Numerical assessment of brittle strength of field welds of the main gas pipelines at transportation of gas-hydrogen mixtures

Gespeichert in:

Bibliographische Detailangaben
Datum:	2023
Hauptverfasser:	O. S. Milenin, O. A. Velykoivanenko, H. P. Rozynka, N. I. Pivtorak
Format:	Artikel
Sprache:	Englisch
Veröffentlicht:	2023
Schriftenreihe:	Technical diagnostics and non-destructive testing
Online Zugang:	http://jnas.nbuv.gov.ua/article/UJRN-0001394329
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Ähnliche Einträge

Numerical analysis of the regularities of the infuence of pipe steel degradation on the reliability of corroded main gas pipelines used for transportation of gas-hydrogen mixtures
von: O. S. Milenin, et al.
Veröffentlicht: (2024)

Features of analysis of the technical state and support of reliability of the main gas pipelines at transportation of gashydrogen mixtures (Review)
von: O. S. Milenin, et al.
Veröffentlicht: (2022)

Numerical methodology of prediction of the reliability and residual life of welded pipeline elements with corrosion-erosion defects
von: O. S. Milenin, et al.
Veröffentlicht: (2020)

Numerical analysis of the features of limiting state of welded pipeline elements under ultra-low-cycle loading
von: O. V. Makhnenko, et al.
Veröffentlicht: (2021)

The influence of the operated gas pipeline steels texture on their resistance to brittle fracture
von: O. I. Zvirko, et al.
Veröffentlicht: (2018)

Degradation of welded joint metal of the exploited main gas pipeline
von: O. T. Tsyrulnyk, et al.
Veröffentlicht: (2010)

Analytical methods of optimization of operational parameters of the main gas pipelines (gas mains)
von: V. Frolov, et al.
Veröffentlicht: (2018)

A numerical method of multiscale modeling of the stress-strain state of large-sized sctructures in site welding
von: O. S. Milenin, et al.
Veröffentlicht: (2023)

Behaviour of hydrogen in repair welding of pressure main pipelines
von: V. I. Makhnenko, et al.
Veröffentlicht: (2011)

Tendency to crack formation in welded joints of repair structures on the gas main pipelines
von: V. S. But, et al.
Veröffentlicht: (2014)

Analysis of conditions of initiation and propagation of corrosion cracks in the zone of circumferential joints of main gas pipelines
von: V. I. Makhnenko, et al.
Veröffentlicht: (2009)

Problems and prospects of transporting a mixture of green hydrogen and natural gas in the context of the development of hydrogen energy in Ukraine
von: O. I. Zvirko
Veröffentlicht: (2024)

Procedure of ranging corrosion defects of the main gas pipelines found at in-pipe diagnostics
von: V. I. Makhnenko, et al.
Veröffentlicht: (2009)

Numerical prediction of effectiveness of reinforcement of defective pipelines by composite material bands
von: E. A. Velikoivanenko, et al.
Veröffentlicht: (2016)

Research of natural gas balance error in main gas pipelines system
von: Ильченко, Б. С., et al.
Veröffentlicht: (2016)

Research of natural gas balance error in main gas pipelines system
von: Ильченко, Б. С., et al.
Veröffentlicht: (2016)

Research of natural gas balance error in main gas pipelines system
von: B. S. Ilchenko, et al.
Veröffentlicht: (2010)

The influence of soil corrosion and transported products on lifetime of oil and gas pipelines welded joins
von: Ye. Andreikiv, et al.
Veröffentlicht: (2013)

Development of technology of mechanized arc welding in repair of main high-pressure gas pipeline
von: O. I. Olejnik, et al.
Veröffentlicht: (2016)

Efficiency of innovation-investment projects assessment of main gas pipelines modernization
von: Ya. S. Vytvytskyi, et al.
Veröffentlicht: (2014)

Automated assessing of damages of the main gas pipeline surface by corrosion pittings
von: I. V. Konovalenko, et al.
Veröffentlicht: (2013)

Prediction of residual strength of pipeline elements with detected corrosion defects based on Monte-Carlo method
von: A. S. Milenin, et al.
Veröffentlicht: (2019)

Multiscale procedure of numerical assessment of damage rate and technical state of structures from fibrous materials
von: O. S. Milenin, et al.
Veröffentlicht: (2021)

Numerical modeling transient processes in a long gas pipeline
von: V. F. Chekurin, et al.
Veröffentlicht: (2019)

Influence of metal shrinkage in longitudinal welds of sleeves on contact pressure in main gas pipeline repair
von: O. I. Olejnik
Veröffentlicht: (2015)

Method of natural gas evacuation from subject to repair area of main gas pipeline
von: T. V. Bunko, et al.
Veröffentlicht: (2018)

Continuous monitoring of the main gas pipelines and gas compressor units by acoustic emission method
von: Ja. Nedoseka, et al.
Veröffentlicht: (2011)

Evaluation of serviceability of main pipeline with a local thinning of wall in arc surfacing repair
von: E. A. Velikoivanenko, et al.
Veröffentlicht: (2015)

Methodology of numerical prediction of serviceability of pipeline elements with corrosion-erosion defects under conditions of high-temperature operation
von: A. S. Milenin, et al.
Veröffentlicht: (2017)

Analysis of technogenic risk for the linear part of the main gas pipelines
von: Z. M. Matsuk
Veröffentlicht: (2019)

The Increase of Energy and Ecology Efficiency of the Main Gas Pipelines Functioning
von: R. M. Govdjak
Veröffentlicht: (2012)

Residual stresses of circumferential welds of main gas pipeline in long-term service under the North conditions
von: N. I. Golikov, et al.
Veröffentlicht: (2012)

Hydrogen Brittleness and Hydrogen Plasticity of Steel
von: V. A. Soshko, et al.
Veröffentlicht: (2014)

Peculiarities of corrosion-hydrogen degradation of oil and gas pipelines and oil tanks
von: Ye. I. Kryzhanivskyi, et al.
Veröffentlicht: (2011)

The influence of hydrogenation of oil-and-gas pipeline walls on their soil corrosion and life
von: O. V. Hembara, et al.
Veröffentlicht: (2011)

Risk of failure during thinning of wall of main pipeline in the area of circumferential welded joints at the presence of bending moments along the axis of pipeline
von: V. I. Makhnenko, et al.
Veröffentlicht: (2012)

Simulation of processes of initiation and propagation of subcritical damage of metal in welded pipeline elements at low-cycle loading
von: E. A. Velikoivanenko, et al.
Veröffentlicht: (2016)

Improvement of method of assessment of risk of fracture in the zone of wall thinning in main pipelines
von: V. I. Makhnenko, et al.
Veröffentlicht: (2010)

Mathematical models for integrity control of linear part of main gas pipelines
von: V. F. Chekurin, et al.
Veröffentlicht: (2020)

Biocorrosion and localization of degradation processes on main gas pipeline steel surface
von: Ye. I. Kryzhanivskyi, et al.
Veröffentlicht: (2019)