ВПЛИВ ЛЕГУЮЧИХ ЕЛЕМЕНТІВ НА ТЕХНОЛОГІЧНІ Й МЕХАНІЧНІ ВЛАСТИВОСТІ СПЛАВІВ СИСТЕМИ Cu–Zn–(Ме): Procesi littâ, 2024, Vol 2 (156), 11-18
Copper-based brazing filler metals with a melting temperature of 600–650 °C, which have a sufficient level of strength and plasticity characteristics, are in demand in modern mechanical engineering. The paper presents the results of research on the assessment of the influence of alloying elements on...
Gespeichert in:
| Datum: | 2024 |
|---|---|
| Hauptverfasser: | , , |
| Format: | Artikel |
| Sprache: | Ukrainian |
| Veröffentlicht: |
National Academy of Sciences of Ukraine, Physical-Technological Institute of Metals and Alloys of NAS of Ukraine
2024
|
| Schlagworte: | |
| Online Zugang: | https://plit-periodical.org.ua/index.php/plit/article/view/238 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Casting Processes |
Institution
Casting Processes| id |
oai:ojs2.localhost:article-238 |
|---|---|
| record_format |
ojs |
| institution |
Casting Processes |
| baseUrl_str |
|
| datestamp_date |
2024-06-05T08:47:57Z |
| collection |
OJS |
| language |
Ukrainian |
| topic |
мідно-фосфорні сплави припій паяння фосфор цинк нікель механічні властивості |
| spellingShingle |
мідно-фосфорні сплави припій паяння фосфор цинк нікель механічні властивості Максимова, С.В. Писарєв, А.М. Воронов, В.В. ВПЛИВ ЛЕГУЮЧИХ ЕЛЕМЕНТІВ НА ТЕХНОЛОГІЧНІ Й МЕХАНІЧНІ ВЛАСТИВОСТІ СПЛАВІВ СИСТЕМИ Cu–Zn–(Ме): Procesi littâ, 2024, Vol 2 (156), 11-18 |
| topic_facet |
мідно-фосфорні сплави припій паяння фосфор цинк нікель механічні властивості copper-phosphorus alloys brazing filler metals brazing phosphorus zinc nickel mechanical properties |
| format |
Article |
| author |
Максимова, С.В. Писарєв, А.М. Воронов, В.В. |
| author_facet |
Максимова, С.В. Писарєв, А.М. Воронов, В.В. |
| author_sort |
Максимова, С.В. |
| title |
ВПЛИВ ЛЕГУЮЧИХ ЕЛЕМЕНТІВ НА ТЕХНОЛОГІЧНІ Й МЕХАНІЧНІ ВЛАСТИВОСТІ СПЛАВІВ СИСТЕМИ Cu–Zn–(Ме): Procesi littâ, 2024, Vol 2 (156), 11-18 |
| title_short |
ВПЛИВ ЛЕГУЮЧИХ ЕЛЕМЕНТІВ НА ТЕХНОЛОГІЧНІ Й МЕХАНІЧНІ ВЛАСТИВОСТІ СПЛАВІВ СИСТЕМИ Cu–Zn–(Ме): Procesi littâ, 2024, Vol 2 (156), 11-18 |
| title_full |
ВПЛИВ ЛЕГУЮЧИХ ЕЛЕМЕНТІВ НА ТЕХНОЛОГІЧНІ Й МЕХАНІЧНІ ВЛАСТИВОСТІ СПЛАВІВ СИСТЕМИ Cu–Zn–(Ме): Procesi littâ, 2024, Vol 2 (156), 11-18 |
| title_fullStr |
ВПЛИВ ЛЕГУЮЧИХ ЕЛЕМЕНТІВ НА ТЕХНОЛОГІЧНІ Й МЕХАНІЧНІ ВЛАСТИВОСТІ СПЛАВІВ СИСТЕМИ Cu–Zn–(Ме): Procesi littâ, 2024, Vol 2 (156), 11-18 |
| title_full_unstemmed |
ВПЛИВ ЛЕГУЮЧИХ ЕЛЕМЕНТІВ НА ТЕХНОЛОГІЧНІ Й МЕХАНІЧНІ ВЛАСТИВОСТІ СПЛАВІВ СИСТЕМИ Cu–Zn–(Ме): Procesi littâ, 2024, Vol 2 (156), 11-18 |
| title_sort |
вплив легуючих елементів на технологічні й механічні властивості сплавів системи cu–zn–(ме): procesi littâ, 2024, vol 2 (156), 11-18 |
| title_alt |
THE INFLUENCE OF ALLOYING ELEMENTS ON THE TECHNOLOGICAL AND MECHANICAL PROPERTIES OF Cu–Zn–(Me) ALLOYS: Procesi littâ, 2024, Vol 2 (156), 11-18 |
| description |
Copper-based brazing filler metals with a melting temperature of 600–650 °C, which have a sufficient level of strength and plasticity characteristics, are in demand in modern mechanical engineering. The paper presents the results of research on the assessment of the influence of alloying elements on the technological and mechanical properties of Cu–P–(Zn, Ni) alloys. With the help of conducted studies of high-temperature differential thermal analysis, mechanical tests and with the use of statistical processing of the results, regression equations were obtained that describe the dependence of liquidus and solidus temperatures, as well as the limits of strength and relative elongation of alloys depending on the content of zinc and phosphorus. Based on the results of Cu-P-(Zn, Ni) alloys metallographic studies, the effect of phosphorus, zinc and nickel on the volume fraction of the solid solution was determined. In particular, it was established that doping alloys of the binary Cu–P system with zinc up to 25 wt. % leads to an increase in the proportion of solid solution in them from 42–45 to 65-69 vol. %. An additional increase in the amount of solid solution in the alloy (up to 72–75 % by volume) is achieved by doping the alloy of the Cu-P-Zn system with nickel (up to 5 % by mass), which allows to obtain an alloy with a strength limit at the level of 450...500 MPa while maintaining plastic characteristics (δ = 6%). It should be noted that doping 5 wt. % of nickel with a zinc content of 25 wt. % makes it possible to maintain non-zero relative elongation at a phosphorus content of 5.5...6 wt. %. This alloying of alloys of the Cu-P-(Zn, Ni) system provides a melting temperature in the range of 650–750 °C with a lower concentration of phosphorus, and, as a result, a sufficiently high level of plastic properties (up to 6...8 %). Based on the results of the research, the composition Cu-P-(Zn, Ni) alloys was determined, which can potentially be used as a filler metals for brazing copper and copper alloys. |
| publisher |
National Academy of Sciences of Ukraine, Physical-Technological Institute of Metals and Alloys of NAS of Ukraine |
| publishDate |
2024 |
| url |
https://plit-periodical.org.ua/index.php/plit/article/view/238 |
| work_keys_str_mv |
AT maksimovasv theinfluenceofalloyingelementsonthetechnologicalandmechanicalpropertiesofcuznmealloysprocesilitta2024vol21561118 AT pisarêvam theinfluenceofalloyingelementsonthetechnologicalandmechanicalpropertiesofcuznmealloysprocesilitta2024vol21561118 AT voronovvv theinfluenceofalloyingelementsonthetechnologicalandmechanicalpropertiesofcuznmealloysprocesilitta2024vol21561118 AT maksimovasv vplivleguûčihelementívnatehnologíčníjmehaníčnívlastivostísplavívsistemicuznmeprocesilitta2024vol21561118 AT pisarêvam vplivleguûčihelementívnatehnologíčníjmehaníčnívlastivostísplavívsistemicuznmeprocesilitta2024vol21561118 AT voronovvv vplivleguûčihelementívnatehnologíčníjmehaníčnívlastivostísplavívsistemicuznmeprocesilitta2024vol21561118 AT maksimovasv influenceofalloyingelementsonthetechnologicalandmechanicalpropertiesofcuznmealloysprocesilitta2024vol21561118 AT pisarêvam influenceofalloyingelementsonthetechnologicalandmechanicalpropertiesofcuznmealloysprocesilitta2024vol21561118 AT voronovvv influenceofalloyingelementsonthetechnologicalandmechanicalpropertiesofcuznmealloysprocesilitta2024vol21561118 |
| first_indexed |
2025-09-24T17:41:09Z |
| last_indexed |
2025-12-17T12:07:40Z |
| _version_ |
1851757177392332800 |
| spelling |
oai:ojs2.localhost:article-2382024-06-05T08:47:57Z THE INFLUENCE OF ALLOYING ELEMENTS ON THE TECHNOLOGICAL AND MECHANICAL PROPERTIES OF Cu–Zn–(Me) ALLOYS: Procesi littâ, 2024, Vol 2 (156), 11-18 ВПЛИВ ЛЕГУЮЧИХ ЕЛЕМЕНТІВ НА ТЕХНОЛОГІЧНІ Й МЕХАНІЧНІ ВЛАСТИВОСТІ СПЛАВІВ СИСТЕМИ Cu–Zn–(Ме): Procesi littâ, 2024, Vol 2 (156), 11-18 Максимова, С.В. Писарєв, А.М. Воронов, В.В. мідно-фосфорні сплави припій паяння фосфор цинк нікель механічні властивості copper-phosphorus alloys brazing filler metals brazing phosphorus zinc nickel mechanical properties Copper-based brazing filler metals with a melting temperature of 600–650 °C, which have a sufficient level of strength and plasticity characteristics, are in demand in modern mechanical engineering. The paper presents the results of research on the assessment of the influence of alloying elements on the technological and mechanical properties of Cu–P–(Zn, Ni) alloys. With the help of conducted studies of high-temperature differential thermal analysis, mechanical tests and with the use of statistical processing of the results, regression equations were obtained that describe the dependence of liquidus and solidus temperatures, as well as the limits of strength and relative elongation of alloys depending on the content of zinc and phosphorus. Based on the results of Cu-P-(Zn, Ni) alloys metallographic studies, the effect of phosphorus, zinc and nickel on the volume fraction of the solid solution was determined. In particular, it was established that doping alloys of the binary Cu–P system with zinc up to 25 wt. % leads to an increase in the proportion of solid solution in them from 42–45 to 65-69 vol. %. An additional increase in the amount of solid solution in the alloy (up to 72–75 % by volume) is achieved by doping the alloy of the Cu-P-Zn system with nickel (up to 5 % by mass), which allows to obtain an alloy with a strength limit at the level of 450...500 MPa while maintaining plastic characteristics (δ = 6%). It should be noted that doping 5 wt. % of nickel with a zinc content of 25 wt. % makes it possible to maintain non-zero relative elongation at a phosphorus content of 5.5...6 wt. %. This alloying of alloys of the Cu-P-(Zn, Ni) system provides a melting temperature in the range of 650–750 °C with a lower concentration of phosphorus, and, as a result, a sufficiently high level of plastic properties (up to 6...8 %). Based on the results of the research, the composition Cu-P-(Zn, Ni) alloys was determined, which can potentially be used as a filler metals for brazing copper and copper alloys. У сучасному машинобудуванні затребувані припої на основі міді з температурою плавлення 600–650 °C, що мають достатній рівень характеристик міцності та пластичності. У роботі представлені результати досліджень щодо оцінки впливу легуючих елементів на технологічні та механічні властивості сплавів системи Cu–P–(Zn, Ni). За допомогою проведених досліджень високотемпературного диференційного термічного аналізу, механічних випробувань та з використанням статистичної обробки результатів отримано рівняння регресії, які описують залежності температури ліквідусу та солідусу, а також межі міцності та відносного видовження сплавів від вмісту цинку й фосфору. На базі результатів металографічних досліджень сплавів системи Cu–P–(Zn, Ni) визначено вплив фосфору, цинку і нікелю на об’ємну частку твердого розчину. Зокрема, встановлено, що легування сплавів бінарної системи Cu–P цинком до 25 мас. % призводить до зростання в них частки твердого розчину з 42–45 до 65–69 об. %. Додаткове збільшення кількості твердого розчину в сплаві (до 72–75 об. %) досягається шляхом легування сплаву системи Сu–Р–Zn нікелем (до мас. 5 %), що дозволяє отримувати сплав із межею міцності на рівні 450…500 МПа зі збереженням пластичних характеристик (δ = 6 %). Слід зазначити, що легування 5 мас. % нікелю при вмісті цинку 25 мас. % дозво ляє підтримувати відмінне від нуля відносне видовження при вмісті фосфору 5,5…6 мас. %. Таке легування сплавів системи Cu–P–(Zn, Ni) забезпечує температуру плавлення в межах 650–750 °С при меншій концентрації фосфору і, як наслідок, доволі високому рівні пластичних властивостей (до 6…8 %). За результатами проведених досліджень визначено склад сплаву системи Cu–P–(Zn, Ni), який потенційно може бути використаний як припой для паяння міді та мідних сплавів. National Academy of Sciences of Ukraine, Physical-Technological Institute of Metals and Alloys of NAS of Ukraine 2024-06-05 Article Article application/pdf https://plit-periodical.org.ua/index.php/plit/article/view/238 10.15407/plit2024.02.011 Casting processes; Casting processes №2 (156) 2024; 11-18 Процеси лиття; Процеси лиття №2 (156) 2024; 11-18 2707-1626 0235-5884 uk https://plit-periodical.org.ua/index.php/plit/article/view/238/242 Авторське право (c) 2024 С.В. Максимова, А.М. Писарєв, В.В. Воронов https://creativecommons.org/licenses/by-nc-nd/4.0 |