Вплив технологічної схеми виготовлення на структуру та властивості високоентропійних сплавів системи Ti – Cr – Fe – Ni – Cu
Using the methods of powder metallurgy, according to three technological schemes, high-entropic alloys of the equiatomic composition TiCrFeNiCu were developed. During the sintering of the mixture of the equiatomic composition of TiCrFeNiCu, the effect of entropy of mixing caused the formation of sol...
Gespeichert in:
| Datum: | 2018 |
|---|---|
| Hauptverfasser: | , , |
| Format: | Artikel |
| Sprache: | Ukrainisch |
| Veröffentlicht: |
Physico- Technological Institute of Metals and Alloys of the NAS of Ukraine
2018
|
| Online Zugang: | https://momjournal.org.ua/index.php/mom/article/view/2018-2-5 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Metal Science and Treatment of Metals |
Institution
Metal Science and Treatment of Metals| Zusammenfassung: | Using the methods of powder metallurgy, according to three technological schemes, high-entropic alloys of the equiatomic composition TiCrFeNiCu were developed. During the sintering of the mixture of the equiatomic composition of TiCrFeNiCu, the effect of entropy of mixing caused the formation of solid substitution solutions based on lattices of BCC and FCC. The most complete realization of mixing entropy is carried out by technology: grinding → hot stamping. Hot stamping of the ground powders leads to the preferential formation of a solid substitution solution based on the FCC lattice with a substantial distortion of the crystal lattice: CSR – 15,3 nm, (Δa/a) – 20,1·10-2 (FCC), dislocation density ρ – 8,6·1012 cm-2 (FCC). The resulting alloy has maximum hardness. |
|---|