature range of 1450 - 2450 °C. Three compositions containing 50, 60 and...

Full description

Saved in:
Bibliographic Details
Date:2018
Main Authors: Сліпченко, К. В., Петруша, І. А., Туркевич, В. З., Бушля, В. М., Штоль, Я.-Е.
Format: Article
Language:Ukrainian
Published: Институт сверхтвердых материалов им. В. Н. Бакуля Национальной академии наук Украины 2018
Subjects:
апарат високого тиску
надтверда кераміка
КНБ
фазовий склад
структура
ванадій
Online Access:http://altis-ism.org.ua/index.php/ALTIS/article/view/44
Tags: Add Tag
No Tags, Be the first to tag this record!
Journal Title:Tooling materials science

Institution

Tooling materials science
id oai:ojs2.altis-ism.org.ua:article-44
record_format ojs
institution Tooling materials science
baseUrl_str
datestamp_date 2019-07-15T12:06:04Z
collection OJS
language Ukrainian
topic апарат високого тиску
надтверда кераміка
КНБ
фазовий склад
структура
ванадій
spellingShingle апарат високого тиску
надтверда кераміка
КНБ
фазовий склад
структура
ванадій
Сліпченко, К. В.
Петруша, І. А.
Туркевич, В. З.
Бушля, В. М.
Штоль, Я.-Е.
ВПЛИВ ДОБАВКИ VC-Al НА СТРУКТУРУ ТА ФАЗОВИЙ СКЛАД НАДТВЕРДИХ МАТЕРІАЛІВ НА ОСНОВІ cBN
topic_facet high pressure apparatus
superhard ceramics
cBN
phase composition
structure
vanadium
аппарат высокого давления
сверхтвердые керамика
КНБ
фазовый состав
структура
ванадий
апарат високого тиску
надтверда кераміка
КНБ
фазовий склад
структура
ванадій
format Article
author Сліпченко, К. В.
Петруша, І. А.
Туркевич, В. З.
Бушля, В. М.
Штоль, Я.-Е.
author_facet Сліпченко, К. В.
Петруша, І. А.
Туркевич, В. З.
Бушля, В. М.
Штоль, Я.-Е.
author_sort Сліпченко, К. В.
title ВПЛИВ ДОБАВКИ VC-Al НА СТРУКТУРУ ТА ФАЗОВИЙ СКЛАД НАДТВЕРДИХ МАТЕРІАЛІВ НА ОСНОВІ cBN
title_short ВПЛИВ ДОБАВКИ VC-Al НА СТРУКТУРУ ТА ФАЗОВИЙ СКЛАД НАДТВЕРДИХ МАТЕРІАЛІВ НА ОСНОВІ cBN
title_full ВПЛИВ ДОБАВКИ VC-Al НА СТРУКТУРУ ТА ФАЗОВИЙ СКЛАД НАДТВЕРДИХ МАТЕРІАЛІВ НА ОСНОВІ cBN
title_fullStr ВПЛИВ ДОБАВКИ VC-Al НА СТРУКТУРУ ТА ФАЗОВИЙ СКЛАД НАДТВЕРДИХ МАТЕРІАЛІВ НА ОСНОВІ cBN
title_full_unstemmed ВПЛИВ ДОБАВКИ VC-Al НА СТРУКТУРУ ТА ФАЗОВИЙ СКЛАД НАДТВЕРДИХ МАТЕРІАЛІВ НА ОСНОВІ cBN
title_sort вплив добавки vc-al на структуру та фазовий склад надтвердих матеріалів на основі cbn
title_alt THE INFLUENCE OF VC-AL ADDITIVE CONTENT ON STRUCTURE AND PHASE COMPOSITION OF cBN BASED SUPERHARD MATERIALS
ВЛИЯНИЕ ДОБАВКИ VC-Al НА СТРУКТУРУ И ФАЗОВЫЙ СОСТАВ СВЕРХТВЕРДЫХ МАТЕРИАЛОВ НА ОСНОВЕ cBN
description Ceramic matrix materials based on cubic boron nitride with additives of vanadium carbide and aluminum were obtained by high pressure high temperature sintering. Sintering was carried out under pressure 7.7 GPa, in the wide temperature range of 1450 - 2450 °C. Three compositions containing 50, 60 and 65 vol.% of cBN were selected for investigation, 5% by volume of aluminum introduced into the mixture as oxygen geter. This paper presents the results of the study of the phase composition, microstructures and mechanical properties. It was found that the variation of the additive content has no effect on the shear modulus of composites, the highest values of microhardness were obtained in composites sintered in the temperature range of 1850 - 2150 °C. Formation of aluminum oxide were detected in all studied systems when sinterinf temperature was higher than 2000 °C. Mechanical properties of developed materialsclose to commercial analogues of BL group materials. Cutting tool materials in system cBN-VC-Al can be used at high-speed processing of alloys on the basis of iron
publisher Институт сверхтвердых материалов им. В. Н. Бакуля Национальной академии наук Украины
publishDate 2018
url http://altis-ism.org.ua/index.php/ALTIS/article/view/44
work_keys_str_mv AT slípčenkokv theinfluenceofvcaladditivecontentonstructureandphasecompositionofcbnbasedsuperhardmaterials
AT petrušaía theinfluenceofvcaladditivecontentonstructureandphasecompositionofcbnbasedsuperhardmaterials
AT turkevičvz theinfluenceofvcaladditivecontentonstructureandphasecompositionofcbnbasedsuperhardmaterials
AT bušlâvm theinfluenceofvcaladditivecontentonstructureandphasecompositionofcbnbasedsuperhardmaterials
AT štolʹâe theinfluenceofvcaladditivecontentonstructureandphasecompositionofcbnbasedsuperhardmaterials
AT slípčenkokv vliâniedobavkivcalnastrukturuifazovyjsostavsverhtverdyhmaterialovnaosnovecbn
AT petrušaía vliâniedobavkivcalnastrukturuifazovyjsostavsverhtverdyhmaterialovnaosnovecbn
AT turkevičvz vliâniedobavkivcalnastrukturuifazovyjsostavsverhtverdyhmaterialovnaosnovecbn
AT bušlâvm vliâniedobavkivcalnastrukturuifazovyjsostavsverhtverdyhmaterialovnaosnovecbn
AT štolʹâe vliâniedobavkivcalnastrukturuifazovyjsostavsverhtverdyhmaterialovnaosnovecbn
AT slípčenkokv vplivdobavkivcalnastrukturutafazovijskladnadtverdihmateríalívnaosnovícbn
AT petrušaía vplivdobavkivcalnastrukturutafazovijskladnadtverdihmateríalívnaosnovícbn
AT turkevičvz vplivdobavkivcalnastrukturutafazovijskladnadtverdihmateríalívnaosnovícbn
AT bušlâvm vplivdobavkivcalnastrukturutafazovijskladnadtverdihmateríalívnaosnovícbn
AT štolʹâe vplivdobavkivcalnastrukturutafazovijskladnadtverdihmateríalívnaosnovícbn
AT slípčenkokv influenceofvcaladditivecontentonstructureandphasecompositionofcbnbasedsuperhardmaterials
AT petrušaía influenceofvcaladditivecontentonstructureandphasecompositionofcbnbasedsuperhardmaterials
AT turkevičvz influenceofvcaladditivecontentonstructureandphasecompositionofcbnbasedsuperhardmaterials
AT bušlâvm influenceofvcaladditivecontentonstructureandphasecompositionofcbnbasedsuperhardmaterials
AT štolʹâe influenceofvcaladditivecontentonstructureandphasecompositionofcbnbasedsuperhardmaterials
first_indexed 2025-09-24T17:41:41Z
last_indexed 2025-09-24T17:41:41Z
_version_ 1850410028221071360
spelling oai:ojs2.altis-ism.org.ua:article-442019-07-15T12:06:04Z THE INFLUENCE OF VC-AL ADDITIVE CONTENT ON STRUCTURE AND PHASE COMPOSITION OF cBN BASED SUPERHARD MATERIALS ВЛИЯНИЕ ДОБАВКИ VC-Al НА СТРУКТУРУ И ФАЗОВЫЙ СОСТАВ СВЕРХТВЕРДЫХ МАТЕРИАЛОВ НА ОСНОВЕ cBN ВПЛИВ ДОБАВКИ VC-Al НА СТРУКТУРУ ТА ФАЗОВИЙ СКЛАД НАДТВЕРДИХ МАТЕРІАЛІВ НА ОСНОВІ cBN Сліпченко, К. В. Петруша, І. А. Туркевич, В. З. Бушля, В. М. Штоль, Я.-Е. high pressure apparatus, superhard ceramics, cBN, phase composition, structure, vanadium аппарат высокого давления, сверхтвердые керамика, КНБ, фазовый состав, структура, ванадий апарат високого тиску, надтверда кераміка, КНБ, фазовий склад, структура, ванадій Ceramic matrix materials based on cubic boron nitride with additives of vanadium carbide and aluminum were obtained by high pressure high temperature sintering. Sintering was carried out under pressure 7.7 GPa, in the wide temperature range of 1450 - 2450 °C. Three compositions containing 50, 60 and 65 vol.% of cBN were selected for investigation, 5% by volume of aluminum introduced into the mixture as oxygen geter. This paper presents the results of the study of the phase composition, microstructures and mechanical properties. It was found that the variation of the additive content has no effect on the shear modulus of composites, the highest values of microhardness were obtained in composites sintered in the temperature range of 1850 - 2150 °C. Formation of aluminum oxide were detected in all studied systems when sinterinf temperature was higher than 2000 °C. Mechanical properties of developed materialsclose to commercial analogues of BL group materials. Cutting tool materials in system cBN-VC-Al can be used at high-speed processing of alloys on the basis of iron Путем термобарического спекания получено керамо-матричный композиционный материал на основе кубического нитрида бора с добавками карбида ванадия и алюминия. Спекания проведено в условиях высокого давления (7,7 ГПа) в широком диапазоне температур (1450-2450°С). Объектом исследования выбраны три композиции с содержанием cBN 50, 60 и 65 об.%, 5 об.% алюминия введено в смесь в качестве гетера кислорода. В работе представлены результаты исследования фазового состава, микроструктур и механических свойств. Варьирование содержания добавки практически не влияет на модуль сдвига композитов, высокие значения микротвердости получено в композитах, спеченных в температурном интервале 1850 - 2150 °С. При повышенных температурах спекания обнаружено формирование оксида алюминия во всех исследуемых системах. Разработанные композиты по своим механическим свойствам приближаются к коммерческим аналогам материалов группы BL и могут использоваться при высокоскоростной обработке сплавов на основе железа Шляхом термобаричного спікання отримано керамо-матричний композиційний матеріал на основі кубічного нітриду бору з добавками карбіду ванадію та алюмінію. Спікання проведено в умовах високого тиску (7,7 ГПа) в широкому діапазоні температур (1450–2450 °С). Об’єктом дослідження обрано три композиції з вмістом cBN 50, 60 та 65 об.%, 5 об.% алюмінію введено в суміш, як гетер кисню. У роботі представлено результати дослідження фазового складу, мікроструктур та механічних властивостей. Варіювання вмісту добавки практично не впливає на модуль зсуву композитів, найвищі значення мікротвердості отримано в композитах, спечених в температурному інтервалі 1850-2150 °С. За підвищених температурах спікання виявлено формування оксиду алюмінію в усіх досліджуваних системах. Розроблені композити за своїми механічними властивостями наближаються до комерційних аналогів матеріалів групи BL та можуть використовуватися для високошвидкісної обробки сплавів на основі заліза Институт сверхтвердых материалов им. В. Н. Бакуля Национальной академии наук Украины 2018-06-14 Article Article application/pdf http://altis-ism.org.ua/index.php/ALTIS/article/view/44 Інструментальне матеріалознавство; Том 21 (2018): Породоруйнівний та металооброблювальний інструмент - техніка і технологія його виготовлення та використання; 275-284 Инструментальное материаловедение; Том 21 (2018): Породоразрушающий и металлообрабатывающий инструмент - техника и технология его изготовления и применения; 275-284 Tooling materials science; Vol 21 (2018): Rock Destruction and Metal-Working Tools – Techniques and Technology of the Tool Production and Applications; 275-284 2708-7328 2708-731X uk http://altis-ism.org.ua/index.php/ALTIS/article/view/44/36

Similar Items