Analysis of causes of failure of site welded butt joints of main pipelines after long-term operation

Gespeichert in:

Bibliographische Detailangaben
Datum:	2023
Hauptverfasser:	L. I. Nyrkova, L. V. Honcharenko
Format:	Artikel
Sprache:	Englisch
Veröffentlicht:	2023
Schriftenreihe:	Automatic Welding
Online Zugang:	http://jnas.nbuv.gov.ua/article/UJRN-0001405700
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Ähnliche Einträge

Structural changes in metal of welded joints of steam pipelines after long term service
von: V. V. Dmytryk, et al.
Veröffentlicht: (2017)

Causes of stress corrosion fracture of site circumferential joint of main gas pipeline
von: A. A. Rybakov, et al.
Veröffentlicht: (2014)

Equipment for preparation of pipe ends to welding of position butt joints of pipeline
von: L. M. Lobanov, et al.
Veröffentlicht: (2015)

About requirements to impact strength of pipeline joints made by flash-butt welding
von: V. I. Kirjan, et al.
Veröffentlicht: (2015)

Risk of failure during thinning of wall of main pipeline in the area of circumferential welded joints at the presence of bending moments along the axis of pipeline
von: V. I. Makhnenko, et al.
Veröffentlicht: (2012)

Equipment for Preparing Pipeline Position Butts for Welding
von: L. M. Lobanov, et al.
Veröffentlicht: (2015)

Investigation of the causes for appearance of defects in welded butt joints of tram rails made by thermit welding
von: E. Turyk, et al.
Veröffentlicht: (2021)

Determination of stressed state in spiral welded joint in the main pipeline
von: L. Senkiv
Veröffentlicht: (2015)

Corrosion-mechanical resistance of welded joints of AMg5M alloy produced in different spatial positions of butts
von: L. I. Nyrkova, et al.
Veröffentlicht: (2022)

Degradation of welded joint metal of the exploited main gas pipeline
von: O. T. Tsyrulnyk, et al.
Veröffentlicht: (2010)

Residual stresses of circumferential welds of main gas pipeline in long-term service under the North conditions
von: N. I. Golikov, et al.
Veröffentlicht: (2012)

Residual lifetime estimation for long exploited section of the main gas pipeline
von: Ye. Andreikiv, et al.
Veröffentlicht: (2012)

Efficiency of strengthening by high-frequency mechanical peening of butt welded joints at long-time service
von: V. V. Knysh, et al.
Veröffentlicht: (2014)

Procedure of accelerated corrosion testing for modelling the long-term effect of moderate climate atmosphere on welded joints
von: V. V. Knysh, et al.
Veröffentlicht: (2019)

Application of high-frequency peening to improve the performance of butt welded joints in the atmosphere of temperate climate
von: V. V. Knysh, et al.
Veröffentlicht: (2017)

Expert system for monitoring the technical state and assessment of the risk of failure of ground sections of gas pipelines in long-term operation
von: I. M. Dmytrakh, et al.
Veröffentlicht: (2016)

Influence of corrosion damages on cyclic life of butt welded joints strengthened by high-frequency mechanical peening
von: V. V. Knysh, et al.
Veröffentlicht: (2018)

Tendency to crack formation in welded joints of repair structures on the gas main pipelines
von: V. S. But, et al.
Veröffentlicht: (2014)

Flash-butt welding of concrete reinforcement under site conditions
von: P. N. Chvertko, et al.
Veröffentlicht: (2014)

Fatigue crack growth resistance of long-term operated steel of the main oil pipeline
von: A. V. Bogdanovich, et al.
Veröffentlicht: (2011)

Restoration of heat-resistant steel properties after long-term operation in a steam pipeline
von: O. Z. Student, et al.
Veröffentlicht: (2021)

Weld formation in consumable electrode welding of butt joints of amg5m aluminium alloy in site with a forming backing element and without it
von: T. M. Labur, et al.
Veröffentlicht: (2021)

Peculiarities of pore formation in welded joints of steam pipelines under conditions of long-time service
von: V. V. Dmitrik, et al.
Veröffentlicht: (2016)

Defects of joints of high-strength rails, made by flash-butt welding
von: S. I. Kuchuk-Jatsenko, et al.
Veröffentlicht: (2013)

Corrosion-resistant inhibited coatings for welded joints of pipelines
von: V. I. Pokhmurskyi, et al.
Veröffentlicht: (2013)

Equipment for heat treatment of welded joints of pipelines
von: E. A. Pantelejmonov
Veröffentlicht: (2012)

Determination of force caused by heating of ring-type products in flash-butt welding
von: A. V. Moltasov, et al.
Veröffentlicht: (2015)

The influence of marine environment on fatigue life of butt welded joints of 15KhSND steel, strengthened by high-frequency mechanical impact
von: V. V. Knysh, et al.
Veröffentlicht: (2019)

The influence of high-frequency mechanical impact strengthening of the butt welded joints of 15KhSND steel on their atmospheric corrosion and resistance to fatigue fracture
von: V. V. Knysh, et al.
Veröffentlicht: (2018)

Prediction of σ-phase content in HAZ of butt joints of duplex steels in arc welding
von: V. I. Makhnenko, et al.
Veröffentlicht: (2011)

Peculiarities of technology of repair welding of HPP turbounits after long-term operation
von: V. P. Yelahin, et al.
Veröffentlicht: (2018)

Cause of secondary hardening in Cr–Mo–V weld during long-term heat exposure
von: P. Mogila, et al.
Veröffentlicht: (2011)

Recovery and recrystallization of metal of steam line welded joints during long-term service
von: V. V. Dmytryk, et al.
Veröffentlicht: (2022)

Stress-strain state of polymer pipe welded joints made by butt welding under angle
von: E. S. Nikonova, et al.
Veröffentlicht: (2009)

Effect of preparation and assembly for welding on quality of welded joints of technological pipelines
von: P. V. Zankovets
Veröffentlicht: (2011)

Methods of evaluation of increase of fatigue resistance in butt welded joints of low-carbon steels after high-frequency mechanical peening
von: V. A. Degtjarev
Veröffentlicht: (2019)

Features of embrittlement of welded joints of operated steam pipelines
von: V. V. Dmitrik, et al.
Veröffentlicht: (2018)

Features of degradation of metal of steam pipeline welded joints
von: V. V. Dmitrik, et al.
Veröffentlicht: (2015)

Inductors for heat treatment of welded butt joints of railway and tram grooved rails
von: Ye. O. Panteleimonov
Veröffentlicht: (2022)

Influence of dimensions of weld convexity on stressed state of a butt joint in tension
von: G. V. Ermolaev, et al.
Veröffentlicht: (2014)