The task of the scientific study is to estimate the level of thermal residual stresses in the thin layers of the binding phase, and the carbide grains it surrounds, in alloys WC-Co. For this purpose, analytical methods, taking into account the stereometric parameters of the microstructure of the ind...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Datum:2019
1. Verfasser: Литошенко, Наталія
Format: Artikel
Sprache:Ukrainian
Veröffentlicht: Институт сверхтвердых материалов им. В. Н. Бакуля Национальной академии наук Украины 2019
Schlagworte:
залишкові термічні напруження
твердий сплав WC–Co
мікроструктурні параметри
аналітичний метод
Online Zugang:http://altis-ism.org.ua/index.php/ALTIS/article/view/52
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:Tooling materials science

Institution

Tooling materials science
id oai:ojs2.altis-ism.org.ua:article-52
record_format ojs
institution Tooling materials science
baseUrl_str
datestamp_date 2019-09-09T07:55:58Z
collection OJS
language Ukrainian
topic залишкові термічні напруження
твердий сплав WC–Co
мікроструктурні параметри
аналітичний метод
spellingShingle залишкові термічні напруження
твердий сплав WC–Co
мікроструктурні параметри
аналітичний метод
Литошенко, Наталія
ОЦІНКА ЗАЛИШКОВИХ ТЕРМІЧНИХ НАПРУЖЕНЬ В ТОНКИХ ПРОШАРКАХ КОБАЛЬТОВОЇ ЗВ’ЯЗКИ СПЛАВІВ WC-Co
topic_facet thermal residual stresses
WC–Co hardmetals
microstructural parameters
analytical method.
остаточные термические напряжения
твердый сплав WC-Co
микроструктурные параметры
аналитический метод
залишкові термічні напруження
твердий сплав WC–Co
мікроструктурні параметри
аналітичний метод
format Article
author Литошенко, Наталія
author_facet Литошенко, Наталія
author_sort Литошенко, Наталія
title ОЦІНКА ЗАЛИШКОВИХ ТЕРМІЧНИХ НАПРУЖЕНЬ В ТОНКИХ ПРОШАРКАХ КОБАЛЬТОВОЇ ЗВ’ЯЗКИ СПЛАВІВ WC-Co
title_short ОЦІНКА ЗАЛИШКОВИХ ТЕРМІЧНИХ НАПРУЖЕНЬ В ТОНКИХ ПРОШАРКАХ КОБАЛЬТОВОЇ ЗВ’ЯЗКИ СПЛАВІВ WC-Co
title_full ОЦІНКА ЗАЛИШКОВИХ ТЕРМІЧНИХ НАПРУЖЕНЬ В ТОНКИХ ПРОШАРКАХ КОБАЛЬТОВОЇ ЗВ’ЯЗКИ СПЛАВІВ WC-Co
title_fullStr ОЦІНКА ЗАЛИШКОВИХ ТЕРМІЧНИХ НАПРУЖЕНЬ В ТОНКИХ ПРОШАРКАХ КОБАЛЬТОВОЇ ЗВ’ЯЗКИ СПЛАВІВ WC-Co
title_full_unstemmed ОЦІНКА ЗАЛИШКОВИХ ТЕРМІЧНИХ НАПРУЖЕНЬ В ТОНКИХ ПРОШАРКАХ КОБАЛЬТОВОЇ ЗВ’ЯЗКИ СПЛАВІВ WC-Co
title_sort оцінка залишкових термічних напружень в тонких прошарках кобальтової зв’язки сплавів wc-co
title_alt ESTIMATION OF THERMAL RESIDUAL STRESSES IN THIN COBALT BOND LAYERS OF THE WC–Cо HARDMETAL
ОЦЕНКА ОСТАТОЧНОГО ТЕРМИЧЕСКИХ НАПРЯЖЕНИЙ В ТОНКИХ СЛОЯХ КОБАЛЬТОВЫХ СВЯЗКИ СПЛАВОВ WC-Co
description The task of the scientific study is to estimate the level of thermal residual stresses in the thin layers of the binding phase, and the carbide grains it surrounds, in alloys WC-Co. For this purpose, analytical methods, taking into account the stereometric parameters of the microstructure of the industrial marks of hardmetals, are defined in the plane section. It was established that the tensile stresses in thin cobalt layers for WC-4 wt% Co to WC-25 wt % Co alloys are 1350-1103 MPa and are lower than the average stresses in the bundle volume. Carbide grains in alloys WC-4 wt % Co  to WC-15 wt % Co are under the influence of tensile stresses, and WC-20 wt %Co and WC-25 wt %Co are compressive stresses, their level is much lower than in polycrystalline aggregates of carbide grains.  The application of the proposed method will allow monitoring the accuracy of the measurement of residual thermal stresses, will help to determine the optimal structure and technological cooling mode after sintering. Reducing local thermal stresses in alloys WC-Co will improve their strength, fracture toughness, wear resistance.
publisher Институт сверхтвердых материалов им. В. Н. Бакуля Национальной академии наук Украины
publishDate 2019
url http://altis-ism.org.ua/index.php/ALTIS/article/view/52
work_keys_str_mv AT litošenkonatalíâ estimationofthermalresidualstressesinthincobaltbondlayersofthewccohardmetal
AT litošenkonatalíâ ocenkaostatočnogotermičeskihnaprâženijvtonkihsloâhkobalʹtovyhsvâzkisplavovwcco
AT litošenkonatalíâ ocínkazališkovihtermíčnihnapruženʹvtonkihprošarkahkobalʹtovoízvâzkisplavívwcco
first_indexed 2025-09-24T17:41:42Z
last_indexed 2025-09-24T17:41:42Z
_version_ 1850410028972900352
spelling oai:ojs2.altis-ism.org.ua:article-522019-09-09T07:55:58Z ESTIMATION OF THERMAL RESIDUAL STRESSES IN THIN COBALT BOND LAYERS OF THE WC–Cо HARDMETAL ОЦЕНКА ОСТАТОЧНОГО ТЕРМИЧЕСКИХ НАПРЯЖЕНИЙ В ТОНКИХ СЛОЯХ КОБАЛЬТОВЫХ СВЯЗКИ СПЛАВОВ WC-Co ОЦІНКА ЗАЛИШКОВИХ ТЕРМІЧНИХ НАПРУЖЕНЬ В ТОНКИХ ПРОШАРКАХ КОБАЛЬТОВОЇ ЗВ’ЯЗКИ СПЛАВІВ WC-Co Литошенко, Наталія thermal residual stresses, WC–Co hardmetals, microstructural parameters, analytical method. остаточные термические напряжения, твердый сплав WC-Co, микроструктурные параметры, аналитический метод залишкові термічні напруження, твердий сплав WC–Co, мікроструктурні параметри, аналітичний метод The task of the scientific study is to estimate the level of thermal residual stresses in the thin layers of the binding phase, and the carbide grains it surrounds, in alloys WC-Co. For this purpose, analytical methods, taking into account the stereometric parameters of the microstructure of the industrial marks of hardmetals, are defined in the plane section. It was established that the tensile stresses in thin cobalt layers for WC-4 wt% Co to WC-25 wt % Co alloys are 1350-1103 MPa and are lower than the average stresses in the bundle volume. Carbide grains in alloys WC-4 wt % Co  to WC-15 wt % Co are under the influence of tensile stresses, and WC-20 wt %Co and WC-25 wt %Co are compressive stresses, their level is much lower than in polycrystalline aggregates of carbide grains.  The application of the proposed method will allow monitoring the accuracy of the measurement of residual thermal stresses, will help to determine the optimal structure and technological cooling mode after sintering. Reducing local thermal stresses in alloys WC-Co will improve their strength, fracture toughness, wear resistance. Задача научного исследования заключалась в том, чтобы оценить уровень остаточных термических напряжений в тонких прослойках связующей фазы, и карбидных зернах, которые она окружает в твердых сплавах WC-Co. Для этого предложены аналитические методы, учитывающие стереометрические параметры микроструктуры промышленных марок твердых сплавов, определенные в плоскости шлифа. Установлено, что растягивающие напряжения в тонких кобальтовых спрослойках для сплавов ВК4–ВК25 составляют 1350–1103 МПа и ниже средних напряжений по объему связи. Зерна WC в сплавах ВК4–ВК15 находятся под влиянием растягивающих напряжений, а в ВК20 и ВК25 – сжимающих, их уровень значительно ниже, чем в поликристаллических агрегатах карбидных зерен. Применение предложенного метода позволяет проводить контроль точности измерения остаточных термических напряжений, помогает установить оптимальную структуру и технологический режим охлаждения после спекания. Уменьшение локальных термонапряжений в сплавах WC-Co улучшит их прочность, вязкость разрушения, износостойкость. Завдання наукового дослідження полягає в тому, щоб оцінити рівень залишкових термічних напружень в тонких прошарках зв’язуючої фази, та карбідних зернах, які вона оточує в твердих сплавах WC-Co. Для цього запропоновано аналітичні методи, що враховують стереометричні параметри  мікроструктури промислових марок твердих сплавів, визначені в площині шліфа. Встановлено, що напруження розтягу в тонких кобальтових прошарках для сплавів ВК4-ВК25 становлять 1350-1103 МПа і є нижчими за середні напруження по об’єму зв’язки. Зерна WC в сплавах ВК4-ВК15 знаходяться під впливом розтягуючих напружень, а в ВК20 і ВК25 – напружень стиску, їх рівень значно нижчий ніж в полікристалічних агрегатах карбідних зерен. Застосування запропонованого методу дає можливість проводити контроль точності вимірювання залишкових термічних напружень, допомагає встановити оптимальну структуру та технологічний режим охолодження після спікання. Зменшення локальних термонапружень в сплавах WC-Co покращить їх міцність, в'язкість руйнування, зносостійкість.        The task of the scientific study is to estimate the level of thermal residual stresses in the thin layers of the binding phase, and the carbide grains it surrounds, in alloys WC-Co. For this purpose, analytical methods, taking into account the stereometric parameters of the microstructure of the industrial marks of hardmetals, are defined in the plane section. It was established that the tensile stresses in thin cobalt layers for WC-4 wt% Co to WC- 25 wt % Co alloys are 1350-1103 MPa and are lower than the average stresses in the bundle volume. Carbide grains in alloys WC- 4 wt % Co  to WC- 15 wt % Co are under the influence of tensile stresses, and WC-20 wt %Co and WC-25 wt %Co  are compressive stresses, their level is much lower than in polycrystalline aggregates of carbide grains.  The application of the proposed method will allow monitoring the accuracy of the measurement of residual thermal stresses, will help to determine the optimal structure and technological cooling mode after sintering. Reducing local thermal stresses in alloys WC-Co will improve their strength, fracture toughness, wear resistance.   Институт сверхтвердых материалов им. В. Н. Бакуля Национальной академии наук Украины 2019-09-06 Article Article application/pdf http://altis-ism.org.ua/index.php/ALTIS/article/view/52 Інструментальне матеріалознавство; Том 22 (2019); 384-390 Инструментальное материаловедение; Том 22 (2019); 384-390 Tooling materials science; Vol 22 (2019); 384-390 2708-7328 2708-731X uk http://altis-ism.org.ua/index.php/ALTIS/article/view/52/110 Авторське право (c) 2019 Породоруйнівний та металооброблювальний інструмент - техніка і технологія його виготовлення та використання

Ähnliche Einträge