Удосконалення технології зміцнення профілів з алюмінієвих сплавів
Based on literature data, the possibilities and mechanisms of strengthening of wrought aluminum alloys of the 2xxx, 4xxx, 6xxx and 7xxx series during quenching and heat treatment, methods of increasing their strength and ductility are considered. It should be noted that this issue is stated very vag...
Збережено в:
| Дата: | 2025 |
|---|---|
| Автори: | , , |
| Формат: | Стаття |
| Мова: | Ukrainian |
| Опубліковано: |
Physico- Technological Institute of Metals and Alloys of the NAS of Ukraine
2025
|
| Теми: | |
| Онлайн доступ: | https://momjournal.org.ua/index.php/mom/article/view/2025-1-6 |
| Теги: |
Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
|
| Назва журналу: | Metal Science and Treatment of Metals |
Репозитарії
Metal Science and Treatment of Metals| id |
oai:ojs2.localhost:article-330 |
|---|---|
| record_format |
ojs |
| institution |
Metal Science and Treatment of Metals |
| baseUrl_str |
|
| datestamp_date |
2025-05-23T07:41:39Z |
| collection |
OJS |
| language |
Ukrainian |
| topic |
деформівні алюмінієві сплави профілі пресування термічна обробка |
| spellingShingle |
деформівні алюмінієві сплави профілі пресування термічна обробка Nogovitsyn, A. V. Prygunov, S. V. Goncharov, O. L. Удосконалення технології зміцнення профілів з алюмінієвих сплавів |
| topic_facet |
deformed aluminum alloys profiles pressing heat treatment деформівні алюмінієві сплави профілі пресування термічна обробка |
| format |
Article |
| author |
Nogovitsyn, A. V. Prygunov, S. V. Goncharov, O. L. |
| author_facet |
Nogovitsyn, A. V. Prygunov, S. V. Goncharov, O. L. |
| author_sort |
Nogovitsyn, A. V. |
| title |
Удосконалення технології зміцнення профілів з алюмінієвих сплавів |
| title_short |
Удосконалення технології зміцнення профілів з алюмінієвих сплавів |
| title_full |
Удосконалення технології зміцнення профілів з алюмінієвих сплавів |
| title_fullStr |
Удосконалення технології зміцнення профілів з алюмінієвих сплавів |
| title_full_unstemmed |
Удосконалення технології зміцнення профілів з алюмінієвих сплавів |
| title_sort |
удосконалення технології зміцнення профілів з алюмінієвих сплавів |
| title_alt |
Improvement of technology for strengthening aluminum alloy profiles |
| description |
Based on literature data, the possibilities and mechanisms of strengthening of wrought aluminum alloys of the 2xxx, 4xxx, 6xxx and 7xxx series during quenching and heat treatment, methods of increasing their strength and ductility are considered. It should be noted that this issue is stated very vaguely and ambiguously in domestic standards. Quenching from the temperature of hot deformation is called incomplete quenching and is designated T5. Under full quenching is understood only quenching from separate heating with the designation T6. There is no mention of any possibility of achieving a state of complete quenching without separate furnace heating. To obtain maximum physical and mechanical properties of this alloy, it is necessary to optimize all technological processes: melting, refining, modification, obtaining ingots, homogenization, pressing and heat treatment. The economic advantages of using the technology of heat treatment of profiles with hardening on the press compared to hardening with separate heating are analyzed and shown, a necessary condition for the implementation of which is the identity of the temperature intervals of heating for hardening and exiting the press. To obtain a supersaturated solid solution, which during further processing operations contributes to dispersion aging and increasing the strength of profiles, their cooling at the exit from the press should be at a speed not lower than the critical one, which depends on the chemical composition of the aluminum alloy. The greatest efficiency of thermal hardening of aluminum alloys of the 6xxx series is achieved with a three-stage heat treatment. Possible ways of implementing this process, their advantages and disadvantages are described. The requirements of American and European standards for deformable aluminum alloys are discussed, as well as the features of the technological process for obtaining high-quality profiles depending on their chemical composition. |
| publisher |
Physico- Technological Institute of Metals and Alloys of the NAS of Ukraine |
| publishDate |
2025 |
| url |
https://momjournal.org.ua/index.php/mom/article/view/2025-1-6 |
| work_keys_str_mv |
AT nogovitsynav improvementoftechnologyforstrengtheningaluminumalloyprofiles AT prygunovsv improvementoftechnologyforstrengtheningaluminumalloyprofiles AT goncharovol improvementoftechnologyforstrengtheningaluminumalloyprofiles AT nogovitsynav udoskonalennâtehnologíízmícnennâprofílívzalûmíníêvihsplavív AT prygunovsv udoskonalennâtehnologíízmícnennâprofílívzalûmíníêvihsplavív AT goncharovol udoskonalennâtehnologíízmícnennâprofílívzalûmíníêvihsplavív |
| first_indexed |
2025-09-24T18:19:37Z |
| last_indexed |
2025-09-24T18:19:37Z |
| _version_ |
1850424257121615872 |
| spelling |
oai:ojs2.localhost:article-3302025-05-23T07:41:39Z Improvement of technology for strengthening aluminum alloy profiles Удосконалення технології зміцнення профілів з алюмінієвих сплавів Nogovitsyn, A. V. Prygunov, S. V. Goncharov, O. L. deformed aluminum alloys profiles pressing heat treatment деформівні алюмінієві сплави профілі пресування термічна обробка Based on literature data, the possibilities and mechanisms of strengthening of wrought aluminum alloys of the 2xxx, 4xxx, 6xxx and 7xxx series during quenching and heat treatment, methods of increasing their strength and ductility are considered. It should be noted that this issue is stated very vaguely and ambiguously in domestic standards. Quenching from the temperature of hot deformation is called incomplete quenching and is designated T5. Under full quenching is understood only quenching from separate heating with the designation T6. There is no mention of any possibility of achieving a state of complete quenching without separate furnace heating. To obtain maximum physical and mechanical properties of this alloy, it is necessary to optimize all technological processes: melting, refining, modification, obtaining ingots, homogenization, pressing and heat treatment. The economic advantages of using the technology of heat treatment of profiles with hardening on the press compared to hardening with separate heating are analyzed and shown, a necessary condition for the implementation of which is the identity of the temperature intervals of heating for hardening and exiting the press. To obtain a supersaturated solid solution, which during further processing operations contributes to dispersion aging and increasing the strength of profiles, their cooling at the exit from the press should be at a speed not lower than the critical one, which depends on the chemical composition of the aluminum alloy. The greatest efficiency of thermal hardening of aluminum alloys of the 6xxx series is achieved with a three-stage heat treatment. Possible ways of implementing this process, their advantages and disadvantages are described. The requirements of American and European standards for deformable aluminum alloys are discussed, as well as the features of the technological process for obtaining high-quality profiles depending on their chemical composition. На основі даних літератури розглянуто можливості і механізми зміцнення деформівних сплавів алюмінію серій 2ххх, 4ххх, 6ххх та 7ххх гартуванням гарячої заготовки, переважно від температури пресування, безпосередньо на виході виробу з пресу. Слід зазначити, що у вітчизняних стандартах це питання викладається дуже туманно і неоднозначно. Гартування з температури гарячої деформації називають неповним гартуванням і позначають Т5. Під повним гартуванням розуміють тільки гартування з окремого нагріву з позначенням Т6. Про будь-яку можливість досягати стану повного гартування без окремого пічного нагріву ніде не згадується. Для отримання максимальних фізико-механічних властивостей даного сплаву потрібно оптимізувати всі технологічні процеси: плавки, рафінування, модифікування, отримання злитків, гомогенізації, пресування та термообробки. Проаналізовано та показано економічні переваги використання технології термічної обробки профілів з гартуванням на пресі порівняно з гартуванням з окремого нагріву, необхідною умовою реалізації якої є ідентичність температурних інтервалів нагріву під гартування і виходу з пресу. Для одержання пересиченого твердого розчину, що при подальших операціях обробки сприяє дисперсійному старінню та підвищенню міцності профілів, їх охолодження на виході з пресу повинно бути зі швидкістю не нижче критичної, яка залежить від хімічного складу алюмінієвого сплаву. Найбільша ефективність термічного зміцнення алюмінієвих сплавів серії 6ххх досягається при триступеневій термічній обробці. Описано можливі шляхи реалізації цього процесу, їх переваги і недоліки. Обговорено вимоги американських і європейських стандартів до алюмінієвих сплавів, що деформуються, а також особливості технологічного процесу одержання якісних профілів у залежності від їх хімічного складу. Physico- Technological Institute of Metals and Alloys of the NAS of Ukraine 2025-03-31 Article Article application/pdf https://momjournal.org.ua/index.php/mom/article/view/2025-1-6 10.15407/mom2025.01.050 Scientific Technical Journal; Vol. 31 No. 1 (2025): The Scientific Technical journal Metal Science and Treatment of Metals; 50-60 Науково-технічний журнал; Том 31 № 1 (2025): Науково-технічний журнал Металознавство та обробка металів; 50-60 2664-2441 2073-9583 10.15407/mom2025.01 uk https://momjournal.org.ua/index.php/mom/article/view/2025-1-6/333 Copyright (c) 2025 Scientific Technical Journal https://creativecommons.org/licenses/by-nc-nd/4.0 |