Вплив перемішування розплаву на структуру та властивості спрямовано закристалізованого сплаву Mo – 17,5Si – 8B
By method of crucibleless zone melting was obtained alloys Mo – 17,5% Si – 8% B (at.%), with additional melt mixing by rotating cylindrical workpiece around its axis. Structure of obtained alloy is a grain of molybdenum solid solution, around which are located two - and three - phase eutectics (Mo –...
Saved in:
| Date: | 2018 |
|---|---|
| Main Authors: | , , , |
| Format: | Article |
| Language: | Ukrainian |
| Published: |
Physico- Technological Institute of Metals and Alloys of the NAS of Ukraine
2018
|
| Online Access: | https://momjournal.org.ua/index.php/mom/article/view/2018-1-3 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Journal Title: | Metal Science and Treatment of Metals |
Institution
Metal Science and Treatment of Metals| Summary: | By method of crucibleless zone melting was obtained alloys Mo – 17,5% Si – 8% B (at.%), with additional melt mixing by rotating cylindrical workpiece around its axis. Structure of obtained alloy is a grain of molybdenum solid solution, around which are located two - and three - phase eutectics (Mo – Mo5SiB2), (Mo3Si - Mo5SiB2) and (Mo – Mo3Si – Mo5SiB2). Due to solid-hardening, the microhardness of molybdenum solid solution increases by more than 4 times compared with pure molybdenum. The crack growth resistance of eutectic areas lies within 14 MPa∙м1/2. It is shown that the directed crystallized Mo – Si – B alloy is characterized by increased resistance of creep, which indicates the perspective of its use in nodes of high – temperature appliance. |
|---|